Flame-resistant resin composition, method for manufacturing same, and hydrogenated petroleum resin
A flame retardant resin composition comprising: a hydrogenated petroleum resin, being a hydrogenated product of a polymer of an unsaturated hydrocarbon comprising at least one selected from the group consisting of an alicyclic compound having a five-membered ring and an aromatic hydrocarbon compound; a polyolefin; and an inorganic filler.
1. A flame retardant resin composition consisting of:
a hydrogenated petroleum resin, being a hydrogenated product of a polymer of an alicyclic compound having a five-membered ring and an aromatic hydrocarbon compound;
a polyolefin;
an inorganic filler; and
at least one additive selected from the group consisting of an antioxidant, a lubricant, a processing stabilizer, a coloring agent, a foaming agent, and a reinforcing agent; wherein
a content of the hydrogenated petroleum resin is 1% by mass or more and 25% by mass or less, based on the total amount of flame retardant resin composition,
a content of the polyolefin is 5% by mass or more and 35% by mass or less, based on the total amount of the flame retardant resin composition,
a content of the additive is 0% by mass or more and 5% by mass or less, based on the total amount of the flame retardant resin composition,
a ratio of a content C1 of the aromatic hydrocarbon compound to a content C2 of the alicyclic compound, C1/C2 (mass ratio), is 0.25 or more and 1.38 or less, and
the polyolefin is at least one selected from the group consisting of an ethylene/vinyl acetate copolymer and an ethylene/ethyl acrylate copolymer.
2. The flame retardant resin composition according to claim 1 , wherein the alicyclic compound is a DCPD compound having a dicyclopentadiene skeleton.
3. The flame retardant resin composition according to claim 1 , wherein the aromatic hydrocarbon compound is at least one selected from the group consisting of an indene-based compound having an indene skeleton and a styrene-based compound having a styrene skeleton.
4. A method for manufacturing a flame retardant resin composition according to claim 1 , comprising:
bringing a hydrogenated petroleum resin, being a hydrogenated product of a polymer of an alicyclic compound having a five-membered ring and an aromatic hydrocarbon compound, into contact with a polyolefin and an inorganic filler.