Composite negative electrode active material, method of producing the same, and negative electrode and lithium secondary battery including the same
Provided are a negative electrode active material including a three-dimensional composite. The three-dimensional composite includes secondary particles containing a silicon carbide-based (SiCx, 0<x≤1) nanosheet having a bent portion and amorphous carbon. Also provided are a method of producing the same, and a negative electrode and a lithium secondary battery including the negative electrode active material.
1. A negative electrode active material comprising a three-dimensional composite,
wherein the three-dimensional composite comprises secondary particles containing a silicon carbide-based nanosheet having a bent portion and amorphous carbon, the silicon carbide-based is represented by SiCx, and 0<x≤1.
2. The negative electrode active material of claim 1 , wherein the silicon carbide-based nanosheet has one to three bent portions.
3. The negative electrode active material of claim 1 , wherein 50% or more of the silicon carbide-based nanosheets with respect to the total number has one to three bent portions.
4. The negative electrode active material of claim 1 , wherein the silicon carbide-based nanosheet has a thickness of 10 to 300 nm.
5. The negative electrode active material of claim 1 , wherein the amorphous carbon is at least one selected from the group consisting of soft carbon, hard carbon, a mesophase pitch carbide, and calcined coke.
6. The negative electrode active material of claim 1 , wherein the three-dimensional composite contains the silicon carbide-based nanosheet in a state of being uniformly dispersed in the composite particles.
7. The negative electrode active material of claim 1 , wherein the three-dimensional composite contains the silicon carbide-based nanosheet and the amorphous carbon at a weight ratio of 5:5 to 9:1.
8. The negative electrode active material of claim 1 , wherein the three-dimensional composite has a particle diameter of 1 to 50 μm.
9. A method of producing the negative electrode active material of claim 1 , the method comprising:
a chemical vapor deposition process of coating a silicon carbide-based compound precursor on an water-soluble salt;
a process of etching the water-soluble salt to prepare a silicon carbide-based nanosheet; and
a process of mixing the silicon carbide-based nanosheet and amorphous carbon to prepare a three-dimensional composite,
wherein the silicon carbide-based is represented by SiCx, and 0<x≤1.
10. The method of producing a negative electrode active material of claim 9 , wherein the silicon carbide-based compound precursor comprises a silicon-based inorganic compound and an ethylene-based hydrocarbon gas.
11. The method of producing a negative electrode active material of claim 9 , wherein the chemical vapor deposition process is to coat the silicon carbide-based compound precursor on the water-soluble salt at a thickness of 10 to 300 nm.
12. A lithium secondary battery comprising: a negative electrode comprising the negative electrode active material of claim 1 ; a positive electrode comprising a positive electrode active material; a separator interposed between the negative electrode and the positive electrode; and an electrolyte solution.