Aspects described herein generally relate to a method of coating a metallic surface. The method includes forming a solution including a corrosion inhibitor having one or more thiol moieties and a hydroxide. The metallic surface is coated with the solution to form a treated metallic surface. The treated metallic surface is further coated with an organosilane, an acid, and a metal alkoxide to form a coating system.
1. A method of coating a metallic surface, comprising:
forming a first solution having a pH 3.5 to about 4.5, the solution comprising a corrosion inhibitor having one or more thiol moieties, a hydroxide, an acid, and a metal alkoxide;
coating the metallic surface with the first solution to form a treated metallic surface;
curing the treated metallic surface at a pressure of about 760 Torr to about 3 Torr and a temperature of about 10° C. to about 50° C.;
coating the treated metallic surface with a second solution comprising an organosilane containing solid dissolved in a solvent; and
curing the treated metallic surface with the second solution to form a coating system.
2. The method of claim 1 , wherein the hydroxide is selected from a group consisting of aluminum hydroxide, sodium hydroxide, potassium hydroxide, lithium hydroxide, and any combination thereof.
3. The method of claim 1 , wherein curing the treated metallic surface with the second solution at about 10° C. to about 50° C. at a pressure of about 760 Torr to about 3 Torr.
4. The method of claim 1 , wherein the acid is acetic acid.
5. The method of claim 1 , wherein:
coating the metallic surface comprises spraying, dip coating, or a combination thereof; and
coating the treated metallic surface comprises spraying, dip coating, or a combination thereof.
6. The method of claim 1 , wherein a weight fraction of the hydroxide in the first solution is about 0.1 wt % to about 10 wt %.
7. The method of claim 1 , wherein the coating system is substantially free of insoluble corrosion inhibitor.
8. The method of claim 1 , wherein the treated metallic surface is cured at about 600 Torr to about 3 Torr.
9. The method of claim 8 , wherein the treated metallic surface is cured at about 20° C. to about 50° C.
10. The method of claim 1 , wherein the treated metallic surface with the second solution is cured at about 600 Torr to about 3 Torr.
11. The method of claim 10 , wherein the treated metallic surface with the second solution is cured at about 40° C. to about 50° C.
12. The method of claim 1 , wherein the organosilane containing solid comprises an organosilane and an alcohol.
13. The method of claim 12 , wherein the organosilane comprises about 98 wt % to about 99.9 wt % of the organosilane containing solid.
14. The method of claim 12 , wherein the alcohol comprises about 0.1 wt % to about 1 wt % of the organosilane containing solid.
15. The method of claim 12 , wherein the alcohol is an alkyl alcohol.
16. The method of claim 15 , wherein the alkyl alcohol is methyl alcohol.
17. The method of claim 12 , wherein the solvent of the second solution is either propanol or isopropanol.
18. The method of claim 17 , wherein the solvent of the second solution is propanol.
19. The method of claim 18 , wherein the second solution comprises a weight ratio of organosilane to propanol of about 1:20 to about 3:5.
20. The method of claim 18 , wherein the second solution comprises a weight ratio of organosilane to propanol of about 1:10 to about 1:5.