Method for manufacturing glass panel unit, and glass panel unit assembly
A method for manufacturing a glass panel unit includes an assembling step, a gas exhausting step, and a sealing step. At least one of a first glass pane or a second glass pane includes a low-emissivity film. In a situation where the low-emissivity film is heated at a temperature increase rate of 4° C./min before a peripheral wall is melted, a ratio of an emission quantity of a rare gas emitted from the low-emissivity film at a deformation temperature of the partition to an emission quantity of the rare gas emitted from the low-emissivity film at 100° C. is equal to or less than 2.0.
1. A method for manufacturing a glass panel unit, the method comprising an assembling step, a bonding step, a gas exhausting step, and a sealing step,
the assembling step including providing an assembly,
the assembly including:
a first glass pane;
a second glass pane arranged to face the first glass pane;
a peripheral wall having a frame shape and provided between the first glass pane and the second glass pane;
an internal space surrounded with the first glass pane, the second glass pane, and the peripheral wall;
a partition to partition the internal space into a first space and a second space;
an exhaust port allowing the second space to communicate with an external environment; and
an air passage allowing the first space to communicate with the second space,
at least one of the first glass pane or the second glass pane including a low-emissivity film,
the low-emissivity film being provided in the first space,
the bonding step including melting the peripheral wall to hermetically bond the first glass pane and the second glass pane together with the peripheral wall,
the gas exhausting step including exhausting a gas from the first space through the air passage, the second space, and the exhaust port,
the sealing step including deforming the partition at a temperature equal to or higher than a softening point of the partition to close the air passage,
a ratio of an emission quantity of a rare gas emitted, in a situation where the low-emissivity film is heated at a temperature increase rate of 4° C./min before the peripheral wall is melted, from the low-emissivity film at a deformation temperature of the partition to an emission quantity of the rare gas emitted from the low-emissivity film at 100° C. being equal to or less than 2.0.
2. The method of claim 1 , wherein
the ratio of the emission quantity of the rare gas emitted from the low-emissivity film at the deformation temperature of the partition to the emission quantity of the rare gas emitted from the low-emissivity film at 100° C. is equal to or less than 1.5.
3. The method of claim 2 , wherein
the ratio of the emission quantity of the rare gas emitted from the low-emissivity film at the deformation temperature of the partition to the emission quantity of the rare gas emitted from the low-emissivity film at 100° C. is equal to or less than 1.0.
4. The method of claim 3 , wherein
the emission quantity of the rare gas emitted from the low-emissivity film at the deformation temperature of the partition is smaller than the emission quantity of the rare gas emitted from the low-emissivity film at 100° C.
5. The method of claim 1 , wherein
the rare gas includes argon.
6. The method of claim 1 , wherein
the softening point of the partition is equal to a softening point of the peripheral wall.
7. The method of claim 1 , further comprising a removing step,
the removing step including removing a portion including the second space to obtain a glass panel unit as a part including the first space.
8. An assembly for use to make a glass panel unit, the assembly comprising:
a first glass pane;
a second glass pane arranged to face the first glass pane;
a peripheral wall having a frame shape and provided between the first glass pane and the second glass pane;
an internal space surrounded with the first glass pane, the second glass pane, and the peripheral wall;
a partition to partition the internal space into a first space and a second space;
an exhaust port allowing the second space to communicate with an external environment; and
an air passage allowing the first space to communicate with the second space,
at least one of the first glass pane or the second glass pane including a low-emissivity film,
the low-emissivity film being provided in the first space,
a ratio of an emission quantity of a rare gas emitted, in a situation where the low-emissivity film is heated at a temperature increase rate of 4° C./min before the peripheral wall is melted, from the low-emissivity film at a deformation temperature of the partition to an emission quantity of the rare gas emitted from the low-emissivity film at 100° C. being equal to or less than 2.0.