Silica gel as reinforcement agent for rubber compounds
The claimed invention refers to the development of rubber recipes to improve essential properties related to correlated rubber compounds. Silica gel is added to the rubber compound as a reinforcing agent, partially replacing some of the precipitated silica. The use of silica gel for the pneumatic market provides improved tear resistance, elongation and adhesion performance, and improves adhesion of the tire on wet surfaces.
1. A reinforced rubber compound comprising rubber and reinforcement fillers, wherein said reinforcement fillers comprise precipitated silica and unmodified silica gel, wherein the unmodified silica gel ranges comprises from 5 wt % to 30 wt % of the total silica content of the reinforcement fillers.
2. The reinforced rubber compound of claim 1 , wherein said unmodified silica gel has a porosity in the range of 1.0 to 1.8 cubic centimeters per gram of unmodified silica gel, a surface area in the range of 200 to 500 square meters per 1 gram of unmodified silica gel, a pH between 5.5 and 8.5, and a particle size in the range of 1 micron to 100 microns.
3. The reinforced rubber compound of claim 1 , wherein said unmodified silica gel has a porosity in the range of 1.0 to 1.8 cubic centimeters per gram of unmodified silica gel.
4. The reinforced rubber compound of claim 1 , wherein said unmodified silica gel has a surface area in the range of 200 to 500 square meters per 1 gram of unmodified silica gel.
5. The reinforced rubber compound of claim 1 , wherein said unmodified silica gel has a pH between 5.5 and 8.5.
6. The reinforced rubber compound of claim 1 , wherein said unmodified silica gel has a particle size in the range of 1 micron to 100 microns.
7. The reinforced rubber compound of claim 1 , wherein said unmodified silica gel has a porosity in the range of 1.0 to 1.8 cubic centimeters per gram of unmodified silica gel, a surface area in the range of 200 to 500 square meters per 1 gram of unmodified silica gel, a pH between 5.5 and 8.5, and a particle size in the range of 1 micron to 100 microns.