Thin-walled heat shrink tubing
A heat shrink tubing is provided exhibiting various desirable properties, which generally comprises at least one fluorinated polymeric resin. The tubing can exhibit desirable physical properties such as heat shrink capability, high expansion/recovery ratio, low longitudinal shrinkage, low temperature recovery, and an average wall thickness of less than about 0.003 inches.
1. A PTFE heat shrink tubing having a recovery ratio (RR) greater than about 5:1.
2. The PTFE heat shrink tubing of claim 1 , wherein the RR is greater than about 5.5:1.
3. The PTFE heat shrink tubing of claim 1 , wherein the RR is greater than about 6:1.
4. The PTFE heat shrink tubing of claim 1 , wherein the PTFE heat shrink tubing has an average wall thickness of 0.003 inches or less after expansion.
5. A PTFE heat shrink tubing, wherein a linear regression performed between 310° C. to 330° C. on a diameter change vs. recovery temperature plot yields a slope value of greater than about 1.3%/° C.
6. The PTFE heat shrink tubing of claim 5 , wherein the PTFE heat shrink tubing has a RR greater than about 5:1.
7. The PTFE heat shrink tubing of claim 5 , wherein the PTFE heat shrink tubing has a RR greater than about 5.5:1.
8. The PTFE heat shrink tubing of claim 5 , wherein the PTFE heat shrink tubing has a RR of greater than about 6:1.
9. The PTFE heat shrink tubing of claim 5 , wherein the PTFE heat shrink tubing has an average wall thickness of 0.003 inches or less after expansion.
10. A PTFE heat shrink tubing, wherein the difference between a temperature corresponding to a peak temperature of a melting endotherm obtained from a DSC temperature ramp using a 10° C. per minute heating rate and a temperature corresponding to a relative minimum in an E′−T curve obtained in a DMA temperature ramp of a heat shrink tubing specimen oriented circumferentially in the tensile grips is greater than about 7.5° C.
11. The PTFE heat shrink tubing of claim 10 , wherein the PTFE heat shrink tubing has a RR greater than about 5:1.
12. The PTFE heat shrink tubing of claim 10 , wherein the PTFE heat shrink tubing has a RR greater than about 5.5:1.
13. The PTFE heat shrink tubing of claim 10 , wherein the PTFE heat shrink tubing has a RR of greater than about 6:1.
14. The PTFE heat shrink tubing of claim 10 , wherein the PTFE heat shrink tubing has an average wall thickness of 0.003 inches or less after expansion.
15. The PTFE heat shrink tubing of claim 10 , wherein a linear regression performed between 310° C. to 330° C. on a diameter change vs. recovery temperature plot yields a slope value of greater than about 1.3%/° C.
16. A heat shrink tubing, comprising a tubing with a wall comprising PTFE and having an inner diameter (ID), wherein the ID is about 0.3 inches or less after expansion and, upon heating to 350° C. for 10 minutes, the ID is reducible by at least about 78%.
17. The heat shrink tubing of claim 16 , wherein, upon heating to 350° C. for 10 minutes, the ID is reducible by at least about 80%.
18. The heat shrink tubing of claim 16 , wherein the wall of the heat shrink tubing have an average wall thickness of about 0.003 inches or less after expansion.
19. The heat shrink tubing of claim 16 , wherein the difference between a temperature corresponding to a peak temperature of a melting endotherm obtained from a DSC temperature ramp using a 10° C. per minute heating rate and a temperature corresponding to a relative minimum in an E′−T curve obtained in a DMA temperature ramp of a heat shrink tubing specimen oriented circumferentially in the tensile grips is greater than about 7.5° C.
20. The heat shrink tubing of claim 16 , wherein a linear regression performed between 310° C. to 330° C. on a diameter change vs. recovery temperature plot yields a slope value of greater than about 1.3%/° C.
21. The PTFE heat shrink tubing of claim 1 , consisting essentially of the PTFE and, optionally, one or more additives.