Zn-Ni as a coating layer on self-drilling screws of austenitic stainless steel
A self-drilling screw ( 10 ) having a head ( 20 ), a shaft ( 30 ) at least partially wearing a thread ( 35 ) and a drill point ( 40 ). The base material of the screw ( 10 ) including the drill point ( 40 ) is integrally manufactured from an austenitic 300 series steel with a surface hardness (uncoated) of 400-600 HV 0.3. The surface of the screw has a top coating of Zn—Ni with a Ni-content between 12-15% deposited on the austenitic base material. This self-drilling screw ( 10 ) is manufactured from a blank of raw austenite 300 series steel which is initially squeezed by cold forming to reduce its diameter in a first operation and, in following cold forming operations the head, the drill point and a thread are formed.
1. A self-drilling screw ( 10 ) comprising:
a head ( 20 ),
a shaft ( 30 ) at least partially wearing a thread ( 35 ), and
a drill point ( 40 ),
wherein a base material of the screw ( 10 ) including the drill point ( 40 ) is integrally manufactured from an austenitic 300 series steel with an uncoated surface hardness of 400-600 HV 0.3, and
a coating of Zn—Ni with a Ni-content between 12-15% deposited on the austenitic 300 series steel base material.
2. The self-drilling screw according to claim 1 , wherein the screw ( 10 ) is manufactured from a blank of raw austenite 300 series steel which is initially cold formed to reduce a diameter thereof in a first operation and, in following operations the head, the drill point and the thread are cold formed.
3. The self-drilling screw according to claim 1 , wherein a thickness of the Zn—Ni coating is between 5-30 μm.
4. The self-drilling screw according to claim 1 , wherein the Zn—Ni coating exhibits a Vickers hardness between 410-450 HV0.1.
5. The self-drilling screw according to claim 1 , further comprising a further lubrication coating comprising a wax, a finely dispersed thermoplast or both, on the coating of Zn—Ni.
6. The self-drilling screw according to claim 5 , wherein the further lubrication coating is applied substantially to the drill point and the shaft of the screw.
7. A method of enhancing drilling performance of a self-drilling screw ( 10 ), the method comprising:
manufacturing the self-drilling screw ( 10 ), including a head ( 20 ), a shaft ( 30 ) at least partially wearing a thread ( 35 ) and a drill point ( 40 ), from an austenitic 300 series steel base material with an uncoated surface hardness of 400-600 HV 0.3; and
depositing a Zn—Ni coating with a Ni-content between 12-15% on a surface of the austenitic 300 series steel base material.
8. The method of claim 7 , wherein the Zn—Ni-coating has a thickness between 5-30 μm.
9. The method of claim 7 , wherein the Zn—Ni coating exhibits a Vickers hardness between 410-450 HV0.1.
10. The method of claim 7 , wherein the manufacturing of the self-drilling screw ( 10 ) includes initially cold forming a blank of raw austenite 300 series steel to reduce a diameter thereof in a first operation and, in following operations cold forming the head, the drill point and the thread.