Electrochemical cells comprising water-retaining components and methods of fabricating
Provided are electrochemical cells, comprising water-retaining components, and methods of fabricating such electrochemical cells. A water-retaining component is configured to deliver water to the positive active material during the operation of the electrochemical cell. The water-retaining component may be a part of the positive active material layer, a part of the electrolyte layer, and/or a standalone component. In some examples, the water-retaining component comprises one or more crystal hydrates (e.g., MgSO 4 , MgCl 2 , Na 2 SO 4 , Na 2 HPO 4 , CuSO 4 , CaCl 2 , KAl(SO 4 ) 2 , and Mg(NO 3 ) 2 ), one or more water-retaining polymers (e.g., sodium polyacrylate, potassium polyacrylate, ammonium polyacrylate, and a cellulose derivative), one or more inorganic compounds (e.g., fumed silica, precipitated silica). In some examples, a method of forming an electrochemical cell comprises printing a positive active material layer, a negative active material layer, and an electrolyte layer, e.g., printing the electrolyte layer directly over the positive active material layer or the negative active material layer.
1. A method of forming an electrochemical cell, the method comprising:
printing a positive active material layer comprising a positive active material;
providing a pre-formed zinc foil as a negative active material layer; and
printing an electrolyte layer,
wherein the electrolyte layer is disposed between and providing ionic communication between the positive active material layer and the negative active material layer, and
wherein the electrolyte layer comprises water and a water-retaining component, configured to deliver water to the positive active material of the positive active material layer during operation of the electrochemical cell, and
wherein an amount of water in the electrochemical cell is 5% to 10% of a total weight of the electrochemical cell.
2. The method of claim 1 , wherein the electrolyte layer is printed directly onto the positive active material layer or the negative active material layer.
3. The method of claim 1 , wherein the water-retaining component comprises one or more crystal hydrates.
4. The method of claim 1 , wherein the water-retaining component comprises one or more water-retaining polymers.
5. The method of claim 1 , wherein the water-retaining component comprises one or more porous inorganic compounds.
6. The method of claim 3 , wherein the one or more crystal hydrates are selected from the group consisting of MgSO 4 , MgCl 2 , Na 2 HPO 4 , CuSO 4 , CaCl 2 , KAl(SO 4 ) 2 , and Mg(NO 3 ) 2 .
7. The method of claim 4 , wherein the one or more water-retaining polymers are selected from the group consisting of sodium polyacrylate, potassium polyacrylate, carboxymethyl cellulose, polyvinyl alcohol, ammonium polyacrylate, and a cellulose derivative.
8. The method of claim 4 , wherein the one or more water-retaining polymers comprise xanthan or methylcellulose.
9. The method of claim 1 , wherein the water-retaining component comprises one or more inorganic compounds selected from the group consisting of fumed silica and precipitated silica.
10. The method of claim 1 , wherein the electrolyte layer comprising water in an amount of 30% to 70% of a total weight of the electrolyte layer.
11. The method of claim 1 , wherein the electrolyte layer provides an ionic conductivity above 50 mS/cm between the positive active material layer and the negative active material layer.
12. The method of claim 1 , wherein an amount the positive active material is 80% to 95% of a total weight of the positive active material layer and also is 5% to 10% of a total weight of the electrochemical cell.
13. The method of claim 1 , wherein an amount of the positive active material and an amount of the negative active material is less than 50% of the total weight of the electrochemical cell.
14. The method of claim 1 , wherein the amount of water in the electrochemical cell is from 6% to 8% by weight of the total weight of the electrochemical cell.
15. The method of claim 1 , wherein more than 50% by weight of the water in the electrochemical cell is present in the electrolyte layer.
16. The method of claim 1 , wherein the electrolyte layer comprises silica.
17. The method of claim 16 , wherein the silica has a concentration of between 2% and 10% by weight in the electrolyte layer.
18. The method of claim 1 , wherein a portion of the water, which is introduced while rehydrating the water-retaining component by exposing the positive active material layer to the humid environment, is lost during subsequent operations of the method of forming the electrochemical cell.
19. The method of claim 1 , wherein the positive active material is selected from the group consisting of manganese oxide (MnO 2 ), silver oxide (Ag 2 O), nickel oxide (NiO 2 ), nickel oxide hydroxide (NiOOH), vanadium oxide (V 2 O 5 ), ferric phosphate (FePO 4 ), cobalt oxide (COO 2 ), lead oxide (PbO), and chromium oxide (Cr 2 O 3 ).
20. The method of claim 1 , wherein one or both of the positive active material layer or the electrolyte layer comprise carboxymethyl cellulose (CMC).