Fluororesin coating composition for forming a topcoat and coating film therefrom
View Patent ↗Provided is a fluororesin coating composition for forming a topcoat having improved non-tackiness and water and oil repellency. The fluororesin is crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer having a perfluoro(ethyl vinyl ether) content of 8 to 20 mass % based on the total mass of the copolymer.
1. A topcoat coating film on a substrate formed from a fluororesin coating composition for forming a topcoat, comprising a crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer having a perfluoro(ethyl vinyl ether) content of 8 to 20 mass % based on the total mass of said copolymer, wherein said substrate is primer coated or the surface of said substrate is chemically treated prior to being coated with said coating film, and wherein said coating film is heat treated at the melting point or higher of said crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer, wherein the crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer consists of tetrafluoroethylene, perfluoro(ethyl vinyl ether), and optionally a monomer selected from the group consisting of a perfluoroalkene including 3 to 6 carbon atoms, a perfluoro(alkyl vinyl ether) including 1 to 6 carbon atoms other than perfluoro(ethyl vinyl ether), chlorotrifluoroethylene, vinylidene fluoride, vinyl fluoride, ethylene, propylene, butylene, pentene, hexene, styrene, acetylene, propyne, and combinations thereof.
2. The coating film of claim 1 , wherein the contact angle of n-hexane on said topcoat coating film is 28 degrees or more.
3. An article, comprising the coating film according to claim 1 coated on a substrate.
4. A method of forming the coating film on the substrate according to claim 1 , comprising the steps of: coating a fluororesin coating composition for forming a topcoat, comprising a crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer having a perfluoro(ethyl vinyl ether) content of 8 to 20 mass % based on the total mass of said copolymer on a substrate; and then performing heat treatment on the coated substrate, wherein said heat treatment is carried out at the melting point or higher of said crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer, and wherein said substrate is primer coated or the surface of said substrate is chemically treated prior to being coated with said coating film, wherein the crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer consists of tetrafluoroethylene, perfluoro(ethyl vinyl ether), and optionally a monomer selected from the group consisting of a perfluoroalkene including 3 to 6 carbon atoms, a perfluoro(alkyl vinyl ether) including 1 to 6 carbon atoms other than perfluoro(ethyl vinyl ether), chlorotrifluoroethylene, vinylidene fluoride, vinyl fluoride, ethylene, propylene, butylene, pentene, hexene, styrene, acetylene, propyne, and combinations thereof.
5. The method of claim 4 , wherein the contact angle of n-hexane on said coating film is 28 degrees or more.
6. The method of claim 4 , wherein the crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer has a perfluoro(ethyl vinyl ether) content of 8 to 15 mass % based on the total mass of said copolymer.
7. The method of claim 6 , wherein the crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer has a perfluoro(ethyl vinyl ether) content of 9 to 12 mass % based on the total mass of said copolymer.
8. The coating film of claim 1 , wherein the crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer has a perfluoro(ethyl vinyl ether) content of 8 to 15 mass % based on the total mass of said copolymer.
9. The coating film of claim 8 , wherein the crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer has a perfluoro(ethyl vinyl ether) content of 9 to 12 mass % based on the total mass of said copolymer.
10. The coating film of claim 1 , wherein the crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer comprises at least 99 mass %, in combination, tetrafluoroethylene and perfluoro(ethyl vinyl ether).
11. The coating film of claim 1 , wherein the sliding angle of pure water on said topcoat coating film is 50 degrees or less.
12. The method of claim 4 , wherein the crystalline tetrafluoroethylene and perfluoro(ethyl vinyl ether) copolymer comprises at least 99 mass %, in combination, tetrafluoroethylene and perfluoro(ethyl vinyl ether).
13. The method of claim 4 , wherein the sliding angle of pure water on said coating film is 50 degrees or less.