Method of preparation of a garnet-type inorganic material
The present invention relates to a method of preparation of a garnet-type inorganic material. It also relates to the garnet-type inorganic material itself. The process comprises the following steps: (1) bringing an aqueous solution S comprising (i) a salt of zirconium, (ii) a salt of lanthanum and (iii) a salt of the element A or a precursor of an oxide of element A into contact with an aqueous solution of a basic compound, as a result of which a precipitate suspended in the reaction medium is obtained; (2) stirring the reaction medium obtained at the end of step (1) for at least 30 min; (3) bringing the precipitate obtained at the end of step (2) into contact with an additive selected in the group consisting of: anionic surfactants; nonionic surfactants; polyethylene glycols; carboxylic acids and their salts; and surfactants of the carboxymethylated fatty alcohol ethoxylate type; (4) calcining in air the precipitate recovered at the end of the previous step at a temperature which is at least 400° C.; (5) bringing into contact the product obtained at the end of step (4) with a salt of lithium; (6) calcining in air the product obtained at the end of step (5) at a temperature between 700° C. and 1100° C.; 20 the inorganic compound M comprising or consisting essentially of a garnet oxide or garnet-type oxide containing, as constituent elements, the elements Li, La, Zr and at least one element A selected in the group consisting of Al, Ga, Nb, Fe, W, Ta, or a mixture thereof.
1. An inorganic material M comprising a garnet oxide or garnet-type oxide containing, as constituent elements, the elements Li, La, Zr and at least one element A selected from the group consisting of Al, Ga, Nb, Fe, W, Ta, and a mixture thereof, the oxide being described by formula (I):
[Li x1 La 3 Zr z A w O 12 ] (I)
wherein:
x1, z and w are positive real numbers;
1.20<z≤2.10;
0<w≤0.80; and
x1 is derived from the electroneutrality of the oxide; and
exhibiting:
a ratio R50 higher than 50%, R50 being defined by:
R 50(%)=( D 50− D US 50)/ D 50×100
wherein D50 and D us 50 are the median diameters of distributions in volume of the diameters of a dispersion of the particles of the inorganic material M in N-methyl-2-pyrrolidone (NMP), obtained with a laser diffractometer, D us 50 being measured after a treatment under ultrasound which consists of inserting an ultrasonic probe into a dispersion of 100 mg of the inorganic material M in 160 mL of NMP and in submitting the dispersion to sonication under a power of 140±10 W for 22 minutes and/or
a ratio R90 higher than 50%, R90 being defined by:
R90 (%)=(D90-D us 90)/D90×100
wherein D90 and D us 90 correspond to the diameters of the particles for which 90% of the particles have a diameter which is less than D90 and are determined from distributions in volume of the diameters of a dispersion of the particles of the inorganic material M in N-methyl-2-pyrrolidone (NMP), obtained with a laser diffractometer, D us 90 being measured after a treatment under ultrasound which consists of inserting an ultrasonic probe into a dispersion of 100 mg of the inorganic material M in 160 mL of NMP and in submitting the dispersion to sonication under a power of 140±10 W for 22 minutes.
2. The inorganic material M according to claim 1 wherein the relative composition of the cations in the inorganic material M corresponds to formula:
Li x1 La 3 Zr z A w (II)
wherein:
w, x and z are positive real numbers;
1.20<z≤2.10;
0<w≤0.80; and
4.00≤x≤10.5.
3. The inorganic material M according to claim 1 wherein the relative composition of the cations in the inorganic material M corresponds to formula:
Li x La 3 Zr z A 1 w1 A 2 w2 (IIa)
wherein:
A1 is selected from the group consisting of Al, Ga, Fe or a combination thereof;
A2 is selected from the group consisting of Nb, Ta or a combination thereof;
w1, w2, x and z are positive real numbers;
1.20<z≤2.10;
0<w1≤0.20;
0.10<w2≤0.80;
w1 and w2 being such that w=w1+w2 and w≤0.80; and
5.60≤x≤10.35.
4. The inorganic material M according to claim 1 wherein the relative composition of the cations in the inorganic material M corresponds to formula:
Li x La 3 Zr z A1 w1 A2 w2 (IIb)
wherein:
A1 is selected from the group consisting of Al, Ga, Fe or a combination thereof;
A2 is W;
w1, w2, x and z are positive real numbers;
1.20<z≤2.10;
0<w1≤0.20;
0.10<w2≤0.80;
w1 and w2 being such that w=w1+w2 and w≤0.80; and
4.80≤x≤10.20.
5. The inorganic material M according to claim 1 wherein Zr is partly replaced by Hf in the oxide.
6. The inorganic material M according to claim 1 wherein the primary particles of the inorganic material M exhibit a d50 between 0.5 μm and 7.0 μm.
7. The inorganic material M according to claim 1 wherein the particles of the inorganic material M exhibt a D50 between 10.0 and 50.0 μm.
8. A process of preparation of the inorganic material M of claim 1 , the process comprising the following steps:
(1) bringing an aqueous solution S comprising (i) a salt of zirconium, (ii) a salt of lanthanum and (iii) a salt of the element A or a precursor of an oxide of element A into contact with an aqueous solution of a basic compound, as a result of which a precipitate suspended in the reaction medium is obtained;
(2) stirring the reaction medium obtained at the end of step (1) for at least 30 min;
(3) bringing the precipitate obtained at the end of step (2) into contact with an additive selected from the group consisting of: anionic surfactants; nonionic surfactants; polyethylene glycols;
carboxylic acids and their salts; and surfactants of the carboxymethylated fatty alcohol ethoxylate type;
(4) calcining in air the precipitate recovered at the end of the previous step at a temperature which is at least 400° C.;
(5) bringing into contact the product obtained at the end of step (4) with a salt of lithium;
(6) calcining in air the product obtained at the end of step (5) at a temperature between 700° C. and 1100° C.;
the inorganic compound M comprising or consisting essentially of a garnet oxide or garnet-type oxide containing, as constituent elements, the elements Li, La, Zr and at least one element A selected in the group consisting of Al, Ga, Nb, Fe, W, Ta, or a mixture thereof.
9. The process according to claim 8 wherein the salt of zirconium is selected from the group of zirconium nitrate and zirconium chloride.
10. The process according to claim 8 wherein in step (2), the reaction medium is stirred for at least 30 minutes and the temperature of the reaction medium is between 50° C. and 200° C.
11. The process according to claim 8 wherein the additive is a carboxylic acid or a salt thereof.
12. The process according to claim 8 wherein the temperature of calcination in step (4) is between 400° C. and 800° C.
13. The process according to claim 8 wherein the bringing into contact of step (5) consists of impregnating the product obtained at the end of the step (4) with an aqueous solution of a salt of lithium or in mixing together the product obtained at the end of step (4) and the salt of lithium, both being in the powder form.
14. The process according to claim 8 wherein in step (6), the product obtained at the end of step (5) is first calcined in air at a temperature between 700° C. and 900° C. and then calcined in air at a temperature between 900° C. and 1100° C.
15. An inorganic material M obtainable by the process according to claim 8 .
16. A composition (C) comprising:
(i) the inorganic material M of claim 1 ;
(ii) at least one electro-active compound (EAC);
(iii) optionally at least one lithium ion-conducting material (LiCM) other than the inorganic material M;
(iv) optionally at least one electro-conductive material (ECM);
(v) optionally a lithium salt (LIS); and
(vi) optionally at least one polymeric binding material (P).
17. An electrode (E) comprising:
a metal substrate;
directly adhered onto said metal substrate, at least one layer L made of a composition (Cof claim 16 .
18. A separator (SP) comprising:
the inorganic material M claim 1 ;
optionally at least one polymeric binding material (P);
optionally at least one metal salt, notably a lithium salt; and
optionally at least one plasticizer.
19. Lithium ion battery comprising the inorganic material M of of claim 1 .
20. An inorganic material M comprising a garnet oxide or garnet-type oxide containing, as constituent elements, the elements Li, La, Zr and at least one element A selected from the group consisting of Al, Ga, Nb, Fe, W, Ta, and a mixture thereof, the oxide being described by formula (I):
[Li x1 La 3 Zr Z A W O 12 ] (I)
wherein:
x1, z and w are positive real numbers;
1.20<z≤2.10;
0<w≤0.80;
x1 is derived from the electroneutrality of the oxide; and
exhibiting:
a ratio R50 higher than 50%, R50 being defined by:
R 50(%)=( D 50 −D us 50)/ D 50×100
wherein D50 and D us 50 are the median diameters of distributions in volume of the diameters of a dispersion of the particles of the inorganic material M in N-methyl-2-pyrrolidone (NMP), obtained with a laser diffractometer, D us 50 being measured after a treatment under ultrasound which consists of inserting an ultrasonic probe into a dispersion of 100 mg of the inorganic material M in 160 mL of NMP and in submitting the dispersion to sonication under a power of 140±10 W for 22 minutes.