Polyamide-based film, method of preparing polyamide-based film, cover window and display device comprising the same
The embodiments provide a polyamide-based film, which comprises a polyamide-based polymer and has a light resistance index of 0.660 GPa-1 or less as represented by the following Equation 1, whereby it has excellent mechanical properties, optical properties, and light resistance. [Equation 1] Light resistance index=ΔYI/Y. In Equation 1, Y is the modulus of the film, and ΔYI is the rate of change in yellow index (YI) of the film before and after a light resistance test in which UV rays are irradiated to the film at 60° C., the UV irradiation is stopped, and water is sprayed at 50° C.
1. A polyamide-based film, which comprises a polyamide-based polymer and has a light resistance index of 0.400 to 0.660 GPa −1 as represented by the following Equation 1, and has a light resistance color change index of 1.55 to 1.64 as represented by the following Equation 2:
Light resistance index=Δ YI/Y [Equation 1]
in Equation 1, Y is the modulus of the film, and ΔYI is the rate of change in yellow index (YI) of the film before and after a light resistance test in which UV rays are irradiated to the film at 60° C., the UV irradiation is stopped, and water is sprayed at 50° C.,
Light resistance color change index=Δ YI/ΔE [Equation 2]
in Equation 2, ΔE is the color difference of the film before and after the light resistance test,
wherein the polyamide-based polymer is prepared by polymerizing a diamine compound and a dicarbonyl compound,
wherein the polyamide-based polymer comprises a first amide-based repeat unit derived from a first dicarbonyl compound and a second amide-based repeat unit derived from a second dicarbonyl compound,
wherein the angle between the two carbonyl groups contained in the first dicarbonyl compound is greater than the angle between the two carbonyl groups contained in the second dicarbonyl compound,
wherein the molar ratio of the repeat unit derived from the first dicarbonyl compound and the repeat unit derived from the second dicarbonyl compound is 21:79 to 79:21,
wherein the polyamide-based film comprises a blue pigment, and the blue pigment is employed in an amount of 100 to 2,000 ppm based on the total weight of the polyamide-based polymer, and
wherein ΔYI is 4.5 or less.
2. The polyamide-based film of claim 1 , wherein Y is 4 or more.
3. The polyamide-based film of claim 1 , which further comprises a UVA absorber mixed with the polyamide-based polymer and the blue pigment.
4. The polyamide-based film of claim 1 , which, based on a thickness of the film of 50 μm, has a modulus of 6 GPa or more, a transmittance of 80% or more, and a haze of 1% or less.
5. A process for preparing the polyamide-based film of claim 1 , which comprises:
polymerizing the diamine compound and the dicarbonyl compound in an organic solvent to prepare a solution comprising the polyamide-based polymer;
casting the solution to prepare a gel sheet; and
thermally treating the gel sheet,
wherein the step of polymerizing the diamine compound and the dicarbonyl compound comprises reacting the diamine compound and the dicarbonyl compound to form a first polymer solution having a viscosity of 1,000 to 10,000 cps, and reacting the first polymer solution with an additional amount of the dicarbonyl compound to form a second polymer solution having a viscosity of 200,000 to 350,000 cps.
6. The process for preparing the polyamide-based film according to claim 5 , wherein, in the step of forming the first polymer solution, a first dicarbonyl compound and a second dicarbonyl compound are sequentially reacted with the diamine compound, and, in the step of forming the second polymer solution, the second dicarbonyl compound is further reacted.
7. A cover window, which comprises a polyamide-based film comprising a polyamide-based polymer and a functional layer, wherein the polyamide-based film has a light resistance index of 0.400 to 0.660 GPa −1 as represented by the following Equation 1, and has a light resistance color change index of 1.55 to 1.64 as represented by the following Equation 2:
Light resistance index=Δ YI/Y [Equation 1]
In Equation 1, Y is the modulus of the film, and ΔYI is the rate of change in yellow index (YI) of the film before and after a light resistance test in which UV rays are irradiated to the film at 60° C., the UV irradiation is stopped, and water is sprayed at 50° C.,
Light resistance color change index=Δ YI/ΔE [Equation 2]
in Equation 2, ΔE is the color difference of the film before and after the light resistance test,
wherein the polyamide-based polymer is prepared by polymerizing a diamine compound and a dicarbonyl compound,
wherein the polyamide-based polymer comprises a first amide-based repeat unit derived from a first dicarbonyl compound and a second amide-based repeat unit derived from a second dicarbonyl compound,
wherein the angle between the two carbonyl groups contained in the first dicarbonyl compound is greater than the angle between the two carbonyl groups contained in the second dicarbonyl compound,
wherein the molar ratio of the repeat unit derived from the first dicarbonyl compound and the repeat unit derived from the second dicarbonyl compound is 21:79 to 79:21, and wherein the polyamide-based film comprises a blue pigment, and the blue pigment is employed in an amount of 100 to 2,000 ppm based on the total weight of the polyamide-based polymer.
8. A display device, which comprises a display unit;
and a cover window disposed on the display unit, wherein the cover window comprises a polyamide-based film comprising a polyamide-based polymer and a functional layer, and the polyamide-based film has a light resistance index of 0.400 to 0.660 GPa −1 as represented by the following Equation 1, and has a light resistance color change index of 1.55 to 1.64 as represented by the following Equation 2:
Light resistance index=Δ YI/Y [Equation 1]
in Equation 1, Y is the modulus of the film, and ΔYI is the rate of change in yellow index (YI) of the film before and after a light resistance test in which UV rays are irradiated to the film at 60° C., the UV irradiation is stopped, and water is sprayed at 50° C.,
Light resistance color change index=Δ YI/ΔE [Equation 2]
in Equation 2, ΔE is the color difference of the film before and after the light resistance test,
wherein the polyamide-based polymer is prepared by polymerizing a diamine compound and a dicarbonyl compound,
wherein the polyamide-based polymer comprises a first amide-based repeat unit derived from a first dicarbonyl compound and a second amide-based repeat unit derived from a second dicarbonyl compound,
wherein the angle between the two carbonyl groups contained in the first dicarbonyl compound is greater than the angle between the two carbonyl groups contained in the second dicarbonyl compound,
wherein the molar ratio of the repeat unit derived from the first dicarbonyl compound and the repeat unit derived from the second dicarbonyl compound is 21:79 to 79:21, and wherein the polyamide-based film comprises a blue pigment, and the blue pigment is employed in an amount of 100 to 2,000 ppm based on the total weight of the polyamide-based polymer.