Bed material for thermolytic fragmentation of sugars
The present invention relates to a process for thermolytic fragmentation of a sugar into a composition comprising C 1 -C 3 oxygenates. In particular, it relates to the use of heat carrying particles providing improved yields of C 1 -C 3 oxygenates and improved fluidization characteristics making it suitable for industrial scale production of e.g. glycolaldehyde. It also regards a circulating fluidized bed system comprising the heat carrying particles.
1. A process for thermolytic fragmentation of a sugar into a composition comprising C 1 -C 3 oxygenates, the process comprising:
a. providing a circulating, fluidized stream of heat carrying particles, wherein the heat carrying particles are circulated to a heating zone to produce heated heat carrying particles, and then the heated heat carrying particles are circulated from the heating zone to a fragmentation zone to provide heat to the fragmentation zone and producing cooled heat carrying particles, and then the cooled heat carrying particles are circulated back to the heating zone for reheating;
b. introducing a feedstock solution comprising the sugar into the fragmentation zone of the circulating, fluidized stream of heat carrying particles to absorb heat and convert the sugar by thermolytic fragmentation into the C 1 -C 3 oxygenates;
c. separating a fragmentation product stream comprising the C 1 -C 3 oxygenates from the stream of cooled heat carrying particles; and then
d. recovering the composition comprising C 1 -C 3 oxygenates from the fragmentation product stream,
wherein the number of acid sites on the surface of the heat carrying particles is less than 3 μmol/g as measured by NH 3 -TPD.
2. The process according to claim 1 , wherein the particle surface area of the heat carrying particles is below 3 square meters per g.
3. The process according to claim 1 , wherein at least 90% by weight of the heat carrying particles consist of silicium, aluminium and oxygen and the mass ratio of silicium to aluminium is from 0.25 to 1.
4. The process according to claim 1 , wherein the number of acid sites on the surface of the heat carrying particles is less than 0.5 μmol/g as measured by NH 3 -TPD.
5. The process according to claim 1 , wherein the number of basic sites on the surface of the heat carrying particles is less than 1 μmol/g as measured by CO 2 -TPD.
6. The process according to claim 1 , wherein the fluidization index of the heat carrying particles is above 1.
7. The process according to claim 1 , wherein 90-100% by weight of the heat carrying particles consist of silicium, aluminium and oxygen and the mass ratio of silicium to aluminium is of from 0.25 to 1.
8. The process according to claim 1 , wherein at least 50% by weight of the heat carrying particles consist of mullite.
9. The process according to claim 1 , wherein the heat carrying particles have been calcined at a temperature of at least 1000° C.
10. The process according to claim 1 , wherein the heat carrying particles has a melting point above 1100° C.
11. The process according to claim 1 , wherein the particle density of the heat carrying particles is below 3.5 g/ml, as measured by Hg porosimetry.
12. The process according to claim 1 , wherein the Sauter mean diameter of the heat carrying particles is from 50-150 μm.
13. The process according to claim 1 , wherein the feedstock solution comprising the sugar is fed directly into the fragmentation zone.
14. The process according to claim 1 , wherein the sugar is a mono- and/or di-saccharide.
15. The process according to claim 1 , wherein the feedstock solution comprises an aqueous solution of a sugar selected from the group consisting of sucrose, lactose, xylose, arabinose, ribose, mannose, tagatose, galactose, glucose and fructose; or mixtures thereof.
16. The process according to claim 1 , wherein the concentration of sugar in the feedstock solution is between 10 and 90% by weight.
17. The process according to claim 1 , wherein the composition comprising the C 1 -C 3 oxygenates comprises one or more of glycolaldehyde, glyoxal, pyruvaldehyde, acetol and formaldehyde.
18. The process according to claim 1 , wherein the fragmentation zone has a fragmentation temperature in the range of from 250-900° C.
19. The process according to claim 1 , wherein the heated heat carrying particles have a temperature in the range of from 300-950° C., as measured when the heated heat carrying particles leave the heating zone.
20. The process according to claim 1 , wherein the cooled heat carrying particles have a temperature in the range of from 200-850° C., as measured when the cooled heat carrying particles leave the fragmentation zone.
21. The process according to claim 1 , wherein the fragmentation zone is delimited by a riser suitable for conducting thermolytic fragmentation of a feedstock solution comprising a sugar and suitable for fluidizing the stream of heat carrying particles.
22. The process according to claim 1 , wherein the heating zone is delimited by a riser suitable for heating and suitable for fluidizing the stream of heat carrying particles.
23. The process according to claim 1 , wherein the fragmentation product stream is separated from the stream of cooled heat carrying particles by inertial separation.
24. The process according to claim 1 , wherein the composition comprising the C 1 -C 3 oxygenates is recovered by quench cooling of the fragmentation product stream.
25. The process according to claim 1 , wherein the ratio of the mass flow rate of heat carrying particles per mass flow rate of feedstock is between 12:1 and 200:1.
26. The process according to claim 1 , wherein step d) of recovering the composition comprising C 1 -C 3 oxygenates comprises collecting the fragmentation product stream and conveying it to a hydrogenation unit to convert the C 1 -C 3 oxygenates into the corresponding poly-alcohols.
27. A process for thermolytic fragmentation of a sugar into a composition comprising C 1 -C 3 oxygenates, the process comprising:
a. providing a circulating, fluidized stream of heat carrying particles, wherein the heat carrying particles are circulated to a heating zone to produce heated heat carrying particles, and then the heated heat carrying particles are circulated from the heating zone to a fragmentation zone to provide heat to the fragmentation zone and producing cooled heat carrying particles, and then the cooled heat carrying particles are circulated back to the heating zone for reheating,
b. introducing a feedstock solution comprising the sugar into the fragmentation zone of the circulating, fluidized stream of heat carrying particles to absorb heat and convert the sugar by thermolytic fragmentation into the C 1 -C 3 oxygenates;
c. separating a fragmentation product stream comprising the C 1 -C 3 oxygenates from the stream of cooled heat carrying particles; and then
d. recovering the composition comprising C 1 -C 3 oxygenates from the fragmentation product stream,
wherein the particle surface area of the heat carrying particles is below 3 square meters per g,
wherein at least 90% by weight of the heat carrying particles consist of silicium, aluminium and oxygen and the mass ratio of silicium to aluminium is from 0.25 to 1.
28. A process for thermolytic fragmentation of a sugar into a composition comprising C 1 -C 3 oxygenates, the process comprising:
a. providing a circulating, fluidized stream of heat carrying particles, wherein the heat carrying particles are circulated to a heating zone to produce heated heat carrying particles, and then the heated heat carrying particles are circulated from the heating zone to a fragmentation zone to provide heat to the fragmentation zone and producing cooled heat carrying particles, and then the cooled heat carrying particles are circulated back to the heating zone for reheating;
b. introducing a feedstock solution comprising the sugar into the fragmentation zone of the circulating, fluidized stream of heat carrying particles to absorb heat and convert the sugar by thermolytic fragmentation into the C 1 -C 3 oxygenates;
c. separating a fragmentation product stream comprising the C 1 -C 3 oxygenates from the stream of cooled heat carrying particles; and then
d. recovering the composition comprising C 1 -C 3 oxygenates from the fragmentation product stream,
wherein the number of basic sites on the surface of the heat carrying particles is less than 1 μmol/g as measured by CO 2 -TPD.
29. The process according to claim 1 , wherein the number of acid sites on the surface of the heat carrying particles is less than 1 μmol/g as measured by NH 3 -TPD.