Fabrics and garments are disclosed that have dual protection against molten metal splashes and electrical arc flashes. The fabrics can be made from spun yarns containing an intimate blend of fibers. The fibers contained in each yarn can include wool fibers, flame resistant cellulose fibers, and nylon fibers. In one aspect, relatively long wool fibers are incorporated into the yarns.
1. A garment that is resistant to molten metals comprising;
a fabric shaped to cover at least a portion of a wearer's body, the fabric, when tested according to ISO Test 11612, displaying a rating of E3 or D3 and when tested according to ASTM Test F1959 displaying an arc flash value of greater than 8 cal/cm 2 , the fabric comprising a woven fabric made from a plurality of yarns, the fabric comprising warp yarns and fill yarns, the warp yarns and fill yarns comprising a fiber blended yarn, the fiber blended yarn comprising a blend of fibers including:
wool fibers in an amount from about 22% to about 43% by weight of the fabric;
flame resistant cellulose fibers, the flame resistant cellulose fibers being present in the fabric in an amount from about 52% to about 82% by weight;
non-aromatic polyamide, the non-aromatic polyamide being present in an amount from about 6% to about 14% by weight; and
wherein the fiber blended yarn comprises greater than 90% by weight of the fabric.
2. A garment as defined in claim 1 , wherein the wool fibers comprise wool staple fibers having an average fiber length of greater than about 3 inches and less than about 5 inches.
3. A garment as defined in claim 1 , wherein the yarns contained within the woven fabric are made from an intimate blend of the wool fibers, the flame resistant cellulose fibers, and the non-aromatic polyamide fibers.
4. A garment as defined in claim 1 , wherein the woven fabric has a twill weave.
5. A garment as defined in claim 1 , wherein the flame resistant cellulose fibers comprise cotton or rayon fibers pretreated with a fire resistant composition.
6. A garment as defined in claim 1 , wherein the woven fabric contains about 25% to about 40% by weight wool fibers, from about 8% to about 12% by weight non-aromatic polyamide fibers, and from about 55% to about 65% by weight flame resistant cellulose fibers.
7. A garment as defined in claim 1 , wherein the woven fabric has a basis weight of from about 8 osy to about 14 osy.
8. A garment as defined in claim 1 , wherein the cellulose fibers comprise rayon staple fibers having an average fiber length of greater than about 3 inches and less than about 6 inches.
9. A garment as defined in claim 1 , wherein the non-aromatic polyamide fibers comprise staple fibers having an average fiber length of greater than about 3 inches and less than about 6 inches.
10. A garment as defined in claim 1 , wherein the yarns are two ply yarns.
11. A garment as defined in claim 1 , wherein the fabric is made exclusively of the fiber blended yarn.
12. A garment as defined in claim 1 , wherein the fabric comprises about 70 yarns per inch to about 110 yarns per inch in the warp direction and about 45 yarns per inch to about 85 yarns per inch in the fill direction.
13. A garment as defined in claim 1 , wherein the garment comprises a shirt, overalls, trousers, or an apron.
14. A fabric material that is resistant to molten metals comprising a woven fabric made from a plurality of yarns, the fabric comprising warp yarns and fill yarns, the warp yarns and fill yarns comprising a fiber blended yarn, the fiber blended yarn comprising a blend of fibers including:
wool fibers in an amount from about 22% to about 43% by weight of the fabric, the wool fibers comprising wool staple fibers having an average fiber length of greater than about 3 inches and less than about 5 inches;
flame resistant cellulose fibers, the flame resistant cellulose fibers being present in the fabric in an amount from about 52% to about 82% by weight; and
non-aromatic polyamide, the non-aromatic polyamide being present in an amount from about 6% to about 14% by weight.
15. A fabric material as defined in claim 14 , wherein the flame resistant cellulose fibers comprise cotton or rayon fibers pretreated with a fire resistant composition.
16. A fabric material as defined in claim 14 , wherein the woven fabric contains about 25% to about 40% by weight wool fibers, from about 8% to about 12% by weight non-aromatic polyamide fibers, and from about 55% to about 65% by weight flame resistant cellulose fibers.
17. A fabric material as defined in claim 14 , wherein the cellulose fibers comprise rayon staple fibers having an average fiber length of greater than about 3 inches and less than about 6 inches and wherein the non-aromatic polyamide fibers comprise staple fibers having an average fiber length of greater than about 3 inches and less than about 6 inches.
18. A fabric material as defined in claim 14 , wherein the yarns are two ply yarns.
19. A fabric material as defined in claim 14 , wherein the fabric, when tested according to ISO Test 11612, displays a rating of E3 or D3 and when tested according to ASTM Test F1959 displays an arc flash value of greater than 8 cal/cm 2 ; and wherein the fabric, when tested according to ISO Test 11611, displays a rating of A1 under Class 2.
20. A garment that is resistant to molten metals comprising;
a fabric shaped to cover at least a portion of a wearer's body, the fabric comprising a woven fabric made from a plurality of yarns, the fabric comprising warp yarns and fill yarns, the warp yarns and fill yarns comprising an identical fiber blended yarn, the fiber blended yarn comprising a blend of fibers including:
wool fibers in an amount from about 22% to about 43% by weight of the fabric;
flame resistant cellulose fibers, the flame resistant cellulose fibers being present in the fabric in an amount from about 52% to about 82% by weight;
non-aromatic polyamide, the non-aromatic polyamide being present in an amount from about 6% to about 14% by weight; and
wherein the fiber blended yarn comprises greater than 90% by weight of the fabric.