Process and plant for thermal decomposition of aluminium chloride hydrate into aluminium oxide
The invention relates to a process and its relating plant for thermal conversion of aluminum chloride hydrate into aluminum oxide and gaseous hydrogen chloride. In a first step, aluminum chloride hydrate is fed into a decomposition reactor where it is heated to a temperature between 120 and 400° C. Afterwards, the partially decomposed aluminum chloride hydrate is finally calcined to aluminum oxide at a temperature between 850 and 1200° C. in a second reactor. The aluminum chloride hydrate is admixed with aluminum oxide in an intensive mixer with a mass ratio between 1:1 and 10:1 aluminum chloride hydrate to aluminum oxide for using a fluidized bed reactor as a decomposition reactor.
1. A process for thermal conversion of aluminum chloride hydrate into aluminum oxide and gaseous hydrogen chloride by partially decomposing the aluminum chloride hydrate in a decomposition reactor by heating to a temperature between 120 and 400° C. and then calcining the partially decomposed aluminum chloride hydrate in a calcining reactor to aluminum oxide at a temperature between 850 and 1200° C., wherein the aluminum chloride hydrate is admixed with aluminum oxide in a mixer with a mass ratio between 1:1 and 10:1 aluminum chloride hydrate to aluminum oxide and that the resulting mixture is fed into the decomposition reactor which is a fluidized bed reactor.
2. The process according to claim 1 , wherein at least parts of the aluminum oxide from the calcination is recirculated in the decomposition reactor.
3. The process according to claim 2 , wherein the recirculated aluminum oxide features a temperature between 600 and 1100° C. in the decomposition reactor.
4. The process according to claim 1 , wherein at least parts of the aluminum oxide from the decomposition is recirculated in the decomposition reactor.
5. The process according to claim 4 , wherein the recirculated aluminum oxide for the admixing in the mixer has a temperature below 100° C.
6. The process according to claim 1 , wherein the aluminum chloride hydrate is passed through a lump breaker and/or a dryer before being fed into the mixer.
7. The process according to claim 1 , wherein the calcination takes part in a fluidized bed/or a rotary kiln.
8. The process according to claim 1 , wherein the decomposition and/or the calcination occur in a circulating fluidized bed.
9. The process according to claim 1 , wherein steam and/or air is added to the decomposition and/or air and/or a fuel is added to the calcination.
10. The process according to claim 1 , wherein off-gases are passed separately from the decomposition and the calcination to an off-gas treatment.
11. The process according to claim 10 , wherein the off-gas treatment contains a quenching step and/or a scrubbing step and/or an absorption step.
12. The process according to claim 1 , wherein the mixing is performed in the mixer with knifes and/or ploughshares and/or paddles.
13. The process according to claim 12 , wherein the knifes rotate at least twice as fast as the ploughshares.
14. The process according to claim 1 , wherein the residence time in the mixer is more than one minute.