Porous materials for energy management
Method for preparing porous polyurethane materials with controlled pore size and shape using isocyanates, polyols, and additives, and the porous polyurethane materials prepared therefrom. Method for preparing porous polyimides using at least one polyamine and a dianhydride and the porous polyimides materials prepared therefrom. The porous materials are useful for energy management, such as thermal, impact and vibration energy, and can exhibit improved fire-resistant performance.
1. A method for preparing a porous polyurethane material, the method comprising:
providing a first composition comprising an isocyanate and a polyol mixture, wherein the isocyanate comprises an aryl isocyanate and the polyol mixture is at least one hydroxyl terminated polyether polyol, ethylene glycol and hydroxyl terminated silicone oil;
providing a second composition comprising at least one polyol, a blowing agent, optionally a pore forming agent, optionally a surfactant, a catalyst, and at least two solvents; and
combining the first composition and the second composition thereby forming the porous polyurethane material.
2. The method of claim 1 , wherein the isocyanate further comprises an alkyl diisocyanate, an alkenyl diisocyanate, a cycloalkyl diisocyanate, an aralkyl diisocyanate, or a mixture thereof.
3. The method of claim 1 , wherein the aryl isocyanate comprises a diphenylmethane diisocyanate, a phenylene diisocyanate, a toluene diisocyanate, a naphthalene diisocyanate, or mixtures thereof.
4. The method of claim 1 , wherein the blowing agent is water and the pore forming agent is a monohydric alkyl alcohol.
5. The method of claim 1 , wherein the catalyst is a Brønsted base or a Lewis acid.
6. The method of claim 1 , wherein the catalyst is selected from the group consisting of bis(2-dimethylaminoethyl) ether, trimethylamine, triethanolamine and 1, 4 diazabicyclo [2.2.2] octane, zinc naphthenate, dibutyltin dilaurate, and mixtures thereof.
7. The method of claim 1 , wherein the hydroxyl terminated silicone oil is a polydimethylsiloxane with an average molecular weight of 400 to 700.
8. The method of claim 1 , wherein the aryl isocyanate and hydroxyl terminated silicone oil are present in a mass ratio of 100:2 to 100:5.
9. The method of claim 1 , wherein the at least two solvents comprise an ether and at least one solvent selected from the group consisting of a fluoroether, acetonitrile, dimethyl sulfoxide, acetone, acetylacetone, and mixtures thereof.
10. The method of claim 9 further comprising the step of exchanging the at least one of the at least two solvents with a fluoroether or acetone; and removing the fluoroether or acetone by supercritical drying after the step of combining the first composition and the second composition thereby forming the porous polyurethane material.
11. The method of claim 1 , wherein the method comprises:
providing the first composition comprising the isocyanate selected from the group consisting of a diphenylmethane diisocyanate, a phenylene diisocyanate, a toluene diisocyanate, and a naphthalene diisocyanate; at least one hydroxyl terminated polyether polyol, ethylene glycol and hydroxyl terminated polydimethylsiloxane;
providing the second composition comprising at least one polyol independently selected from the group consisting of hydroxyl-terminated polybutadiene, hydroxyl-terminated polyether polyols, hydroxyl-terminated polyester polyol, 1,4-butanediol, cyclohexane dimethanol, ethylene glycol, hydroquinone bis(2-hydroxyethyl)ether, trimethylol propane, 1,4-butanediol, 1,6-hexanediol, and a dipropylene glycol; optionally a monohydric alkyl alcohol; water; at least two solvents, wherein one of the at least two solvents is tetrahydrofuran and at least one solvent selected from the group consisting of a 1,1,2,2-tetrafluoroethyl 2,2,2-trifluoroethyl ether, acetonitrile, dimethyl sulfoxide, acetone, acetylacetone; and a catalyst selected from the group consisting of bis(2-dimethylaminoethyl) ether, trimethylamine, triethanolamine and 1, 4 diazabicyclo [2.2.2] octane, zinc naphthenate, and dibutyltin dilaurate;
combining the first composition and the second composition;
exchanging at least a portion of the at least two solvents with 1,1,2,2-tetrafluoroethyl 2,2,2-trifluoroethyl ether or acetone; and removing the 1,1,2,2-tetrafluoroethyl 2,2,2-trifluoroethyl ether or acetone by supercritical drying thereby forming the porous polyurethane material.
12. The method of claim 1 , wherein the polyol mixture is present at a weight percentage between 1-20% relative to the weight of the isocyanate and the polyol mixture.