Soft polypropylene composition with improved optical behavior

1. A polyolefin composition (C) comprising:

(a) a heterophasic propylene copolymer (TERHECO) comprising:

(a1) a matrix (M) being a crystalline propylene copolymer (P); and

(a2) an elastomeric propylene copolymer (EC) dispersed in said matrix (M), the heterophasic propylene copolymer (TERHECO) consisting of units derived from propylene, ethylene and 1-hexene;

and

(b) a styrenic thermoplastic elastomer (sTPE) having a Shore A hardness measured according to ASTM D 2240 from 25 to 70;

wherein

(i) a weight ratio between the heterophasic propylene copolymer (TERHECO) and the styrenic thermoplastic elastomer (sTPE) [(TERHECO)/(sTPE)] is in a range of 30/70 to 90/10;

(ii) an overall weight of the heterophasic propylene copolymer (TERHECO) and the styrenic thermoplastic elastomer (sTPE) based on a weight of the composition (C) [((TERHECO)+(sTPE))/(C)] is at least 80 wt. %;

(iii) the 1-hexene content, based on a weight of the heterophasic propylene copolymer (TERHECO), is in a range of 1.0 to 12.0 wt. %;

(iv) the ethylene content, based on the weight of the heterophasic propylene copolymer (TERHECO), is in a range of 0.1 to 12.0 wt. %;

(v) the xylene cold soluble fraction (XCS) of the heterophasic propylene copolymer (TERHECO) is in a range of 12 to 45 wt. %; and

(vi) the heterophasic propylene copolymer (TERHECO) is obtained in the presence of a metallocene catalyst and has a content of <2,1> erythro regiodefects as determined from 13 C-NMR of more than 0.0 mol-%.

2. The polyolefin composition (C) according to claim 1 having

(a) a melt flow rate MFR 2 (230° C.; 2.16 kg) measured according to ISO 1133 in a range of 0.5 to 20 g/10 min;

and/or

(b) a glass transition temperature Tg below −20° C.

3. The polyolefin composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (TERHECO) has

a melting temperature in the range of 125 to 140° C.

4. The polyolefin composition (C) according to claim 1 , wherein

(a) a weight ratio between the 1-hexene content and the ethylene content of the heterophasic propylene copolymer (TERHECO) [(C6) total/(C2) total] is in the range of 1.2 to 12.0;

and/or

(b) a weight ratio between the ethylene content and the 1-hexene content of the xylene cold soluble fraction (XCS) of the heterophasic propylene copolymer (TERHECO) [(C2) XCS/(C6) XCS] is in the range of 1.2 to 10.0.

5. The polyolefin composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (TERHECO) has

(a) a melt flow rate MFR 2 (230° C.; 2.16 kg) measured according to ISO 1133 in the range of 0.5 to 20 g/10 min;

and/or

(b) an ethylene content, based on the weight of the heterophasic propylene copolymer (TERHECO), is in the range of 0.1 to 6.0 wt. %.

6. The polyolefin composition (C) according to claim 1 , wherein the matrix (M) is

(a) a crystalline propylene copolymer (C3/C6-PP) consisting of units derived from propylene and 1-hexene, or

(b) a crystalline propylene terpolymer (C3/C2/C6) consisting of units derived from of propylene, ethylene and 1-hexene.

7. The polyolefin composition (C) according to e claim 1 , wherein the elastomeric propylene copolymer (EC) consists of units derived from propylene and ethylene.

8. The polyolefin composition (C) according to claim 1 , wherein the xylene cold soluble fraction (XCS) of the heterophasic propylene copolymer (TERHECO) has

(a) a 1-hexene content in the range of 1.0 to 8.0 wt. %; and/or

(b) an ethylene content in the range of 3.0 to 18.0 wt. %; and/or

(a) an intrinsic viscosity (IV) measured according to DIN ISO 1628/1 (in decaline at 135° C.) in the range of 1.2 to 2.5 dl/g.

9. The polyolefin composition (C) according to claim 1 , wherein the ethylene and 1-hexene content together of the heterophasic propylene copolymer (TERHECO), based on the weight of the heterophasic propylene copolymer (TERHECO), is in the range of 1.2 to 10.0 wt. %.

10. The polyolefin composition (C) according to e claim 1 , wherein the ethylene and 1-hexene content together of the xylene cold soluble fraction of the heterophasic propylene copolymer (TERHECO), based on the weight of xylene cold soluble fraction (XCS) of the heterophasic propylene copolymer (TERHECO), is in the range of 5.0 to 20.0 wt. %.

11. The polyolefin composition (C) according to e claim 1 , wherein,

(a) the weight ratio between the 1-hexene content of the heterophasic propylene copolymer (TERHECO) and the 1-hexene content of the xylene cold soluble fraction (XCS) of the heterophasic propylene copolymer (TERHECO) [(C6) total/(C6) XCS] is in the range of more than 1.0 to 5.0; and/or

(b) the weight ratio between the ethylene content of the xylene cold soluble fraction (XCS) of the heterophasic propylene copolymer (TERHECO) and the ethylene content of the heterophasic propylene copolymer (TERHECO) [(C2) XCS/(C2) total] is in the range of 2.0 to 20.0.

12. The polyolefin composition (C) according to claim 1 , wherein the styrenic thermoplastic elastomer (sTPE) has

(a) a melt flow rate MFR 2 (230° C.; 2.16 kg) measured according to ISO 1133 in the range of 0.5 to 10 g/10 min;

and/or

(b) a styrene content, based on the weight of the styrenic thermoplastic elastomer (sTPE), in the range of 5 to 40 wt. %.

13. The polyolefin composition (C) according to claim 1 , wherein the styrenic thermoplastic elastomer (sTPE) is a styrene-ethylene/butylene-styrene block copolymer (SEBS).

14. An article comprising at least 90 wt. %, based on the weight of the article, the polyolefin composition (C) according claim 1 .

15. A process comprising the steps of

(a) producing an article according to claim 14 , and

(b) sterilizing the article.

16. The polyolefin composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (TERHECO) has a content of <2,1> erythro regiodefects as determined from 13 C-NMR in the range of 0.1 to 2.0 mol-%.