Flux core wire for a welding method, welding method using the flux core wire, and method for producing the flux core wire
A flux core wire for a welding method, having a tubular wire sheath, a wire core of flux powder, which is surrounded by the tubular wire sheath, wherein the wire sheath and the wire core have a composition such that during the welding a melt of CuSn 12 Ni 2 materialises.
1. A flux core wire for a welding method to repair or build-up a functional layer of a sliding bearing, comprising:
a wire sheath, which is tubular and having a content of Cu of at least 95% by mass; and
a wire core of flux powder that is surrounded by the wire sheath, which is tubular,
wherein the wire sheath and the wire core have a composition such that a melt of CuSn 12 Ni 2 materialises during welding,
wherein the wire core and thus the flux powder comprises:
a content of Cu of 50 to 80% by mass;
a content of Sn of 19.99 to 40% by mass; and
a content of Ni of 0.01 to 10% by mass,
wherein a total of Cu, Sn, Ni amounts to 100% by mass; and
wherein:
the flux powder of the wire core comprises as one or more trace elements S, and/or Fe, and/or Si, and/or Pb, and/or Zn, and/or Sb, and/or Al, and/or O, and/or Mn, and/or Ag, and/or Bi,
a content of a respective trace element in the flux powder of the wire core as a super addition in each case amounts to maximally 0.5% by mass,
a content of the wire sheath in the flux core wire amounts to 60±20% by mass, and
the content of the wire core in the flux core wire is the remainder thereof.
2. The flux core wire according to claim 1 , wherein the wire sheath comprises:
a remainder as trace element S, and/or Fe, and/or Si, and/or Pb, and/or Zn, and/or Sb, and/or Al, and/or O, and/or Mn, and/or Ag, and/or Bi.
3. The flux core wire according to claim 2 , wherein a content of the respective trace element in the wire sheath amounts to maximally 0.1 by mass.
4. The flux core wire according to claim 2 , wherein the wire sheath comprises at least one of:
the content of Cu at least 96% by mass,
the content of Cu at least 97% by mass, and
the content of Cu at least 99% by mass.
5. The flux core wire according to claim 1 , wherein the wire sheath has:
an outer diameter of 0.8 to 2 mm and
a thickness of 0.05 to 0.7 mm.
6. The flux core wire according to claim 1 , wherein the wire core and thus the flux powder comprises:
a content of Cu of 60 to 73% by mass;
a content of Sn of 25 to 32% by mass; and
a content of Ni of 2 to 8% by mass.
7. The flux core wire according to claim 1 , wherein the flux powder of the wire core has a grain size of up to 250 μm.
8. A welding method comprising:
providing a flux core wire according to claim 1 ,
performing one of a MIG welding method or a MAG welding method for a repair or a building-up of a functional layer or for building up a solid material component as machine element of a CuSn 12 Ni 2 alloy.
9. The welding method according to claim 8 , wherein the functional layer is a sliding bearing layer of a sliding bearing.
10. A method for producing a flux core wire according to claim 1 , having a tubular wire sheath and a wire core of flux powder that is surrounded by the tubular wire sheath, wherein the tubular wire sheath and the wire core have a composition such that a melt of CuSn 12 Ni 2 materialises during welding, comprising:
providing a metal sheet for the wire sheath;
cutting off a blank for the tubular wire sheath;
providing the flux powder for the wire core;
forming the blank for the wire sheath into the tubular wire sheath with a hollow space; and
filling the hollow space of the tubular wire sheath with the flux powder during and/or after the forming of the blank for the wire sheath into the wire sheath forming the wire core.