Non-aqueous electrolyte secondary battery
In a non-aqueous electrolyte secondary battery that is one example of the embodiment, a positive electrode mix layer comprises a positive electrode active material comprising a lithium transition metal composite oxide represented by general formula: Li a Ni b Co (1-b-c) Al c O d (0.9<a≤1.2, 0.88≤b≤0.96, 0.04≤c≤0.12, 1.9≤d≤2.1) and lithium carbonate in an amount of 0.1 to 1.0% by mass relative to the mass of the positive electrode active material. The lithium transition metal composite oxide has the form of secondary particles formed by the aggregation of primary particles, wherein tungsten is present, on the surface of each of the primary particles, in an amount of 0.05 to 0.20 mol % relative to the total molar amount of non-Li-metal elements contained in the positive electrode active material.
1. A non-aqueous electrolyte secondary battery, comprising a positive electrode having a positive electrode core and a positive electrode mixture layer provided on a surface of the positive electrode core, wherein
the positive electrode mixture layer includes:
a positive electrode active material including a lithium-transition metal composite oxide represented by a general formula of Li a Ni b Co (1-b-c) Al c O d , where 0.9<a≤1.2, 0.88≤b≤0.96, 0.04≤c<0.12, and 1.9≤d≤2.1; and
0.1 to 1.0 mass % of lithium carbonate based on a mass of the positive electrode active material, and wherein
the lithium-transition metal composite oxide is secondary particles formed by aggregation of primary particles;
0.05 to 0.20 mol % of tungsten is present on a surface of the primary particles based on a total molar amount of metal elements excluding Li, in the positive electrode active material; and
a median diameter of a volume-based particle size distribution of the lithium carbonate is 2 μm or more and is smaller than a median diameter of a volume-based particle size distribution of the positive electrode active material.
2. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the lithium-transition metal composite oxide is a composite oxide represented by a general formula of Li a Ni b CO (1-b-c) Al c O d , where 0.9<a≤1.2, 0.88≤b≤0.92, 0.04≤c≤0.06, and 1.9≤d≤2.1.
3. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the lithium-transition metal composite oxide is a composite oxide represented by a general formula of Li a Ni b CO (1-b-c) Al c O d , where 0.9<a≤1.2, 0.91≤b≤0.92, 0.04≤c≤0.06, and 1.9≤d≤2.1.
4. The non-aqueous electrolyte secondary battery according to claim 1 , wherein in the positive electrode mixture layer, the lithium carbonate is present on a particle surface of the positive electrode active material and in a space among the positive electrode active materials.
5. The non-aqueous electrolyte secondary battery according to claim 1 ,
wherein a content of a binder included in the positive electrode mixture layer is 0.3 to 0.9 mass % based on a total mass of the positive electrode mixture layer.
6. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the median diameter of the volume-based particle size distribution of the lithium carbonate is 2 μm or more and 12 μm or less.