Composite materials based on dual-cure urethane polymers and dual-cure isocyanurate polymers
The invention relates to reaction mixtures having a high ratio of isocyanate groups to isocyanate-reactive groups, which reaction mixtures mostly cure through the formation of isocyanurate groups, and to the use of such reaction mixtures for producing semifinished materials.
1. A reaction mixture having a molar ratio of isocyanate groups to isocyanate-reactive groups of 2:1 to 10:1 comprising
a) a polyisocyanate composition A having a proportion of aliphatically and/or cycloaliphatically bonded isocyanate groups based on a total amount of isocyanate groups present of at least 80 mol %;
b) an isocyanate-reactive component B;
c) at least one catalytic functionality C1 which catalyzes a reaction of isocyanate groups with isocyanate-reactive groups to afford urethane and/or urea groups; and
d) at least one catalytic functionality C2 which catalyzes a reaction of isocyanate groups to afford isocyanurate groups,
wherein the catalytic functionalities C1 and C2 are brought about by the same compound or by at least two different compounds and a type and amount of the catalytic functionalities C1 and C2 is such that in a temperature range between 10° C. and 50° C. the reaction of isocyanate groups to afford urethane and/or urea groups proceeds at least twice as fast as all other reactions in which isocyanate groups are consumed in the reaction mixture.
2. The reaction mixture as claimed in claim 1 , wherein the catalytic functionality C1 has a reaction rate coefficient for the reaction of isocyanate groups k(T) ISOC1 at temperatures of at most 50° C. which is larger than a reaction rate coefficient k(T) ISOC2 of the catalytic functionality C2 by at least a factor of 2.
3. The reaction mixture as claimed in claim 1 , wherein the isocyanate-reactive component B has a number-average molecular weight of at most 21 000 g/mol.
4. The reaction mixture as claimed in claim 1 , wherein the isocyanate-reactive component B on average has an OH number between 100 and 2000 mg KOH/g.
5. The reaction mixture as claimed in claim 1 , wherein a proportion of physical and chemical blowing agents in the reaction mixture is at most 1% by weight based on a total weight of the reaction mixture.
6. The reaction mixture as claimed in claim 1 , wherein the reaction mixture has a pot life of at least 5 minutes, wherein the pot life is defined as the time elapsed until doubling of the viscosity of the reaction mixture at a temperature of 23° C.
7. A fiber D wetted with the reaction mixture as claimed in claim 1 .
8. A process for producing a semifinished product containing
a) providing a reaction mixture having a molar ratio of isocyanate groups to isocyanate-reactive groups of 2:1 to 10:1 comprising:
(i) a polyisocyanate composition A;
(ii) an isocyanate-reactive component B;
(iii) at least one catalytic functionality C1 which catalyzes a reaction of isocyanate groups with isocyanate-reactive groups to afford urethane and/or urea groups; and
(iv) at least one catalytic functionality C2 which catalyzes a reaction of isocyanate groups to afford isocyanurate groups,
wherein the catalytic functionalities C1 and C2 are brought about by the same compound or by at least two different compounds;
and
b) crosslinking the polyisocyanate component A and the isocyanate-reactive component B by temperature-controlling the reaction mixture to a temperature between 10° C. and 50° C.
9. The process as claimed in claim 8 , wherein after performance of process step b) the reaction mixture has a modulus G′ of at least 1*10 4 Pa as determined by a plate/plate rheometer according to ISO 6721-10:2015-09 at 1/s at 23° C.
10. The process as claimed in claim 8 , wherein the reaction mixture provided in process step a) is applied to a fiber before performance of process step b).
11. A semifinished product obtained by the process as claimed in claim 8 .
12. A method of producing a product, comprising producing the product, at least in part, with the semifinished product as claimed in claim 11 , wherein the product comprises profiles, beams, reinforcing struts, sporting goods, manhole covers, plates, housings, parcel shelves, engine bay covers, leaf springs, bumpers, trim pieces, aprons, pipes, pressure vessels, or tanks.
13. A process for producing a polyisocyanurate plastic, wherein a semifinished product produced by a process as claimed in claim 8 is subjected to catalytic trimerization by heating to a temperature of at least 60° C.
14. The process as claimed in claim 13 , wherein the catalytic trimerization is performed at a location at least 10 m away from a location at which urethanization to produce the semifinished product is carried out.
15. The process as claimed in claim 13 , wherein at least 80% of free isocyanate groups present in the semifinished product are consumed during the catalytic trimerization.
16. A polyisocyanurate plastic obtainable by the process as claimed in claim 13 .