Walkway roll
A walkway roll includes a thermoplastic olefin; and an olefin block copolymer present in an amount of 5 wt. % to 18 wt. % based on a total weight of the walkway roll. The walkway roll includes an embossed region. The embossed region, according to a heat aging test at 275° F. for 37 weeks, shows no cracks.
1. A pad of a walkway roll having an upper surface and a lower surface, the pad comprising:
a thermoplastic olefin; and
an olefin block copolymer present in an amount of 5 wt. % to 18 wt. % based on a total weight of the pad,
wherein at least the upper surface of the pad comprises (i) an embossed region, wherein the embossed region, tested according to a heat aging test at 275° F. for 37 weeks, shows no cracks, and (ii) at least one lap weld region that is not embossed, wherein the at least one lap weld region is configured to be attached to a thermoplastic roofing membrane,
wherein the pad is configured to protect and to at least partially cover the thermoplastic roofing membrane, such that the lower surface of the pad is configured to attach to an upper surface of the thermoplastic roofing membrane, and
wherein, when the lower surface of the pad is attached to the upper surface of the thermoplastic roofing membrane, the embossed region is provided on the upper surface of the pad and is configured to be exposed to foot traffic on a roof.
2. The pad of claim 1 , wherein the thermoplastic olefin is present in an amount of 28 wt. % to 88 wt. % based on the total weight of the pad.
3. The pad of claim 1 , wherein the embossed region has an average stiffness in a length direction of 140 S T to 400 S T .
4. The pad of claim 1 , wherein the embossed region has an average stiffness in a width direction of 140 S T to 350 S T .
5. The pad of claim 1 , wherein the embossed region is disposed between a pair of lap weld regions.
6. The pad of claim 1 , wherein the at least one lap weld region has an average stiffness in a length direction of 50 S T to 200 S T .
7. The pad of claim 1 , wherein the at least one lap weld region has an average stiffness in a width direction of 50 S T to 150 S T .
8. The pad of claim 1 , wherein the at least one lap weld region, tested according to a heat aging test at 275° F. for 37 weeks, shows no cracks.
9. The pad of claim 1 , comprising CaCO 3 .
10. The pad of claim 1 , wherein the olefin block copolymer, tested according to ASTM D792, has a density of 0.87 g/cm 3 to 0.90 g/cm 3 .
11. The pad of claim 1 , wherein the thermoplastic olefin has a melt flow rate, tested according to ASTM D1238, of 0.6 g/10 min to 15 g/10 min, and a density, tested according to ASTM D792, of 0.87 g/cm 3 to 0.90 g/cm 3 .
12. A walkway roll having an upper surface and a lower surface, the walkway roll comprising:
a thermoplastic olefin; and
an olefin block copolymer present in an amount of 5 wt. % to 18 wt. % based on a total weight of the walkway roll,
wherein at least the upper surface of the walkway roll comprises (i) an embossed region, wherein the embossed region, tested according to a heat aging test at 275° F. for 37 weeks, shows no cracks, and (ii) at least one lap weld region that is not embossed, wherein the at least one lap weld region is configured to be attached to a thermoplastic roofing membrane,
wherein the lower surface of the walkway roll is configured to attach to an upper surface of the thermoplastic roofing membrane, and
wherein, when the lower surface of the walkway roll is attached to the upper surface of the thermoplastic roofing membrane, the embossed region is provided on the upper surface of the walkway roll and is configured to be exposed to foot traffic on a roof.
13. The walkway roll of claim 12 , wherein the olefin block copolymer is present in an amount of 5 wt. % to 16 wt. % based on the total weight of the walkway roll.
14. The walkway roll of claim 12 , wherein the olefin block copolymer is present in an amount of 8 wt. % to 14 wt. % based on the total weight of the walkway roll.
15. The walkway roll of claim 12 , comprising from 1 wt. % to 50 wt. % CaCO 3 based on the total weight of the walkway roll.
16. A roofing system, comprising:
a roof decking;
a thermoplastic roofing membrane on an upper surface of the roof decking; and
a walkway roll on an upper surface of the thermoplastic roofing membrane, the walkway roll having an upper surface and a lower surface, and the walkway roll comprising:
a thermoplastic olefin; and
an olefin block copolymer present in an amount of 5 wt. % to 18 wt. % based on a total weight of the walkway roll,
wherein at least the upper surface of the walkway roll comprises (i) an embossed region, wherein the embossed region, tested according to a heat aging test at 275° F. for 37 weeks, shows no cracks, and (ii) at least one lap weld region that is not embossed, wherein the walkway roll is attached to the thermoplastic roofing membrane along the at least one lap weld region,
wherein the lower surface of the walkway roll is attached to the upper surface of the thermoplastic roofing membrane, such that the embossed region is provided on the upper surface of the walkway roll and is configured to be exposed to foot traffic on a roof.
17. The roofing system of claim 16 , wherein the olefin block copolymer has a density, tested according to ASTM D792, of 0.87 g/cm 3 to 0.90 g/cm 3 .
18. The roofing system of claim 16 , wherein the thermoplastic olefin has a melt flow rate, tested according to ASTM D1238, of 0.6 g/10 min to 15 g/10 min, and a density, tested according to ASTM D792, of 0.87 g/cm 3 to 0.90 g/cm 3 .
19. The roofing system of claim 16 , wherein the walkway roll comprises CaCO 3 .
20. The roofing system of claim 16 , wherein the at least one lap weld region, tested according to a heat aging test at 275° F. for 37 weeks, shows no cracks.