Method of manufacturing gypsum board with improved fire resistance
The present disclosure is directed to a method of manufacturing gypsum board as well as the resulting gypsum board. The method comprises providing a gypsum slurry with a shrinkage-reducing additive comprising a metal salt of an acid, a silica, or a mixture thereof. As a result, the gypsum board includes gypsum and a shrinkage-reducing additive comprising a metal salt of an acid, a silica, or a mixture thereof. The gypsum board exhibits an area shrinkage of less than 10%.
1. A method for manufacturing a gypsum board, the method comprising:
providing a gypsum slurry comprising stucco and a shrinkage-reducing additive comprising a silica comprising colloidal silica, precipitated silica, or a mixutre thereof onto a bottom facing material, wherein the shrinkage-reducing additive is present in an amount of 0.05 wt. % or more to 2 wt. % or less based on the weight of the stucco, and
providing a top facing material on the gypsum slurry,
wherein the gypsum board exhibits an area shrinkage of 10% or less, and
wherein the gypsum board exhibits a nail pull strength of 70 lb f or more.
2. The method according to claim 1 , wherein the silica comprises colloidal silica.
3. The method according to claim 1 , wherein the silica comprises precipitated silica.
4. The method according to claim 1 , wherein the shrinkage-reducing additive has a particle size of 5 nanometers or more to 100 micrometers or less.
5. The method according to claim 1 , wherein the gypsum board exhibits an area shrinkage of 8% or less.
6. The method according to claim 1 , wherein the shrinkage-reducing additive is present in an amount of 0.05 wt. % or more to 1 wt. % or less.
7. The method according to claim 1 , wherein the shrinkage-reducing additive has an average particle size of 5 nanometers or more to 100 nanometers or less.
8. A gypsum board comprising:
gypsum and a shrinkage-reducing additive comprising a silica wherein the shrinkage-reducing additive is present in an amount of 0.05 wt. % or more to 2 wt. % or less based on the weight of the gypsum, wherein the silica is from colloidal silica, precipitated silica, or a mixutre thereof,
wherein the gypsum board exhibits an area shrinkage of 10% or less, and
wherein the gypsum board exhibits a nail pull strength of 70 lb f or more.
9. The gypsum board according to claim 8 , wherein the silica comprises colloidal silica.
10. The gypsum board according to claim 8 , wherein the silica comprises precipitated silica.
11. The gypsum board according to claim 8 , wherein the shrinkage-reducing additive has a particle size of 5 nanometers or more to 100 micrometers or less.
12. The gypsum board according to claim 8 , wherein the gypsum board exhibits an area shrinkage of 8% or less.
13. The gypsum board according to claim 8 , wherein shrinkage-reducing additive is present in an amount of 0.05 wt. % or more to 1 wt. % or less.
14. The gypsum board according to claim 8 , wherein the shrinkage-reducing additive has an average particle size of 5 nanometers or more to 100 nanometers or less.