Inorganic matrix nanoimprint lithographs and methods of making thereof with reduced carbon
The disclosure provides high refractive index ceramic material nanoimprint lithography (NIL) gratings having a relatively lower amount of carbon compared to traditional NIL gratings, and methods of making and using thereof, and devices including such gratings. The ceramic material includes one or more of titanium oxide, zirconium oxide, hafnium oxide, tungsten oxide, zinc tellurium, gallium phosphide, or any combination or derivative thereof.
1. A nanoimprint lithography (NIL) grating comprising a ceramic material having a relative amount of carbon of about 10% or less.
2. The NIL grating of claim 1 , wherein the relative amount of carbon in the ceramic material is about 9% or less, about 8% or less, about 7% or less, about 6% or less, about 5% or less, about 4% or less, about 3% or less, about 2% or less, or about 1% or less.
3. The NIL grating of claim 1 , wherein the ceramic material is substantially free of organic material.
4. The NIL grating of claim 1 , wherein ceramic material comprises one or more of titanium oxide, zirconium oxide, hafnium oxide, tungsten oxide, zinc tellurium, gallium phosphide, or any combination or derivative thereof.
5. The NIL grating of claim 1 , wherein the grating has a duty cycle ranging from 10% to 90%.
6. The NIL grating of claim 1 , wherein the grating has a duty cycle ranging from 30% to 90%.
7. The NIL grating of claim 1 , wherein the grating is a non-slanted grating.
8. The NIL grating of claim 1 , wherein the grating is a slanted grating.
9. The NIL grating of claim 8 , wherein a slant angle ranges from more than 0° to about 70°.
10. The NIL grating of claim 8 , wherein a slant angle is greater than 30°.
11. The NIL grating of claim 1 , wherein the grating has a depth from 30 nm to 450 nm.
12. The NIL grating of claim 1 , wherein the grating has a depth from 50 nm to 350 nm.
13. The NIL grating of claim 1 , wherein the grating has a depth from 75 nm to 250 nm.
14. The NIL grating of claim 1 , wherein the grating has a depth greater than 100 nm and lower than 500 nm.
15. The NIL grating of claim 1 , wherein the grating has an aspect ratio from 0.5:1 to 6:1.
16. The NIL grating of claim 1 , wherein the grating has an aspect ratio from 1:1 to 5:1.
17. The NIL grating of claim 1 , wherein the grating has an aspect ratio greater than 3:1 and lower than 8:1.
18. The NIL grating of claim 1 , wherein the ceramic material has a refractive index ranging from 1.90 to 2.25.
19. The NIL grating of claim 1 , wherein the refractive index is measured at 460 nm.
20. An optical component comprising the NIL grating of claim 1 .