Positive electrode active material for lithium secondary battery, method of preparing the same, and lithium secondary battery including the positive electrode active material
The present invention relates to a positive electrode active material for a lithium secondary battery which includes a lithium composite transition metal oxide including nickel (Ni), cobalt (Co), and manganese (Mn), wherein a portion of nickel (Ni) sites of the lithium composite transition metal oxide is substituted with tungsten (W), and an amount of a lithium tungsten oxide remaining on surfaces of lithium composite transition metal oxide particles is 1,000 ppm or less.
1. A method of preparing a positive electrode active material for a lithium secondary battery, the method comprising:
preparing a metal solution including a nickel-containing raw material, a cobalt-containing raw material, a manganese-containing raw material, and a tungsten-containing raw material;
preparing a positive electrode active material precursor by a co-precipitation reaction of the metal solution;
mixing and sintering the positive electrode active material precursor and a lithium raw material to prepare a lithium composite transition metal oxide in which a portion of nickel sites is substituted with tungsten; and
washing the sintered lithium composite transition metal oxide to remove a lithium tungsten oxide remaining on a surface of the lithium composite transition metal oxide.
2. The method of claim 1 , wherein the tungsten-containing raw material comprises at least one of Na 2 WO 4 , WO 3 , or H 2 WO 4 .
3. The method of claim 1 , wherein the metal solution comprises the tungsten-containing raw material in an amount of 0.05 mol % to 0.5 mol % based on a total of the nickel-containing raw material, the cobalt-containing raw material, the manganese-containing raw material, and the tungsten-containing raw material.
4. The method of claim 1 , wherein the positive electrode active material precursor is represented by Formula 2:
Ni 1−x2−y2−z2 W z2 Co x2 M 1 y2 (OH) 2 Formula 2
wherein, in Formula 2, 0<x 2 ≤0.2, 0<y 2 ≤0.2, and 0<z 2 ≤0.2, and M1 comprises at least one of Mn or Al.
5. The method of claim 4 , wherein, in Formula 2, 0<x 2 +y 2 +z 2 ≤0.2 is satisfied.
6. The method of claim 1 , wherein a sintering temperature is in a range of 700° C. to 900° C.
7. The method of claim 1 , wherein the washing is performed in a temperature range of −10° C. to 30° C.
8. The method of claim 1 , wherein the lithium composite transition metal oxide contains tungsten in an amount of 10 ppm to 5,000 ppm in a crystal structure.
9. The method of claim 1 , wherein an amount of the lithium tungsten oxide remaining on a surface of a lithium composite transition metal oxide particle after the washing is 1,000 ppm or less.