Transparent and antistatic PMMA composition
A transparent antistatic composition based on polymethyl methacrylate (PMMA), including: 55% to 99.9% by weight of PMMA, and 0.1% to 45% by weight of at least one polyamide (PA) block-containing and polyether (PE) block-containing copolymer (PEBA) comprising polyethylene glycol (PEG), with respect to the total composition weight, the copolymer includes in the range 50% to 80% by weight of PEG with respect to the total weight of copolymer.
1. A transparent antistatic composition based on polymethyl methacrylate (PMMA), comprising:
65% to 93% by weight of PMMA,
7% to 35% by weight of at least one polyamide (PA) block-containing and polyether (PE) block-containing copolymer (PEBA) comprising polyethylene glycol (PEG), and
0.1% to 5% by weight of at least one organic salt in the molten state,
with respect to the total composition weight,
wherein said copolymer comprises about 60% by weight of PEG with respect to the total weight of copolymer,
in which said copolymer is selected from: PA6-PEG, PA11-PEG, PA12-PEG, PA10.10-PEG, PA10.12-PEG and mixtures thereof,
wherein the composition has a haze value less than 10%.
2. The composition of claim 1 , in which said copolymer consists of polyamide 11 blocks and PEG blocks.
3. The composition of claim 1 , in which said copolymer further comprises at least one polyether other than PEG selected from polytetramethylene glycol (PTMG), polypropylene glycol (PPG), polytrimethylene glycol (PO3G), and mixtures thereof.
4. The composition of claim 1 , in which said copolymer is a segmented block copolymer comprising three different types of blocks and is chosen from copolyetheresteramides and copolyetheramideurethanes.
5. The composition of claim 1 , in which said copolymer has an inherent viscosity of 2 or less.
6. The composition of claim 1 , further comprising at least one agent improving the surface conductivity selected from: hygroscopic agents, fatty acids, lubricants, metals, metallic films, metallic powders, metallic nanopowders, aluminosilicates, amines, esters, fibers, carbon black, carbon fibers, carbon nanotubes, polyethylene glycol, intrinsically conductive polymers, masterbatches, and mixtures thereof.
7. The composition of claim 1 , wherein the composition possesses a surface resistivity of less than 10 12 ohm/square measured in accordance with the standard ASTM D257.
8. The composition of claim 1 , wherein the composition has a haze value less than 4%.
9. The composition of claim 1 , wherein the organic salt has a fusion temperature of less than 300° C.
10. The composition of claim 1 , wherein the composition comprises 70% to 93% by weight of PMMA.
11. The composition of claim 1 , wherein the at least one organic salt in the molten state comprises at least one cation selected from the group consisting of:
ammonium, sulfonium, pyridinium, pyrrolidinium, imidazolium, imidazolinium, phosphonium, lithium, guanidinium, piperidinium, thiazolium, triazolium, oxazolium, pyrazolium, and mixtures thereof.
12. The composition of claim 1 , wherein the at least one organic salt in the molten state comprises at least one anion selected from the group consisting of: imides, borates, phosphates, phosphinates, phosphonates, amides, aluminates, halides, cyanates, acetates, sulfonates, sulfates, and mixtures thereof.
13. The composition of claim 1 , wherein the at least one organic salt in the molten state is a disubstituted imidazole, a monosubstituted imidazole or a trisubstituted imidazole.
14. The composition of claim 1 , wherein the composition further comprises at least one inorganic salt.
15. The composition of claim 1 , wherein the composition comprises:
70% to 93% by weight of PMMA,
7% to 30% by weight of at least one polyamide (PA) block-containing and polyether (PE) block-containing copolymer (PEBA) comprising polyethylene glycol (PEG).