Process for preparing a polyamide, a nylon salt to be used therein and a process for making the salt
Processes for preparing a polyamide, a polyamide material obtained by such processes, a nylon salt to be used therein, and processes for making the nylon salt are disclosed. The processes for preparing the polyamide include a direct solid state polymerization process. The salt used herein is a granulate material, prepared by a process, comprising spraying an aqueous solution comprising a diamine and a dicarboxylic acid dissolved in an aqueous medium, or an aqueous slurry comprising a diammonium dicarboxylate salt dispersed in an aqueous medium directly obtained from such an aqueous solution, onto or in a fluidized bed of diammonium dicarboxylate salt particles, while evaporating the aqueous medium, thereby forming a granulate salt material.
1. A process for preparing a polyamide comprising conducting direct solid state polymerization (DSSP) of a diammonium dicarboxylate salt, wherein
the diammonium dicarboxylate salt is a granulate salt material prepared by fluidized bed spray granulation of an aqueous solution or slurry comprising diammonium dicarboxylate salt dissolved or dispersed in an aqueous medium, and wherein
the diammonium dicarboxylate salt has the following physical properties:
(a) a particle size distribution with a median particle size (d50) in the range of 200-1000 μm, measured by laser granulometry with the method according to ISO 13320-1 at 20° C., and
(b) a tapped bulk density in the range of 350-750 kg/m 3 , measured by the method according to ASTM D6393.
2. The process according to claim 1 , wherein the granulate salt material is a nylon salt.
3. The process according to claim 2 , wherein the direct solid state polymerization (DSSP) is carried out in a reactor comprising an agitator, or in a rotatable reactor, or a combination thereof, and wherein during the polymerization the granulate salt material and the resulting nylon polymer are mechanically agitated.
4. The process according to claim 1 , which further comprising dosing additional diamine at least during some part of the direct solid state polymerization or after the direct solid state polymerization.
5. The process according to claim 1 , wherein the polyamide is:
(i) an aromatic polyamide selected from PA-MXDT and PA-PXDT;
(ii) a semi-aromatic polyamide selected from the group consisting of PA-XT, PA-XI, PA-XT/XI, PA-XT/X6, XT/Y6 and PA-XT/YT, and any copolymer thereof, wherein T represents terephthalic acid, I represents isophthalic acid, 6 represents adipic acid, and X and Y represent diamines, independently from each other chosen from aliphatic diamines from the group consisting of ethylene diamine, 1,3-propanediamine, 1,4-diaminobutane, 1,5-pentanediamine, 2-methyl-1,5-pentanediamine, 1,6-hexanediamine, 2,2,4-trimethyl-1,6-hexanediamine, 2,4,4-trimethyl-1,6-hexanediamine, cis-1,4-cyclohexanediamine, trans-1,4-cyclohexanediamine, 1,8-octanediamine, 1,9-nonanediamine, and 1,10-decanediamine;
(iii) an aliphatic polyamide selected from the group consisting of PA-46, PA-66, PA-46/66, PA-66/68, and PA-410, and any copolymer thereof; or
(iv) a copolyamide of one or more of the semi-aromatic polyamides and/or one or more of the aliphatic polyamides, and/or one or more of the aromatic polyamides.
6. A polyamide granulate material which is obtained by direct solid state polymerization (DSSP) of a diammonium dicarboxylate salt, wherein
the diammonium dicarboxylate salt is a fluidized bed spray granulation product of an aqueous solution or an aqueous slurry comprising a diammonium dicarboxylate salt dissolved or dispersed in an aqueous medium, and wherein
the diammonium dicarboxylate salt has the following physical properties:
(a) a particle size distribution with a median particle size (d50) in the range of 200-1000 μm, measured by laser granulometry with the method according to ISO 13320-1 at 20° C., and
(b) a tapped bulk density in the range of 350-750 kg/m 3 , measured by the method according to ASTM D6393.
7. The polyamide granulate material according to claim 6 , wherein the polyamide granulate material comprises a polyamide polymer consisting of:
(i) an aromatic polyamide selected from PA-MXDT and PA-PXDT;
(ii) a semi-aromatic polyamide selected from the group consisting of PA-XT, PA-XI, PA-XT/XI, PA-XT/X6, XT/Y6 and PA-XT/YT, and any copolymer thereof, wherein T represents terephthalic acid, I represents isophthalic acid, 6 represents adipic acid, and X and Y represent diamines, independently from each other chosen from aliphatic diamines from the group consisting of ethylene, 1,3-propanediamine, diamine, 1,4-diaminobutane, 1,5-pentanediamine, 2-methyl-1,5-pentanediamine, 1,6-hexanediamine, 2,2,4-trimethyl-1,6-hexanediamine, 2,4,4-trimethyl-1,6-hexanediamine, cis-1,4-cyclohexanediamine, trans-1,4-cyclohexanediamine, 1,8-octanediamine, 1,9-nonanediamine, and 1,10-decanediamine;
(iii) an aliphatic polyamide selected from the group consisting of PA-46, PA-66, PA-46/66, PA-66/68, and PA-410, and any copolymer thereof; or
(iv) a copolyamide of one or more of the semi-aromatic polyamides and/or one or more of the aliphatic polyamides, and/or one or more of the aromatic polyamides.
8. A process for preparing a polyamide comprising polymerizing a diammonium dicarboxylate salt in a liquid state, wherein
the diammonium dicarboxylate salt comprises a granulate salt material prepared by fluidized bed spray granulation that is either molten or dissolved, and wherein
the granulate salt material is the spray granulation product of an aqueous solution or slurry comprising diammonium dicarboxylate salt dissolved or dispersed in an aqueous medium, and wherein
the granulate salt has the following physical properties:
(a) a particle size distribution with a median particle size (d50) in the range of 200-1000 μm, measured by laser granulometry with the method according to ISO 13320-1 at 20° C., and
(b) a tapped bulk density in the range of 350-750 kg/m 3 , measured by the method according to ASTM D6393.