Protection film having variable adhesion for foldable display and foldable display device comprising same

1. A foldable display protective film comprising:

an adhesive layer comprising an adhesive composition comprising a (meth)acrylate resin comprising a copolymerized product of a mixture containing an alkyl (meth)acrylate monomer, a crosslinkable functional group-containing monomer, and a photoinitiator monomer; and

a protective substrate provided on one surface of the adhesive layer,

wherein,

the photoinitiator monomer is contained in an amount of 0.2 to 4.5 wt % based on the total weight of the mixture,

the crosslinkable functional group-containing monomer is contained in an amount of more than 0 to not more than 20 wt % based on the total weight of the mixture,

the protective substrate is maintained without being damaged or detached when subjected to a 4-mm radius folding test, and

the protective film satisfies the following equation 1:

1≤100* B/A≤ 30  [Equation 1]

wherein

A is an adhesive strength measured at 23° C. and 50 RH % before light irradiation after a surface of the adhesive layer, which is opposite to a surface thereof being in contact with the protective substrate, is attached to a PI substrate, and

B is an adhesive strength measured at 23° C. and 50 RH % after the irradiation with light having a wavelength of 380 nm or less after the surface of the adhesive layer, which is opposite to the surface thereof being in contact with the protective substrate, is attached to the PI substrate.

2. The foldable display protective film of claim 1 , wherein A is at least 800 gf/in, and B is 10 gf/in to 300 gf/in.

3. The foldable display protective film of claim 1 , wherein the photoinitiator monomer is a benzophenone-based compound having a (meth)acrylate group.

4. The foldable display protective film of claim 1 , wherein the alkyl (meth)acrylate monomer comprises at least one of pentyl (meth)acrylate, n-butyl (meth)acrylate, ethyl (meth)acrylate, methyl (meth)acrylate, hexyl (meth)acrylate, n-octyl (meth)acrylate, isooctyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, dodecyl (meth)acrylate, or decyl (meth)acrylate.

5. The foldable display protective film of claim 1 , wherein the crosslinkable functional group-containing monomer comprises at least one of a carboxyl group-containing monomer or a hydroxyl group-containing monomer.

6. The foldable display protective film of claim 5 , wherein the carboxyl group-containing monomer comprises at least one of (meth)acrylic acid, 2-(meth)acryloyloxy acetic acid, 3-(meth)acryloyloxy propylic acid, 4-(meth)acryloyloxy butyric acid, an acrylic acid dimer, itaconic acid, maleic acid, or a maleic anhydride.

7. The foldable display protective film of claim 5 , wherein the hydroxyl group-containing monomer comprises at least one of 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, or 4-hydroxybutyl (meth)acrylate.

8. The foldable display protective film of claim 1 , wherein the adhesive composition further comprises at least one of a solvent, a curing agent, a dispersant, a thermal initiator, a silane coupling agent, a plasticizer, a tackifier, a photoinitiator, an antioxidant, or a UV stabilizer.

9. The foldable display protective film of claim 1 , wherein the adhesive layer has a thickness of 10 μm to 100 μm.

10. The foldable display protective film of claim 1 , wherein the protective substrate has a thickness of 25 μm to 150 μm.

11. The foldable display protective film of claim 1 , wherein the protective substrate is selected from the group consisting of polyethylene terephthalate (PET), polyester, polycarbonate (PC), polyimide (PI), polyethylene naphthalate (PEN), polyether ether ketone (PEEK), polyarylate (PAR), polycyloolefin (PCO), polynorbornene, polyethersulfone (PES), glass, and a cycloolefin polymer (COP).

12. The foldable display protective film of claim 1 , further comprising a release film provided on a surface of the adhesive layer, which is opposite to a surface thereof being in contact with the protective substrate.

13. The foldable display protective film of claim 1 , having a haze of more than 0% to not more than 2%, a yellow index of more than 0 to not more than 3, and a light transmittance of 85% or more at a wavelength of 550 nm.

14. A foldable display device comprising:

a foldable display; and

the foldable display protective film according to claim 1 provided on one surface of the foldable display,

wherein the adhesive layer of the foldable display protective film is in contact with one surface of the foldable display.

15. The foldable display device of claim 14 , wherein the foldable display has a structure in which a flexible substrate, an organic light-emitting layer, a polarizing plate and a cover window are sequentially laminated, and the adhesive layer of the foldable display protective film is provided on a surface of the cover window, which is opposite to a surface thereof being in contact with the polarizing plate.

16. The foldable display device of claim 15 , wherein the flexible substrate is at least one of thermoplastic polyurethane (TPU), polydimethylsiloxane (PDMS), glass, polyethylene terephthalate (PET), polyester, polycarbonate (PC), polyimide (PI), polyethylene naphthalate (PEN), polyether ether ketone (PEEK), polyarylate (PAR), polycycloolefin (PCO), polynorbornene, polyethersulfone (PES), or a cycloolefin polymer (COP).