Additive formulation for reduction or prevention of microbially induced corrosion in concrete or cementitious material
An additive formulation for reduction or prevention of microbially induced corrosion in concrete, cementitious material (such as mortar or grout), or a combination thereof. The additive formulation comprises a Quat Silane and a fungicide, wherein the ratio of the Quat Silane to the fungicide in the formulation is in a range of about 10:1 to about 1:10, preferably in a range of about 5:1 to about 1:5.
1. A method of using comprising:
adding an additive formulation comprising a Quat Silane configured to cure on and within a material, and a fungicide to the material; wherein the material is in a wet-state selected from the group consisting of an uncured concrete, an uncured cementitious material, and a combination thereof; and wherein the addition results in a reduction or an elimination of microbially induced corrosion.
2. The method of using according to claim 1 , wherein the Quat Silane is in a ratio of the Quat Silane to the fungicide in a range of about 10:1 to about 1:10.
3. The method of using according to claim 2 , wherein the Quat Silane is in a ratio of the Quat Silane to the fungicide in a range of about 5:1 to about 1:5.
4. The method of using according to claim 1 , wherein the additive formulation further comprises a defoamer.
5. The method of using according to claim 4 , wherein the defoamer is selected from the group consisting of polyether amine, ethoxylated alcohol, silicone-based defoamer, tributyl phosphate, and a combination thereof.
6. The method of using according to claim 4 , wherein the defoamer is from about 2 weight % to about 25 weight % of the amount of the Quat Silane in the formulation.
7. The method of using according to claim 1 , wherein the fungicide is selected from the group consisting of Sodium OrthophenylPhenol, Imazalil Sulphate, diiodomethyl-p-tolylsulfone, carbamate, isothiazolinone, azole, chlorothalonil, zinc pyrithione, copper pyrithione, sodium pyrithione, tebuconazole and propiconazole; chlorothalonil, diiodomethyl-p-tolylsulfone, zinc pyrithione, copper pyrithione, sodium pyrithione, and a combination thereof.
8. The method of using according to claim 7 , wherein the carbamate is selected from the group consisting of lodopropynyl butylcarbamate (IPBC), carbendazim, and a combination thereof.
9. The method of using according to claim 7 , wherein the isothiazolinone is selected from the group consisting of OIT (2-Octyl-2H-isothiazol-3-one), DCOIT (4,5-Dichloro-2-octyl-4-isothiazolin-3-one), BBIT (N-butyl-1, 2-benzisothiazolin-3-one), and a combination thereof.
10. The method according to claim 1 , wherein the Quat Silane is added at an effective amount to reduce bacteria and fungus in the material prior to curing.
11. An article comprising:
a material, in a wet-state, selected from the group consisting of an uncured concrete, an uncured cementitious material, and a combination thereof having an additive formulation cured therein, wherein the additive formulation comprises a Quat Silane, a fungicide, and a defoamer.