PROCESS FOR PRODUCING ISOCYANATE-BASED FOAM CONSTRUCTION BOARDS
A process for producing a polyurethane or polyisocyanurate construction board, the process comprising (i) providing an A-side reactant stream that includes an isocyanate-containing compound; (ii) providing a B-side reactant stream that includes a polyol and a physical blowing agent, where the physical blowing agent includes pentane, butane, and optionally a blowing agent additive that has a Hansen Solubility Parameter (δ t ) that is greater than 17 MPa −0.5 ; and (iii) mixing the A-side reactant stream with the B-side reactant stream to produce a reaction mixture.
1 . A process for producing a polyurethane or polyisocyanurate construction board, the process comprising:
(i) providing an A-side reactant stream that includes an isocyanate-containing compound;
(ii) providing a B-side reactant stream that includes a polyol and a physical blowing agent, where the physical blowing agent includes pentane, butane, and optionally a blowing agent additive that has a Hansen Solubility Parameter (δ t ) that is greater than 17 MPa −0.5 ; and
(iii) mixing the A-side reactant stream with the B-side reactant stream to produce a reaction mixture.
2 . The process of claim 1 , further comprising the step of exposing the reaction mixture to heat, and where the reaction mixture is formed into a foam construction board within a laminator.
3 . The process of claim 1 , where the B-side reactant stream includes at least 12 parts by weight blowing agent per 100 parts by weight of polyol, and where the B-side reactant stream includes at most 40 parts by weight blowing agent per 100 parts by weight of polyol.
4 . The process of claim 1 , where the mole percent of butane in the blowing agent is greater than 5 mole % based upon the entire moles of physical blowing agent, and where the mole percent of butane in the blowing agent is less than 33 mole % based upon the entire moles of physical blowing agent.
5 . The process of claim 1 , where the process produces a construction board having an index of at least 220.
6 . The process of claim 1 , where pentane component of the blowing agent is n-pentane.
7 . The process of claim 1 , where pentane component of the blowing agent is isopentane.
8 . The process of claim 1 , where pentane component of the blowing agent is devoid of cyclopentane.
9 . The process of claim 1 , where butane component of the blowing agent is n-butane.
10 . The process of claim 1 , where butane component of the blowing agent is isobutane.
11 . The process of claim 1 , where butane component of the blowing agent is devoid of cyclobutane.
12 . The process of claim 1 , where the B-side reactant stream includes at least 0.9 parts by weight blowing agent additive per 100 parts by weight polyol, and at most 6.0 parts by weight blowing agent additive per 100 parts by weight polyol.
13 . The process of claim 1 , where the blowing agent additive has a Hansen Solubility Parameter that is greater than 17.5 MPa −0.5 .
14 . The process of claim 1 , where the blowing agent additive has a Hansen Solubility Parameter of from 17.0 to 35.0 MPa −0.5 .
15 . The process of claim 1 , where the blowing agent additive has a boiling point, at one atmosphere, of less than 150° C.
16 . The process of claim 1 , where the blowing agent additive has a boiling point, at one atmosphere, of from about 5° C. to about 150° C.
17 . The process of claim 1 , where the blowing agent consists of the butane, pentane, optionally the blowing agent additive, and optionally a chemical blowing agent.
18 . The process of claim 1 , where the blowing agent additive is selected from the group consisting of ketones, aldehydes, ethers, esters, halogenated hydrocarbons, and aromatics.
19 . A process for producing a polyurethane or polyisocyanurate construction board, the process comprising:
(i) combining polyol, isocyanate, pentane, butane, optionally a blowing agent additive that has a Hansen Solubility Parameter (δ t ) that is greater than 17 MPa −0.5 , and less than 1.5 parts by weight water per 100 parts by weight polyol to form a foam-forming mixture where the ratio of polyol to isocyanate provides a closed-cell foam having an Index of at least 210, and where the amount of pentane, butane, blowing agent additive, and any water present provide a closed-cell foam having a density of 1.0 to 2.5 lbs/ft 3 , and where the pentane, butane, and the optional blowing agent additive form a blowing agent mixture, and where the optional blowing agent mixture includes from about 5 to about 33 mole % blowing agent additive based on the total moles of blowing agent mixture;
(ii) depositing the foam-forming mixture on a facer; and
(iii) heating the foam-forming mixture to form a closed-cell foam.
20 . A method of improving the R-Value of a construction board at a median temperature of 40° F. relative to the R-Value of the construction board at a median temperature of 75° F., the method comprising:
preparing a polyisocyanurate construction board by forming a foam-forming mixture by combining an isocyanate, an aromatic polyester polyol, less than 1.5 parts by weight water per 100 parts by weight polyol, and a blowing agent including pentane, butane, and an optional blowing agent additive that has a Hansen Solubility Parameter (δ t ) that is greater than 17 MPa −0.5 , where the blowing agent mixture includes from about 5 to about 33 mole % of the blowing agent additive based on the total moles of the blowing agent mixture.