Age-hardenable and highly formable aluminum alloys and methods of making the same
Provided herein are new aluminum alloy products and methods of making these alloys. The aluminum alloy products are age-hardenable, display high strength and formability, and allow for the use of recycled scrap. The aluminum alloys can serve as the core in a clad aluminum alloy product. The alloy products can be used in a variety of applications, including automotive, transportation, and electronics applications.
1. An aluminum alloy, comprising:
from 1.1 wt. % to 1.6 wt. % Mg;
from 0.2 wt. % to 0.5 wt. % Si;
from 0.01 to 1.0 wt. % Fe;
from 0.01 to 0.5 wt. % Cu;
from 0.01 to 0.5 wt. % Mn;
from 0.005 to 0.3 wt. % Cr;
from 0.01 to 0.3 wt. % Ti;
up to 0.5 wt. % Zn;
wherein the Mg and Si are present in a ratio of from 8:1 to 2:1 of Mg to Si by weight;
up to 0.25 wt. % impurities; and
balance Al.
2. The aluminum alloy of claim 1 , wherein:
the amount of Mg is from 1.1 wt. % to 1.5 wt. %;
the amount of Si is from 0.3 wt. % to 0.45 wt. %;
the amount of Fe is from 0.01 to 0.5 wt. %;
the amount of Cu is from 0.01 to 0.4 wt. %;
the amount of Mn is from 0.01 to 0.4 wt. %;
the amount of Cr is from 0.005 to 0.25 wt. %;
the amount of Ti is from 0.01 to 0.15 wt. %;
the amount of Zn is up to 0.4 wt. %;
V; and
the amount of impurities is up to 0.20 wt. %.
3. The aluminum alloy of claim 1 , wherein the Mg and Si are present in a ratio of from 5:1 to 2:1 of Mg to Si by weight.
4. The aluminum alloy of claim 1 , wherein the Mg and Si are present in a ratio of from 4:1 to 2:1 of Mg to Si by weight.
5. The aluminum alloy of claim 1 , wherein:
the amount of Mg is from 1.1 wt. % to 1.5 wt. %;
the amount of Si is from 0.25 wt. % to 0.45 wt. %;
the amount of Fe is from 0.01 wt. % to 1.0 wt. %;
the amount of Cu is from 0.01 wt. % to 0.5 wt. %;
the amount of Mn is from 0.01 wt. % to 0.5 wt. %;
the amount of Cr is from 0.005 wt. % to 0.3 wt. %;
the amount of Ti is from 0.01 wt. % to 0.25 wt. %;
the amount of Zn is up to 0.4 wt. %;
V; and
the amount of impurities is up to 0.20 wt. %.
6. The aluminum alloy of claim 1 , wherein the aluminum alloy, when in a T8x temper, has a yield strength (Rp0.2) of from 160 MPa to 230 MPa when tested according to ISO 6892-1 (2016).
7. The aluminum alloy of claim 1 , wherein the aluminum alloy has a bake hardening value from 70 MPa to 140 MPa.
8. The aluminum alloy of claim 1 , comprising at least 40 wt. % recycled content.
9. The aluminum alloy of claim 1 , comprising at least 40 wt. % UBC.
10. The aluminum alloy of claim 1 , wherein the combined concentration of Fe, Mn and Cu in the aluminum alloy is at least 0.7 wt. %.
11. The aluminum alloy of claim 1 , wherein the combined concentration of Fe, Mn, and Cu in the aluminum alloy is between 0.7 wt. % and 3.0 wt. %.
12. The aluminum alloy of claim 1 , wherein the aluminum alloy is a core layer in a clad product.
13. A monolithic sheet, comprising the aluminum alloy of claim 1 .
14. A clad aluminum alloy product, comprising:
a core layer having a first side and a second side; and
a first clad layer in contact with the first side of the core layer;
wherein the core layer comprises the aluminum alloy of claim 1 .
15. The clad aluminum alloy product of claim 14 , wherein the first clad layer has a thickness of from 0.05 mm to 0.80 mm.
16. The clad aluminum alloy product of claim 14 , wherein the core layer has a thickness of from 0.7 to 2.3 mm.
17. The clad aluminum alloy product of claim 14 , further comprising a second clad layer in contact with the second side of the core layer.
18. The clad aluminum alloy product of claim 14 , wherein the first clad layer comprises an 1xxx series aluminum alloy, 2xxx series aluminum alloy, a 3xxx series aluminum alloy, a 4xxx series alloy, a 5xxx series aluminum alloy, a 6xxx series aluminum alloy, a 7xxx series aluminum alloy, or an 8xxx series aluminum alloy.
19. The clad aluminum alloy product of claim 14 , wherein the clad aluminum alloy product when in a T8x temper has a yield strength of at least 150 MPa and when in a T4 temper has a total elongation above 20% in all directions.
20. The clad aluminum alloy product of claim 14 , wherein the clad aluminum alloy product is a sheet, a plate, an electronic device housing, an automotive structural part, an aerospace structural part, an aerospace non-structural part, a marine structural part, or a marine non-structural part.