Polyamide powders and use thereof in powder agglomeration processes by sintering
A polyamide powder for use in a process of powder agglomeration by sintering, including at least one chain limiting agent. A process for preparing a powder including at least one chain limiting agent, wherein the chain limiter is mixed with the polyamide powder, and if need be at least one thioether antioxidant, by dry blending.
1 . A powder composition intended to be used in a process for agglomeration of powder by melting, the powder composition comprising a polyamide and at least one chain limiter,
wherein the chain limiter comprises sebacic acid, and
wherein the composition further comprises at least one thioether antioxidant.
2 . The powder composition as claimed in claim 1 , wherein the chain limiter represents from 0.01% to 10% by weight relative to the total weight of powder composition representing 100%.
3 . The powder composition as claimed in claim 1 , wherein the chain limiter further comprises a second chain limiter selected from the group consisting of acetic acid, propionic acid, benzoic acid, stearic acid, lauric acid, butanoic acid, pentanoic acid, hexanoic acid, heptanoic acid, octanoic acid, nonanoic acid, decanoic acid, undecanoic acid, acrylic acid, methacrylic acid, crotonic acid, cinnamic acid, hexadecanoic acid, octodecanoic acid, tetradecanoic acid, adipic acid, azelaic acid, suberic acid, dodecanedicarboxylic acid, ortho-phthalic acid, butanedioic acid, 1-aminopentane, 1-aminohexane, 1-aminoheptane, 1-aminooctane, 1-aminononane, 1-aminodecane, 1-aminoundecane, 1-aminododecane, benzylamine, oleylamine, bis(4-aminocyclohexyl) methane (BACM), bis(3-methyl-4-aminocyclohexyl) methane (BMACM), and 2,2-bis(3-methyl-4-aminocyclohexyl) propane (BMACP), para-aminodicyclohexylmethane (PACM), isophoronediamine (IPDA), 2,6-bis(aminomethyl) norbornane (BAMN), and piperazine.
4 . The powder composition as claimed in claim 1 , wherein the polyamide comprises at least one monomer selected from the group consisting of 46, 4T, 54, 59, 510, 512, 513, 514, 516, 518, 536, 6, 64, 69, 610, 612, 613, 614, 616, 618, 636, 6T, 9, 104, 109, 1010, 1011, 1012, 1013, 1014, 1016, 1018, 1036, 10T, 11, 12, 124, 129, 1210, 1212, 1213, 1214, 1216, 1218, 1236, 12T, MXD6, MXD10, MXD12, and MXD14.
5 . The powder composition as claimed in claim 1 , wherein the polyamide is selected from the group consisting of PA 6, PA 66, PA 1010, PA 11, PA 12, PA 1011, PA 610, PA 612, PA 613, and mixtures thereof.
6 . The powder composition as claimed in claim 1 , wherein said at least one thioether antioxidant is selected from the group consisting of dilauryl thiodipropionate (DLTDP), ditridecyl thiodipropionate (DTDTDP), distearyl thiodipropionate (DSTDP), dimyristyl thiodipropionate (DMTDP), and pentaerythrityl tetrakis(3-laurylthiopropionate).
7 . The powder composition as claimed in claim 1 , wherein said at least one thioether antioxidant represents from 0.1% to 5% by weight relative to the total weight of powder representing 100%.
8 . A process for preparing the powder composition as claimed in claim 1 , wherein the chain limiter is mixed with the polyamide powder by dry blending.
9 . A powder composition obtained from the process of claim 8 .
10 . A process for preparing the powder composition as claimed in claim 1 , wherein the polyamide is a polyamide prepolymer, wherein the chain limiter is mixed with a powder of the polyamide prepolymer having an inherent viscosity of less than or equal to 0.80, comprising a step of solid-state polycondensation of said mixture.
11 . The process as claimed in claim 10 , wherein the chain limiter is mixed with the polyamide prepolymer powder, after a water treatment step and/or an acid treatment step.
12 . A process for manufacturing an object wherein the powder composition of claim 1 is agglomerated by melting.
13 . An object manufactured using the powder composition as defined in claim 1 .
14 . The powder composition as claimed in claim 1 , wherein the chain limiter has been added to an already formed polyamide, wherein the chain limiter is not added to a reaction mixture comprising monomers of the polyamide.
15 . The powder composition as claimed in claim 1 , wherein the chain limiter and the polyamide powder have been mixed by dry blending.
16 . The powder composition as claimed in claim 15 , wherein the chain limiter, the polyamide powder, and the thioether antioxidant have been mixed by dry blending.
17 . The powder composition as claimed in claim 15 , wherein the polyamide is in the form of polyamide powder particles, wherein the polyamide powder particles have a volume median diameter (D50) of between 5 and 200 μm.
18 . The powder composition as claimed in claim 1 , wherein the polyamide has a difference between a crystallization temperature (T c ) and a first heat melting temperature (T m1 ), (T c −T m1 ), of greater than 3° C.
19 . The powder composition as claimed in claim 1 , wherein the powder composition has an inherent viscosity in solution, before use thereof in a powder agglomeration process, of less than 1.90, and wherein the powder composition has an inherent viscosity in solution, after a first run in the process for agglomeration of powder by melting, of greater than 1.