Compositions useful for making additive manufactured articles are comprised of a styrenic thermoplastic elastomer, the styrenic thermoplastic elastomer being comprised of a block copolymer being comprised of at least two blocks of a vinyl aromatic monomer and at least one block of a conjugated diene monomer, and a solid particulate filler dispersed therein, wherein the filler has a surface area of 0.05 m 2 /g to 120 m 2 /g. The compositions may be formed into filaments for use in fused filament fabrication additive manufacturing. The filaments display good printability without drying or storage under dry conditions.
1 . An additive manufacturing composition comprising:
a styrenic thermoplastic elastomer, the styrenic thermoplastic elastomer being comprised of a block copolymer being comprised of at least two blocks of a vinyl aromatic monomer and at least one block of a conjugated diene monomer. and a solid particulate filler dispersed therein, wherein the filler has a surface area of 0.05 m 2 /g to 120 m 2 /g and is acicular having an aspect ratio of 3 to 25.
2 . The composition of claim 1 , wherein the conjugated diene monomer is of the formula:
R 2 C═CR—CR═CR 2
wherein each R, independently each occurrence, is hydrogen or alkyl of one to four carbons, where any two R groups may form a ring and the vinyl aromatic monomer has at most 20 carbons, and the vinyl aromatic monomer is of the formula:
Ar—C(R 1 )—C(R 1 ) 2
wherein each R 1 is independently in each occurrence hydrogen or alkyl or forms a ring with another R 1 , Ar is phenyl, halophenyl, alkylphenyl, alkylhalophenyl, naphthyl, pyridinyl, or anthracenyl, wherein any alkyl group contains 1 to 6 carbon atoms which may optionally be mono or multi-substituted with functional groups.
3 . The composition of claim 2 , wherein the blocks of the conjugated diene monomer have been hydrogenated to eliminate at least a portion of residual carbon-carbon double bonds.
4 . (canceled)
5 . The composition of claim 2 , wherein the styrenic thermoplastic elastomer is a styrene-(ethylene-butylene)-styrene (SEBS) thermoplastic elastomer.
6 . The composition of claim 1 , wherein the filler has particle size where the D50 is from about 0.5 micrometer to about 5 micrometer and the D90 is between about 20 to about 40 micrometers and the D10 is about 0.1 micrometer to 2 micrometers.
7 . The composition of claim 1 , wherein the filler has an aspect ratio of about 5 to about 25.
8 . The composition of claim 7 , wherein the filler is clay, wollastonite, graphitic carbon, boron nitride, silicon carbide or talc.
9 . (canceled)
10 . (canceled)
11 . (canceled)
12 . The composition of claim 1 further comprising a polyolefin.
13 . The composition of claim 12 , wherein the polyolefin is a homopolymer of propylene, or copolymer of propylene and ethylene.
14 . The composition of claim 12 , wherein the polyolefin has a melt flow rate of 1 to 50 g/10 minutes at (230° C./2.16 kg).
15 . The composition of claim 14 , wherein the styrenic thermoplastic elastomer has a melt flow rate of 50 to 150 g/10 minutes at (210° C./2.16 kg).
16 . The composition of claim 15 , wherein the melt flow rate of the styrenic thermoplastic elastomer at (210° C./2.16 kg) and the melt flow rate of the polyolefin at (230° C./2.16 kg) has a ratio of 10 to 3.
17 . (canceled)
18 . (canceled)
19 . A method of printing an object comprising:
drawing, heating and extruding a filament comprised of a composition comprising a styrenic thermoplastic elastomer, the styrenic thermoplastic elastomer being comprised of a block copolymer being comprised of at least two blocks of a vinyl aromatic monomer and at least one block of a conjugated diene monomer. and a solid particulate filler dispersed therein, wherein the filler has a surface area of 0.05 m 2 /g to 120 m 2 /g and is acicular having an aspect ratio of 3 to 25 through a print head to form an extrudate, and, depositing the extrudate onto a base such that multiple layers are controllably deposited and fused to form an additive manufactured article.
20 . The method of claim 19 wherein the extruding is by a Bowden extruder having a Bowden tube.
21 . (canceled)
22 . An article comprising an additive manufactured article comprising a plurality of layers fused or adhered together, wherein at least two layers are comprised of a thermoplastic elastomer comprised of a styrenic thermoplastic elastomer comprised of a block copolymer that is comprised of at least two blocks of a vinyl aromatic monomer and at least one block of a conjugated diene monomer. and a solid particulate filler dispersed therein, wherein the filler has a surface area of 0.05 m 2 /g to 120 m 2 /g and is acicular having an aspect ratio of 3 to 25.
23 . The article of claim 22 , wherein, the styrenic thermoplastic elastomer has been hydrogenated to remove at least a portion of residual double bonds in the conjugated diene monomer block.
24 . (canceled)
25 . The article of claim 22 , wherein the layer is further comprised of a polyolefin that is a homopolymer of polypropylene or copolymer of ethylene and propylene.
26 . The article of claim 25 , wherein the styrenic thermoplastic elastomer has a melt flow rate at (210° C./2.16 kg) and the polyolefin has a melt flow rate at (230° C./2.16 kg) such that the ratio of said styrenic thermoplastic elastomer to said polyolefin melt flow rate has a ratio of 10 to 3
27 . The article of claim 26 , wherein the layer is comprised of about 10-80 wt % of the styrenic thermoplastic elastomer; about 10-70 wt % of the polyolefin; and
about 10-30 wt % of the filler.
28 . The article of claim 22 , wherein the thermoplastic elastomer consists of the styrenic thermoplastic elastomer.