BINDER COMPOSITION FOR ELECTRICITY STORAGE DEVICES, SLURRY FOR ELECTRICITY STORAGE DEVICE ELECTRODES, ELECTRICITY STORAGE DEVICE ELECTRODE, AND ELECTRICITY STORAGE DEVICE
A binder composition for an electrical storage device, may allow producing an electrical storage device electrode excellent in flexibility and adhesiveness, and show satisfactory charge-discharge durability. Such binder compositions may include: a polymer (A); and a liquid medium (B), wherein, with respect to 100 parts by mass in total of repeating units contained in the polymer (A), the polymer (A) contains: 20 parts by mass to 60 parts by mass of a repeating unit (a1) derived from a conjugated diene compound; 35 parts by mass to 75 parts by mass of a repeating unit (a2) derived from an aromatic vinyl compound; and 1 part by mass to 10 parts by mass of a repeating unit (a3) derived from an unsaturated carboxylic acid, and wherein a THF-soluble component of the polymer (A) has a weight average molecular weight of from 100,000 to 600,000.
1 . A binder composition suitable for an electrical storage device, the composition comprising:
a polymer (A); and
a liquid medium (B),
wherein a THF-soluble component of the polymer (A) has a weight average molecular weight in a range of from 100.000 to 600.000, and
wherein, with respect to 100 parts by mass in total of repeating units in the polymer (A), the polymer (A) comprises:
a conjugated diene compound (a1), in polymerized form, in a range of from 20 to 60 parts by mass;
an aromatic vinyl compound (a2), in polymerized form, in a range of from 35 to 75 parts by mass; and
an unsaturated carboxylic acid (a3), in polymerized form, in a range of from 1 to 10 parts by mass.
2 . The composition of claim 1 , having a surface tension in a range of from 45 to 60 mN/m at a solid content concentration of 40% and a temperature of 25° C.
3 . The composition of claim 1 , wherein the polymer (A) has a THF gel in a range of from 60 to 99%.
4 . The composition of claim 1 , wherein the polymer (A) is polymer particles, and
wherein the polymer particles have a number average particle diameter in a range of from 50 to 500 nm.
5 . The composition of claim 1 , wherein the liquid medium (B) is water.
6 . A slurry suitable for an electrical storage device electrode, the slurry comprising:
the binder composition of claim 1 ; and
an active material.
7 . The slurry of claim 6 , wherein the active material comprises a silicon material.
8 . An electrical storage device electrode, comprising:
a current collector; and
an active material layer, formed on a surface of the current collector by applying and drying the slurry of claim 6 .
9 . An electrical storage device, comprising:
the electrical storage device electrode of claim 8 .