Colored glass frits and related methods for laser marking applications
A marking composition for forming marks or indicia on a substrate is provided for laser marking applications. The composition includes a glass frit, a carrier, and absorber particles. The glass frit includes alkali metal oxides, glass forming oxides, and one or more transition metal oxides. The glass frit is devoid of at least one of bismuth and zinc.
1. A glass frit for a composition for forming marks or indicia on a substrate, the glass comprising:
from 4 to 13.5 mol % Li 2 O,
from 4 to 13 mol % Na 2 O,
from 0 to 12 mol % K 2 O+Rb 2 O+Cs 2 O,
from 35 to 60 mol % SiO 2 ,
from 0.1 to 27 mol % of one or more transition metal oxides selected from the group consisting of Fe 2 O 3 , MnO 2 , Cr 2 O 3 , and Co 3 O 4 ,
from 1 to 27 mol % B 2 O 3 ,
from 0.1 to 12 mol % Al 2 O 3 ,
from 0.1 to 11 mol % TiO 2 , and
from 0 to 40 mol % F,
wherein the composition is Bi-free and Zn-free.
2. The glass frit of claim 1 comprising:
from 4 to 13 mol % Li 2 O,
from 5 to 13 mol % Na 2 O,
from 0 to 12 mol % K 2 O+Rb 2 O+Cs 2 O,
from 35 to 60 mol % SiO 2 ,
from 0.1 to 26 mol % of one or more transition metal oxides selected from the group consisting of Fe 2 O 3 , MnO 2 , Cr 2 O 3 , and Co 3 O 4 ,
from 1 to 25 mol % B 2 O 3 ,
from 0.1 to 12 mol % Al 2 O 3 ,
from 0.1 to 11 mol % TiO 2 , and
from 0 to 35 mol % F.
3. The glass frit of claim 1 comprising:
from 6 to 13 mol % Li 2 O,
from 6 to 12 mol % Na 2 O,
from 0 to 9 mol % K 2 O+Rb 2 O+Cs 2 O,
from 35 to 55 mol % SiO 2 ,
from 2 to 24.5 mol % of one or more transition metal oxides selected from the group consisting of Fe 2 O 3 , MnO 2 , Cr 2 O 3 , and Co 3 O 4 ,
from 3 to 25 mol % B 2 O 3 ,
from 0.1 to 8 mol % Al 2 O 3 ,
from 0.1 to 8 mol % TiO 2 , and
from 0 to 30 mol % F.
4. The glass frit of claim 1 comprising:
from 6 to 12 mol % Li 2 O,
from 7 to 12 mol % Na 2 O,
from 0 to 9 mol % K 2 O+Rb 2 O+Cs 2 O,
from 41 to 53 mol % SiO 2 ,
from 11 to 24.5 mol % of one or more transition metal oxides selected from the group consisting of Fe 2 O 3 , MnO 2 , Cr 2 O 3 , and Co 3 O 4 ,
from 9 to 23 mol % B 2 O 3 ,
from 0.1 to 5 mol % Al 2 O 3 ,
from 0.1 to 5 mol % TiO 2 , and
from 0 to 30 mol % F.
5. The glass frit of claim 1 comprising:
from 8.3 to 12 mol % Li 2 O,
from 6 to 9 mol % Na 2 O,
from 0 to 7 mol % K 2 O+Rb 2 O+Cs 2 O,
from 44 to 55 mol % SiO 2 ,
from 2 to 7 mol % of one or more transition metal oxides selected from the group consisting of Fe 2 O 3 , MnO 2 , Cr 2 O 3 , and Co 3 O 4 ,
from 3 to 10 mol % B 2 O 3 ,
from 0.1 to 5 mol % Al 2 O 3 ,
from 2 to 7.5 mol % TiO 2 , and
from 0 to 30 mol % F.
6. The glass frit of claim 1 comprising:
from 5 to 10 mol % Li 2 O,
from 6 to 11 mol % Na 2 O,
from 0 to 10 mol % K 2 O+Rb 2 O+Cs 2 O,
from 47 to 60 mol % SiO 2 ,
from 0.1 to 9 mol % of one or more transition metal oxides selected from the group consisting of Fe 2 O 3 , MnO 2 , Cr 2 O 3 , and Co 3 O 4 ,
from 5 to 17 mol % B 2 O 3 ,
from 0.1 to 5 mol % Al 2 O 3 ,
from 0.1 to 7 mol % TiO 2 , and
from 0 to 35 mol % F.
7. The glass frit of claim 1 comprising:
from 6 to 10 mol % Li 2 O,
from 6.5 to 11.5 mol % Na 2 O,
from 0 to 7.5 mol % K 2 O+Rb 2 O+Cs 2 O,
from 49 to 58 mol % SiO 2 ,
from 0.1 to 4 mol % of one or more transition metal oxides selected from the group consisting of Fe 2 O 3 , MnO 2 , Cr 2 O 3 , and Co 3 O 4 ,
from 8 to 15 mol % B 2 O 3 ,
from 0.1 to 3.5 mol % Al 2 O 3 ,
from 1 to 6 mol % TiO 2 , and
from 0 to 30 mol % F.