Annealing separator composition for grain-oriented electrical steel sheet, grain-oriented electrical steel sheet, and method for manufacturing grain-oriented electrical steel sheet
An oriented electrical steel sheet according to an embodiment of the present invention includes: a base texture; an AI permeation layer positioned on the base texture; and a film positioned on the AI permeation layer, wherein the AI permeation layer includes AI at 0.5 to 5 wt %, and the film includes an Al—Mg composite.
1. An oriented electrical steel sheet comprising:
a base texture;
an AI permeation layer positioned on the base texture; and
a film positioned on the AI permeation layer,
wherein the AI permeation layer includes AI at 0.5 to 5 wt %, and
the film includes an Al—Mg composite, and
the film consists of 0.1 to 10 wt % of Al, 5 to 30 wt % of Mg, 0.1 to 20 wt % of Si, 10 to 55 wt % of O, and the balance of Fe.
2. The oriented electrical steel sheet of claim 1 , wherein
the film has a thickness of 0.1 to 10 μm.
3. The oriented electrical steel sheet of claim 1 , wherein
the AI permeation layer includes α-oxide aluminum.
4. The oriented electrical steel sheet of claim 3 , wherein
an occupied area of the α-oxide aluminum relative to the AI permeation layer area is 0.1 to 50% with respect to the cross-section in the thickness direction of the steel sheet.
5. The oriented electrical steel sheet of claim 1 , wherein
the AI permeation layer has a thickness of 0.1 to 10 μm.
6. The oriented electrical steel sheet of claim 1 , wherein
the base texture includes silicon (Si) at 2.0 to 7.0 wt %, aluminum (Al) at 0.020 to 0.040 wt %, manganese (Mn) at 0.01 to 0.20 wt %, phosphorus (P) at 0.01 to 0.15 wt %, carbon (C) at 0.01 wt % or less (excluding 0%), N at 0.005 to 0.05 wt %, and 0.01 to 0.15 wt % of antimony (Sb), tin (Sn), or a combination thereof, and the balance includes Fe and other inevitable impurities.