An elastomeric article is formed from a blend of nitrile rubber and polychloroprene rubber. The elastomeric article can be a glove, such as a medical exam glove. The elastomeric article is softer than a conventional nitrile elastomeric article. The elastomeric article is formed from a blended rubber latex emulsion of nitrile and polychloroprene. The blended rubber latex emulsion may be free of sulfur and vulcanization accelerators.
1. An elastomeric article comprising: an article comprising a flexible layer of elastomeric material, wherein the elastomeric material is formed from a blended emulsion of nitrile rubber and chloroprene rubber, the article having a first surface and a second surface,
wherein the blended emulsion comprises a divalent metal oxide and a trivalent crosslinker, and
wherein the blended emulsion is free from sulfur and free from a dithiocarbamate accelerator, zincediethyldithiocarbamate (ZDEC), zinc mercaptobenzothiazole (ZMBT), diphenyl guanidine (DPG), or a combination thereof.
2. The elastomeric article of claim 1 , wherein the ratio of nitrile rubber to chloroprene rubber in the blended emulsion is in a range from about 50:50 to about 95:5.
3. The elastomeric article of claim 1 , wherein the blended emulsion includes a solids content of between about 15 percent and about 30 percent, by weight.
4. The elastomeric article of claim 1 , wherein coagulation of the blended emulsion to form the elastomeric article is accelerated by the crosslinker.
5. The elastomeric article of claim 1 , wherein the article is a glove.
6. The elastomeric article of claim 5 , wherein the first surface is a donning side of the glove and the second surface is a grip side of the glove.
7. The elastomeric article of claim 1 , wherein coagulation of the blended emulsion to form the elastomeric article is accelerated by a metallic salt, wherein the metallic salt includes nitrate, sulfate, or chloride salts of calcium, aluminum, or zinc, or a combination thereof.
8. The elastomeric article of claim 7 , wherein coagulation of the blended emulsion to form the elastomeric article is further accelerated by the trivalent crosslinker.
9. The elastomeric article of claim 8 , wherein the metallic salt is a divalent compound.
10. The elastomeric article of claim 8 , wherein the metallic salt is calcium nitrate.
11. The elastomeric article of claim 8 , wherein the trivalent crosslinker is a metallic oxide that forms bonds with carboxyl groups of the nitrile rubber.