Aluminosilicates, related processes and uses thereof as supplementary cementing materials
The present disclosure concerns an aluminosilicate having a Blaine fineness of about 500 m 2 /kg to about 3000 m 2 /kg and/or a specific surface area of about 4 m 2 /g to about 20 m 2 /g, as well as the uses thereof. The present disclosure also comprises a dry cementing composition and a mortar or concrete composition, the compositions comprising said aluminosilicate. The present disclosure also comprises a process for the manufacture of aluminosilicate. The process comprises: roasting a spodumene concentrate in an acid medium; leaching the acidic roast spodumene concentrate so as to obtain a mixture comprising a solid comprising the aluminosilicate and a leachate; and separating the aluminosilicate from the leachate in an acid medium, wherein said aluminosilicate contains a calcium concentration of less than about 5%.
1. Aluminosilicate having a Blaine fineness of about 500 m 2 /kg to about 3000 m 2 /kg, said aluminosilicate having a silica content of about 66% to about 90% by weight and said aluminosilicate having an alumina content of about 10% to 45% by weight.
2. The aluminosilicate according to claim 1 , said aluminosilicate having the Blaine fineness of about 750 m 2 /kg to about 2500 m 2 /kg.
3. The aluminosilicate according to claim 1 , said aluminosilicate having the Blaine fineness of about 1500 m 2 /kg to about 2000 m 2 /kg.
4. The aluminosilicate according to claim 1 , said aluminosilicate having a density of about 2 g/cm 2 to about 3 g/cm 2 .
5. The aluminosilicate according to claim 1 , said aluminosilicate having a density of about 2.5 g/cm 2 to about 3 g/cm 2 .
6. The aluminosilicate according to claim 1 , said aluminosilicate having a passing rate at 45 μm of about 40% to 90%.
7. The aluminosilicate according to claim 1 , said aluminosilicate having a passing rate at 45 μm of about 45% to 55%.
8. The aluminosilicate according to claim 1 , said aluminosilicate having a silica content of about 66% to about 85% by weight.
9. The aluminosilicate according to claim 1 , said aluminosilicate having a silica content of about 66% to about 75% by weight.
10. The aluminosilicate according to claim 1 , said aluminosilicate having an alumina content of about 15% to 40% by weight.
11. The aluminosilicate according to claim 1 , said aluminosilicate having an alumina content of about 20% to 30% by weight.
12. The aluminosilicate according to claim 1 , said aluminosilicate having an alumina content of about 23% to 27% by weight.
13. The aluminosilicate according to claim 1 , said aluminosilicate comprising less than 2% by weight alkali metal or alkaline earth metal content.
14. The aluminosilicate according to claim 13 , said alkali metals being chosen from Li, Na and K.
15. The aluminosilicate according to claim 13 , said alkaline earth metals being chosen from Mg and Ca.
16. The aluminosilicate according to claim 1 , said aluminosilicate comprising less than 2% by weight calcium content.
17. The aluminosilicate according to claim 1 , said aluminosilicate comprising about 0.1% to about 3% by weight calcium content.
18. The aluminosilicate according to claim 1 , said aluminosilicate comprising about 0.1% to about 1% by weight calcium content.
19. The aluminosilicate according to claim 15 , said calcium being in the form of gypsum.
20. The aluminosilicate according to claim 1 , said aluminosilicate comprising a moisture content of less than 2% by weight.