Non-magnetic austenitic stainless steel
Provided is a non-magnetic austenitic stainless steel. According to an embodiment of the disclosed non-magnetic austenitic stainless steel, the non-magnetic austenitic stainless steel includes, in percent by weight (wt %), 0.01 to 0.1% of carbon (C), 1.5% or less (excluding 0) of silicon (Si), 0.5 to 3.5% of manganese (Mn), 16 to 22% of chromium (Cr), 7 to 15% of nickel (Ni), 3% or less of molybdenum (Mo), 0.01 to 0.3% of nitrogen (N), and the remainder of iron (Fe) and inevitable impurities, wherein a value of Expression (1) below is a negative value: (1) 3*(Cr+Mo)+5*Si−65*(C+N)−2*(Ni+Mn)−28, wherein in Expression (1), Cr, Mo, Si, C, N, Ni, and Mn denote contents (wt %) of the alloy elements, respectively.
1. A non-magnetic austenitic stainless steel comprising, in percent by weight (wt %), 0.01 to 0.1% of carbon (C), 1.5% or less (excluding 0) of silicon (Si), 0.5 to 3.5% of manganese (Mn), 16 to 22% of chromium (Cr), 7 to 15% of nickel (Ni), 3% or less of molybdenum (Mo), 0.01 to 0.3% of nitrogen (N), and the remainder of iron (Fe) and inevitable impurities,
wherein the austenitic stainless steel comprises more than 0% by area fraction of the ferrite phase,
wherein a magnetic permeability is 1.02 or less when a thickness is 1 mm or less,
wherein a value of Expression (2) below is 70 or more:
Σ A 5 /ΣA× 100 (2)
(wherein in Expression (2), ΣA 5 is a sum of areas of ferrite grains having an area of 5 μm2 or less, and ΣA is a sum of areas of all ferrite grains).
2. The non-magnetic austenitic stainless steel of claim 1 , further comprising, in percent by weight (wt %), 2.5% or less of copper (Cu).