Wet laid disposable absorbent structures with high wet strength and method of making the same
A method of making an absorbent structure including mixing ultra-high molecular weight (“UHMW”) glyoxalated polyvinylamide adducts (“GPVM”) and/or high molecular weight (“HMW”), glyoxalated polyacrylamide and/or high cationic charge glyoxalated polyacrylamide (“GPAM”) copolymers and high molecular weight (“HMW”) anionic polyacrylamide (“APAM”) with the furnish during stock preparation of a wet laid papermaking process.
1. An absorbent product comprising cellulose fibers, comprising a 1,3-dichloro-2-propanol concentration of less than 50 ppb and a 3-monochloro-1,2 propanediol concentration of less than 300 ppb, and a cross direction wet strength of 80 to 200 N/m, wherein the product is free from polyaminoamide-epihalohydrin as measured using an “Adipate test”, wherein all of the cellulose fibers contained in the absorbent product are non-synthetic, cellulose fibers.
2. The absorbent product of claim 1 , wherein the product is through air dried facial tissue, napkin, or towel.
3. The absorbent product of claim 1 , wherein the absorbent product is a retail roll towel product.
4. The absorbent product of claim 3 , wherein the retail roll towel product comprises:
a two-ply cellulose sheet or web having a cross direction wet strength of 80 to 200 N/m and a two-ply caliper of 600 to 1500 microns, wherein the retail roll towel product contains 0 to 550 ppb 3-monochloro-1,2 propanediol and 0 to 0.09% by weight polyaminoamide-epihalohydrin.
5. The absorbent product of claim 4 , wherein the cross direction wet strength is 80 to 150 N/m, the two-ply caliper is 700 to 1300 microns, and the retail roll towel product has a basis weight of 38 to 50 g/m 2 , wherein the retail roll towel product contains 50 to 550 ppb 3-monochloro-1,2 propanediol and 0.01 to 0.04% by weight polyaminoamide-epihalohydrin.
6. The absorbent product of claim 1 , further comprising:
95 to 99 percent by weight cellulose fibers; and
0.25 to 1.5 percent by weight ultra-high molecular weight glyoxalated polyvinylamide adducts and high molecular weight anionic polyacrylamide.
7. The absorbent product of claim 1 , further comprising:
95 to 99 percent by weight cellulose fibers;
0.25 to 1.5 percent by weight ultra-high molecular weight glyoxalated polyvinylamide adducts and high molecular weight anionic polyacrylamide; and
0.03 to 0.5 percent by weight polyvinylamine.
8. A tissue product comprising:
a two-ply creped through air dried retail towel with a cross direction wet strength of 80 to 150 N/m, a dry caliper of 700 to 1200 microns, measured 3-monochloro-1,2 propanediol from 50 to 300 parts per billion in paper that makes up the product, and measured 1,3-dichloro-2-propanol from 5 to 50 parts per billion in the paper,
wherein no PAE resin is added to a wet-end of a papermaking machine used to make the tissue product.