Fabrication method of negative electrode for secondary battery and secondary battery including negative electrode
The present invention provides a fabrication method of a negative electrode for a secondary battery, including: (a) heating a slurry composition for a negative electrode containing a negative electrode active material, a binder, and a solvent to a temperature lower than a boiling point (T b ) of the solvent; (b) applying the heated slurry composition for a negative electrode onto a current collector; and (c) cooling the applied slurry composition for a negative electrode.
1. A fabrication method of a negative electrode for a secondary battery, comprising:
(a) heating a slurry composition for a negative electrode containing a negative electrode active material, a binder, and a solvent to a temperature lower than a boiling point (Tb) of the solvent,
wherein a viscosity (A 1 ) of the slurry composition for a negative electrode before being heated is 20,000 to 70,000 cP;
(b) applying the heated slurry composition for a negative electrode onto a current collector;
(c) cooling the applied slurry composition for a negative electrode, wherein the cooling is performed at a temperature of 10° C. to 30° C. for 5 to 10 seconds; and
(d) drying the cooled slurry composition for a negative electrode, wherein the drying is performed at a temperature of 95° C. or more and less than 130° C. for 50 to 130 seconds, and
wherein a solid in the slurry composition for the negative electrode is contained in an amount of more than 55 parts by weight and 85 parts by weight or less based on 100 parts by weight of the slurry composition for the negative electrode,
wherein a temperature (T) of the heating of the slurry composition for a negative electrode satisfies the following Relational Equation 1:
0.3 T b <T< 0.9 T b [Relational Equation 1]
wherein T b is the boiling point of the solvent
wherein the solvent is water.
2. The fabrication method of a negative electrode for a secondary battery of claim 1 , wherein the slurry composition for a negative electrode satisfies the following Relational Equations 2 and 3:
1.3 ≤A 1 /A 2≤12 [Relational Equation 2]
1.2 ≤A 3 /A 2≤10 [Relational Equation 3]
wherein A1 is a viscosity of the slurry composition for a negative electrode before being heated, A2 is a viscosity of the heated slurry composition for a negative electrode, and A3 is a viscosity of the cooled slurry composition for a negative electrode.
3. A fabrication method of a negative electrode for a secondary battery, comprising:
(a) heating a slurry composition for a negative electrode containing a negative electrode active material, a binder, and a solvent to a temperature lower than a boiling point (T b ) of the solvent,
wherein a viscosity (A 1 ) of the slurry composition for a negative electrode before being heated is 12,000 to 70,000 cP;
(b) applying the heated slurry composition for a negative electrode onto a current collector
(c) cooling the applied slurry composition for a negative electrode,
wherein the cooling is performed at a temperature of 10 to 30° C. for 5 to 10 seconds; and
(d) drying the cooled slurry composition for a negative electrode,
wherein the drying is performed at a temperature of 100° C. or more and less than 120° C. for 60 to 100 seconds, and
wherein a solid in the slurry composition for a negative electrode is contained in an amount of more than 55 parts by weight and 85 parts by weight or less based on 100 parts by weight of the slurry composition for a negative electrode.