Continuous additive manufacturing method for making ceramic articles, and ceramic articles
The present disclosure provides a method of making a ceramic article. The method includes (a) obtaining a photopolymerizable slurry or sol including a plurality of ceramic particles distributed in the photopolymerizable slurry or sol and (b) selectively polymerizing the photopolymerizable slurry or sol using actinic radiation and continuous movement of a build substrate through the photopolymerizable slurry or sol to form a gelled article. The method also includes (c) extracting solvent from the gelled article to form an aerogel article or a xerogel article; (d) heat treating the aerogel article or the xerogel article to form a porous ceramic article; and (e) sintering the porous ceramic article to form a sintered ceramic article. The sintered ceramic article exhibits a particular density. Further, additive manufactured ceramic articles are provided that exhibit a particular density, opacity, or both. Preferably, all cross-sectional portions of an interior of the ceramic article having selected dimensions are free of a frequency analysis signal maxima larger than a background signal.
1 . An additive manufacturing method of making a ceramic article, the method comprising:
a) obtaining a photopolymerizable sol comprising a plurality of ceramic particles distributed in the photopolymerizable sol, wherein the ceramic particles have an average particle size diameter of 1 nanometer (nm) to 100 nm;
b) selectively polymerizing the photopolymerizable sol using actinic radiation while moving a build substrate through the photopolymerizable sol in an uninterrupted motion during an entirety of the polymerization to form a gelled article;
c) extracting solvent from the gelled article to form an aerogel article or a xerogel article;
d) heat treating the aerogel article or the xerogel article to form a porous ceramic article; and
e) sintering the porous ceramic article to form a sintered ceramic article;
wherein the sintered ceramic article exhibits a density of 98% or greater with respect to a theoretical density of a ceramic material of the ceramic particles and exhibits an opacity of 80% or less.
2 . The method of claim 1 , wherein the actinic radiation is directed at the photopolymerizable sol from above the photopolymerizable sol.
3 . The method of claim 1 , wherein the photopolymerizable sol is provided in a container and the build substrate moves towards a floor of the container during the selective polymerization of the photopolymerizable sol.
4 . The method of claim 1 , wherein the actinic radiation is provided by a projector projecting a sequence of two-dimensional images.
5 . The method of claim 1 , wherein the extracting is performed using supercritical fluid.
6 . The method of claim 1 , wherein the sintered ceramic article exhibits a density of 99% or greater, with respect to a theoretical density of the ceramic material.
7 . The method of claim 1 , wherein all cross-sectional portions of an interior of the sintered ceramic article having a plane with dimensions of 0.5 millimeters (mm)×0.5 mm are free of any frequency analysis signal maxima larger than a background signal.
8 . The method of claim 1 , wherein the sintered ceramic article exhibits an opacity of 70% or less.
9 . The method of claim 1 , wherein the sintered ceramic article exhibits a flex strength of 100 megapascals (MPa) or greater.
10 . The method of claim 1 , wherein the photopolymerizable sol comprises 3 to 45 vol. % of ceramic particles, based at least in part on the total volume of the photopolymerizable sol.
11 . The method of claim 1 , wherein the ceramic particles comprise metal oxide ceramic particles, non-oxide ceramic particles, or combinations thereof.
12 . The method of claim 1 , wherein the ceramic particles are selected from the group consisting of zirconia, silica, alumina, yttria, ceria, magnesium-magnesia aluminate (MMA), magnesium oxide, hydroxyapatite, fluorapatite, chlorapatite, calcite, cordierite, silicon carbide, silicon nitride, boron carbide, titanium diboride, zirconium diboride, boron nitride, titanium carbide, zirconium carbide, aluminum nitride, calcium hexaboride, MAX phase, and combinations thereof.
13 . The method of claim 1 , further comprising, prior to step b), retrieving, from a non-transitory machine readable medium, data representing a 3D model of a gelled article; and executing, by one or more processors, a 3D printing application interfacing with a manufacturing device using the data to generate, by the manufacturing device, a physical object of the gelled article.
14 . The method of claim 1 , further comprising, prior to step b), receiving, by a manufacturing device having one or more processors, a digital object comprising data specifying a gelled article; and generating, with the manufacturing device by an additive manufacturing process, the gelled article based at least in part on the digital object.
15 . The method of claim 1 , wherein the actinic radiation is provided as a continuous sequence of projected images during the uninterrupted motion of the build substrate.
16 . The method of claim 1 , further comprising forming a coating layer on at least a portion of the gelled article prior to heat treating.
17 . The method of claim 1 , wherein the photopolymerizable sol comprises an absorption modifier in an amount of 0.01 to 1 weight percent based at least in part on a total weight of the photopolymerizable sol.
18 . The method of claim 1 , wherein the gelled article is formed at a substantially constant rate of 0.5 millimeters per minute or greater along a build axis.
19 . A ceramic article made by the method of claim 1 .
20 . An additive manufactured ceramic article exhibiting a density of 98% or greater with respect to a theoretical density of a ceramic material and exhibiting an opacity of 80% or less, wherein all cross-sectional portions of an interior of the additive manufactured ceramic article having a plane with dimensions of 0.5 mm×0.5 mm are free of a frequency analysis signal maxima larger than a background signal, and wherein the additive manufactured ceramic article is formed by continuous additive manufacturing involving uninterrupted movement of a substrate during photopolymerization of a photopolymerizable sol.