Resin material for hose and hose
A resin material, in which the elongation at break in an environmental condition at a predetermined temperature of 100° C. or higher and 150° C. or lower is 50% or more, a content of a plasticizer is 3 mass % or less with respect to the total mass of the resin material, a strength at break in the environmental condition at this predetermined temperature is 5 MPa or more, the elongation at break is 500% or less, and a 10% modulus is 3 MPa or less, is formed into a tubular form and used as an inner surface layer, an intermediate layer, and an outer surface layer of a hose, and components of an air conditioner are connected through the hose. Such resin material, and also a hose including the resin material, which are mainly used for an air conditioner installed in a vehicle, have improved durability in a high temperature environment.
1. A resin material for a hose in which a thermoplastic resin and an elastomer or rubber are blended, having an islands-in-the-sea structure, and in which the thermoplastic resin is the sea and the elastomer or rubber is the islands, and having an elongation at break in an environmental condition at a predetermined temperature of 100° C. or higher and 150° C. or lower of 50% or more, a content of a plasticizer being 3 mass % or less with respect to a total mass.
2. The resin material for a hose according to claim 1 , wherein a strength at break in the environmental condition at the predetermined temperature is 5 MPa or more.
3. The resin material for a hose according to claim 1 , wherein the elongation at break in the environmental condition at the predetermined temperature is 500% or less.
4. The resin material for a hose according to claim 1 , wherein a 10% modulus in the environmental condition at the predetermined temperature is 3 MPa or less.
5. The resin material for a hose according to claim 1 , further comprising a resin having a melting point of 170° C. or higher and 230° C. or lower.
6. The resin material for a hose according to claim 1 , further comprising a polyamide.
7. The resin material fora hose according to claim 1 , wherein a content of the plasticizer is less than 3 mass % with respect to a total mass.
8. The resin material for a hose according to claim 1 , wherein a content of the plasticizer is less than 0.1 mass % with respect to a total mass.
9. A hose comprising the resin material for a hose according to claim 1 being formed into a tubular form and used as a constituent member.
10. The hose according to claim 9 comprising the resin material for a hose as an inner surface layer or an outer surface layer, the resin material being formed into a tubular form.
11. The hose according to claim 10 , wherein the hose connects components of an air conditioner installed in a vehicle and circulates a refrigerant.