Solid electrolyte material and solid-state battery made therewith

1. A solid electrolyte material comprising Li, T, X and A, wherein T comprises Sb; X comprises one or more halogens, pseudo-halogens, or N; A comprises one or more of S or Se; and wherein the solid electrolyte material has peaks at 2θ=14.5°±0.50°, 16.8°±0.50°, 23.9°±0.50°, 28.1°±0.50°, and 32.5°±0.50 in X-ray diffraction measurement with Cu-Kα(1,2)=1.54064 Å.

2. The solid electrolyte material of claim 1 comprising a formula:

Li 1-a-b-c T a A b X c

wherein 0.074<a≤0.105, 0.370<b≤0.421, 0.074<c≤0.105.

3. The solid electrolyte material of claim 2 , wherein a=0.1, b=0.4, c=0.1, T=Sb, A=S, and X=I.

4. The solid electrolyte material of claim 1 , wherein T comprises a blend of Sb and non-Sb elements selected from the group consisting of P, As, Si, Ge, Al, B, and W.

5. The solid electrolyte material of claim 1 , wherein a proportion of Sb to total element T is 1% or greater.

6. The solid electrolyte material of claim 1 , comprising at least one of glass ceramic phases, crystalline phases and mixed phases and further comprising an ionic conductivity greater than about 0.500 mS/cm at room temperature.

7. The solid electrolyte material of claim 6 , wherein the mixed phases comprise other crystalline phases containing peaks at 20.2°±0.50° and 23.6°±0.50°, and/or 21.0°±0.50° and 28.0°±0.50°, and/or 17.5°±0.50° and 18.2°±0.50°, and/or 17.1° and 25.8° in X-ray diffraction measurement with Cu-Kα(1,2)=1.5418 Å.

8. A lithium solid-state battery comprising a positive electrode active material layer containing a positive electrode active material; a negative electrode active material layer containing a negative electrode active material; and a solid electrolyte layer disposed between the positive electrode active material layer and the negative electrode active material layer, wherein at least one of the positive electrode active material layer, the negative electrode active material layer, and the solid electrolyte layer comprises a solid electrolyte material comprising Li, T, X and A, wherein T comprises Sb; X comprises one or more halogens, pseudo-halogens, or N; A comprises one or more of S or Se; and wherein the solid electrolyte material has peaks at 2θ=14.5°±0.50°, 16.8°±0.50°, 23.9°±0.50°, 28.1°±0.50°, and 32.5°±0.50 in X-ray diffraction measurement with Cu-Kα(1,2)=1.54064 Å.

9. The lithium solid-state battery of claim 8 , wherein the solid electrolyte material comprises the formula Li 1-a-b-c T a A b X c wherein 0.074<a≤0.105, 0.370<10.421, 0.074<c≤0.105.

10. The lithium solid-state battery of claim 9 , wherein a=0.1, b=0.4, c=0.1, T=Sb, A=S, and X=I.

11. The lithium solid-state battery of claim 8 , wherein T further comprises a blend of Sb and non-Sb elements selected from the group consisting of Sb, P, As, Si, Ge, Al, B, and W.

12. The lithium solid-state battery of claim 8 , wherein a proportion of Sb to total element T is 1% or greater.

13. The lithium solid-state battery of claim 8 , wherein the solid-electrolyte material comprises at least one of glass, ceramic phases, crystalline phases or mixed phases.

14. The lithium solid-state battery of claim 13 , wherein the mixed phases comprise other crystalline phases containing peaks at 20.2°±0.50° and 23.6°±0.50°, and/or 21.0°±0.50° and 28.0°±0.50°, and/or 17.5°±0.50° and 18.2°±0.50°, and/or 17.1° and 25.8° in X-ray diffraction measurement with Cu-Kα(1,2)=1.5418 Å.

15. The lithium solid-state battery of claim 8 wherein the positive electrode active material comprises one or more particles, wires, or filaments comprising at least one of aluminum, nickel, titanium, stainless steel, magnesium, iron, zinc, indium, germanium, silver, platinum, gold, lithium or alloy thereof.

16. The lithium solid-state battery of claim 8 wherein the negative electrode active material comprises at least one of an alkali metal comprising lithium metal, lithium alloys, sodium metal, sodium alloys, potassium metal, potassium alloys; or at least one of an alkali earth metal comprising magnesium metal, magnesium alloys, calcium metal, calcium alloys; and optionally wherein the negative electrode active material further comprises silicon, tin, iron, germanium, or indium.

17. The lithium solid-state battery of claim 8 , wherein the positive electrode active material layer and the negative electrode active material layer each comprise one or more carbon containing materials comprising carbon fiber, graphite, graphene, carbon black, conductive carbon, amorphous carbon, VGCF, and carbon nanotubes; and wherein the carbon containing materials are added in the amount of 2% by mass to 50% by mass of the respective positive electrode active material layer or the negative electrode active material layer.

18. The lithium solid-state battery of claim 8 , wherein the positive electrode active material layer and the negative electrode active material layer each comprise one or more of metal particles, filaments, or other structures;

wherein the positive electrode active material layer and the negative electrode active material layer each further comprise one or more binders or polymers comprising a fluororesin containing vinylidene fluoride (VdF), hexafluoropropylene (HFP), tetrafluoroethylene (TFE), and derivatives thereof;

wherein the positive electrode active material layer and the negative electrode active material layer each further comprise one or more binders or polymers comprising homopolymers comprising polyvinylidene fluoride (PVdF), polyhexafluoropropylene (PHFP), or polytetrafluoroethylene (PTFE), or binary copolymers comprising copolymers of VdF and HFP comprising poly(vinylene difluoride-hexafluoropropylene) copolymer (PVdF-HFP);

wherein the positive electrode active material layer and the negative electrode active material layer each further comprise one or more binders or polymers comprising thermoplastic elastomers comprising styrene-butadiene rubber (SBR), styrene-butadiene-styrene copolymer (SBS), styrene-isoprene block copolymer (SIS), styrene-ethylene-butylene-styrene (SEBS), polyacrylonitrile (PAN), nitrile-butylene rubber (NBR), polybutadiene, polyisoprene, or poly(methacrylate) nitrile-butadiene rubber (PMMA-NBR);

wherein the positive electrode active material layer and the negative electrode active material layer each further comprise one or more binders or polymers comprising an acrylic resin comprising polymethyl (meth) acrylate, polyethyl (meth) acrylate, polyisopropyl (meth) acrylate polyisobutyl (meth) acrylate, polybutyl (meth) acrylate;

wherein the positive electrode active material layer and the negative electrode active material layer each further comprise one or more binders or polymers comprising a polycondensation polymer comprising polyurea, polyamide paper, or polyimide, polyester; or

wherein the positive electrode active material layer and the negative electrode active material layer each further comprise one or more binders or polymers comprising nitrile rubber comprising acrylonitrile-butadiene rubber (ABR), polystyrene nitrile-butadiene rubber (PS-NBR), or mixtures thereof.

19. The lithium solid-state battery of claim 8 , wherein the positive electrode active material layer and the negative electrode active material layer each comprise one or more binders or polymers present in the amount of 1% mass to 80% by mass.

20. The lithium solid-state battery of claim 8 , wherein the lithium solid-state battery does not comprise a negative electrode and the negative electrode active material possesses sufficient electronic activity and mechanical strength so as to act as a negative electrode.

21. The lithium solid-state battery of claim 8 , wherein the positive electrode active material layer comprises Li(Ni a Co b Mn c )O 2 wherein 0<a≤1, 0<b≤1, 0<c≤1, a+b+c=1;

wherein the positive electrode active material layer comprises Li(Ni 0.33 Co 0.33 Mn 0.33 )O 2 , Li(Ni 0.4 Co 0.3 Mn 0.3 )O 2 , Li(Ni 0.5 Co 0.2 Mn 0.3 )O 2 , Li(Ni 0.6 Co 0.2 Mn 0.2 )O 2 , Li(Ni 0.8 Co 0.1 Mn 0.1 )O 2 or a combination thereof;

wherein the positive electrode active material layer comprises one or more metal oxides comprising V 2 O 5 , V 6 O 13 , MoO 3 , LiCoO 2 , LiNiO 2 , LiMnO 2 , LiMn 2 O 4 , LiNi 1-Y Co Y O 2 , LiCo 1-Y Mn Y O 2 , LiNi 1-Y Mn Y O 2 (0≤Y<1), Li(Ni a Co b Mn c )O 4 (0<a<2, 0<b<2, 0<c<2, a+b+c=2), LiMn 2-Z Ni Z O 4 , LiMn 2-Z Co Z O 4 (0<Z<2), LiCoPO 4 , LiFePO 4 , CuO, Li(NiaCobAlc)O 2 (0<a<1, 0<b<1, 0<c<1, a+b+c=1) or a combination thereof; or

wherein the positive electrode active material layer comprises one or more of a metal sulfide including titanium sulfide (TiS 2 ), molybdenum sulfide (MoS 2 ), iron sulfide (FeS, FeS 2 ), copper sulfide (CuS), nickel sulfide (Ni 3 S 2 ) and lithium sulfide (Li 2 S), or combination thereof.

22. The lithium solid-state battery of claim 8 , wherein the positive electrode active material is present in the amount of 20% by mass to 99% by mass.

23. The lithium solid-state battery of claim 8 , wherein the negative electrode active material is present in the amount of 20% by mass to 99% by mass.

24. The lithium solid-state battery of claim 8 , wherein the positive electrode active material layer comprises one or more of Li 2 S—P 2 S 5 , Li 2 S—P 2 S 5 —LiI, Li 2 S—P 2 S 5 —GeS 2 , Li 2 S—P 2 S 5 —Li 2 O, Li 2 S—P 2 S 5 —Li 2 O—LiI, Li 2 S—P 2 S 5 —LiI—LiBr, Li 2 S—SiS 2 , Li 2 S—SiS 2 —LiI, Li 2 S—SiS 2 —LiBr, Li 2 S—S—SiS 2 —LiCl, Li 2 S—S—SiS 2 —B 2 S 3 —LiI, Li 2 S—S—SiS 2 —P 2 S 5 —LiI, Li 2 S—B 2 S 3 , Li 2 S—P 2 S 5 —Z m S n (where m and n are positive numbers, and Z is Ge, Zn or Ga), Li 2 S—GeS 2 , Li 2 S—S—SiS 2 —Li 3 PO 4 , and Li 2 S—S—SiS 2 —Li x MO y (where x and y are positive numbers, and M is P, Si, Ge, B, Al, Ga or In);

wherein the positive electrode active material layer comprises one or more of Li 3 PS 4 , Li 4 P 2 S 6 , Li 7 P 3 S 11 , Li 10 GeP 2 S 12 , Li 10 SnP 2 S 12 ;

wherein the positive electrode active material layer comprises one or more of Li 6 PS 5 Cl, Li 6 PS 5 Br, Li 6 PS 5 I or expressed by the formula Li 7-y PS 6-y X y wherein X represents at least one halogen elements and or pseudo-halogen and where 0<y≤2.0 and wherein a halogen comprises one or more of F, Cl, Br, I, and a pseudo-halogen comprises one or N, NH, NH 2 , NO, NO 2 , BF 4 , BH 4 , AlH 4 , CN, and SCN; or

wherein the positive electrode active material layer comprises one of more of a Li 8-y-z P 2 S 9-y-z X y X y W z wherein X and W represents at least one halogen elements and or pseudo-halogen and wherein 0≤y≤1 and 0≤z≤1) and wherein a halogen comprises one or more of F, Cl, Br, I, and a pseudo-halogen comprises one or N, NH, NH, NO, NO 2 , BR 4 , CN, and SCN.

25. The lithium solid-state battery of claim 8 , wherein the positive electrode active material layer comprises a thickness in the range of 1 micron to 1000 microns.

26. The lithium solid-state battery of claim 8 , wherein the negative electrode active material layer comprises a thickness in the range of 500 nanometers to 1000 microns.

27. The lithium solid-state battery of claim 8 , wherein the solid electrolyte layer material layer comprises a thickness in the range of 500 nanometers to 1000 microns.

28. The lithium solid-state battery of claim 8 , wherein the solid electrolyte material is present in the positive electrode active material layer, the negative electrode active material layer, or the solid electrolyte layer in the amount of 5% by mass to 80% by mass.

29. A method for producing a sulfide solid electrolyte material including glass ceramics comprising: Li, T, X and A wherein T is at least one of Sb, P, As, Si, Ge, Al, B, and W; X is one or more halogens, pseudo-halogens, or N; A is one or more of S or Se; the method comprising mixing and milling a raw material composition containing an element A or compound Li2A, an element T or sulfide of T, and a compound LiX or Li3N to render the mixture amorphous under x-ray diffraction; and/or heating the sulfide glass at a heat treatment temperature equal to or greater than a crystallization temperature of the sulfide glass to synthesize the glass ceramics having peaks at 2θ=14.5°±0.50°, 16.8°±0.50°, 23.9°±0.50°, 28.1°±0.50°, and 32.5°±0.50 in X-ray diffraction measurement with Cu-Kα(1,2)=1.54064 Å.