Electrolyte components for charging of lithium-ion batteries
The present disclosure includes bridged bicyclic compounds and other non-flat organic molecules that have the ability to solvate lithium salts in higher concentrations without significant changes to the electrolyte viscosity which assists in improving the fast charge capability of lithium-ion cells. Using non-flat polar molecules may enable higher solubility of the salts while minimizing viscosity changes to the electrolyte. In some embodiments, the fused bicyclic compound is 7-oxabicyclo[2.2.1]heptane-2-carbonitrile (BHCN).
1. A composition of an electrolyte solution for a lithium-ion battery, the composition comprising:
a fused bicyclic compound comprising: an oxygen group in a cross bridge;
a fluoroethylene carbonate (FEC); and
a salt; wherein:
the fused bicyclic compound comprises 7-oxabicyclo[2.2.1]heptane-2-carbonitrile BHCN)
the fused bicyclic compound has a concentration of about 5 wt % to about 50 wt %, and
the FEC has a concentration of about 0.5 wt % to about 10 wt %.
2. The composition of claim 1 , wherein the salt comprises at least one of lithium tetrafluoroborate (LiBF 4 ), lithium bis(trifluoromethanesylfonyl)imide (LiTFSI), lithium oxalyldifluoroborate (LiODFB), lithium fluoroalkylphosphate, lithium 4,5-dicycano-2-(trifluoromethyl)imidazolide (LiTDI), or lithium hexafluoraphosphate (LiPF 6 ).
3. The composition of claim 1 , wherein:
the salt has a concentration in the range of about 0.01 M to about 4.2 M.
4. The composition of claim 1 , further comprising:
a vinylene carbonate (VC).
5. The composition of claim 4 , wherein:
the VC has a concentration of about 0.5 wt % to about 10 wt %.
6. The composition of claim 4 , wherein:
the fused bicyclic compound has a concentration of about 10 wt %,
the FEC has a concentration of about 1 wt %, and
the VC has a concentration of about 1 wt %.
7. A lithium-ion battery comprising:
an anode;
a cathode; and
an electrolyte solution; wherein:
the electrolyte solution comprises:
a fused bicyclic compound comprising an oxygen group in a cross bridge,
a fluoroethylene carbonate (FEC), and
a salt, wherein:
the fused bicyclic compound comprises 7-oxabicyclo[2.2.1]heptane-2-carbonitrile (BHCN),
the fused bicyclic compound has a concentration of about 5 wt % to about 50 wt %, and
the FEC has a concentration of about 0.5 wt % to about 10 wt %.
8. The lithium-ion battery of claim 7 , wherein:
the lithium-ion battery has an increased cell capacity (mAh/g) over a typical lithium-ion battery containing 1.2M LiPF 6 in a combination of solvents (e.g., EC: EMC in the ratio 3:7) when the charging time to 4.2V is less than about 12 minutes.
9. The lithium-ion battery of claim 8 , wherein:
the increased cell capacity is at least 10%, when subjected to charging at currents of less than about 5 C in less than about 12 minutes for voltages less than about 4.2 V.
10. The lithium-ion battery of claim 7 , wherein:
the lithium-ion battery can be charged from 1 to 100% state of charge in less than about 12 minutes.
11. The lithium-ion battery of claim 7 , further comprising:
a vinylene carbonate (VC).
12. The lithium-ion battery of claim 11 , wherein:
the VC has a concentration of about 0.5 wt % to about 10 wt %.
13. The lithium-ion battery of claim 11 , wherein:
the fused bicyclic compound has a concentration of about 10 wt %,
the FEC has a concentration of about 1 wt %, and
the VC has a concentration of about 1 wt %.