Multilayer floor panel based on a PVC plastisol
Floor panels that includes a substrate and a multi-layered top layer directed attached to the substrate. The multi-layered top layer includes a décor layer that includes a fused PVC plastisol, a print pattern deposited as single or stacked dots of a digitally printed material on top of the décor layer, a wear-resistant layer including a fused PVC plastisol provided above the print pattern. Optionally, a lacquer layer is provided directly on top of the wear-resistant layer.
1. A floor panel comprising:
a substrate;
a multi-layered top layer directly attached to the substrate;
wherein the multi-layered top layer comprises:
a decor layer comprising a fused PVC plastisol,
a print pattern deposited as single or stacked dots of a digitally printed material on top of the decor layer,
a wear-resistant layer comprising a fused PVC plastisol provided above the print pattern, wherein the wear-resistant layer is obtained by gelling a PVC plastisol and by mechanically embossing the PVC plastisol during gelling and subsequently fusing the gelled PVC plastisol to obtain the fused wear-resistant layer, wherein the ratio between elastic moduli of the substrate and multi-layered top layer is at least 20 measured at 23±2° C. and 50±10% R.H. according to ISO 527.
2. The floor panel according to claim 1 , further comprising a lacquer layer provided directly on top of the wear-resistant layer.
3. The floor panel according to claim 2 , wherein the lacquer layer is a continuous or discontinuous, transparent layer that conforms to a mechanically and/or chemically embossed relief pattern, or
wherein the lacquer layer is conformal with the wear-resistant layer.
4. The floor panel according to claim 1 , wherein the multi-layered top layer has an elastic modulus of less than 100 MPa at 23° C. measured at 23±2° C. and 50±10% R.H., according to ISO 527 or wherein the multi-layered top layer does not comprise a reinforcement layer.
5. The floor panel according to claim 1 , wherein the substrate has an elastic modulus of more than 2000 MPa measured at 23±2° C. and 50±10% R.H., according to ISO 527 or
wherein the substrate is a single layer substrate, or
wherein the substrate does not comprise a reinforcement layer, or
wherein the substrate is a foamed substrate, or
wherein the substrate is a single layer substrate.
6. The floor panel according to claim 1 , wherein the floor panel is free of interlayer adhesive material.
7. The floor panel according to claim 6 , wherein a density of the foamed substrate is equal to or less than 1600 kg/m 3 , and the density is equal to or more than 400 kg/m 3 , or
wherein the density is in the range 1050 kg/m 3 to 1300 kg/m 3 .
8. The floor panel according to claim 1 , wherein the substrate has a thickness of 1 mm to 25 mm, or
wherein the substrate has a glass transition temperature (T g ) of 80° C. or higher.
9. The floor panel according to claim 1 , wherein the decor layer comprises a chemically embossed relief pattern formed by single or stacked dots of digitally printed material comprising a foam inhibiting agent, or wherein a thickness of the décor layer is in the range 0.1 to 0.7 mm.
10. The floor panel according to claim 1 , wherein the wear-resistant layer has a mechanically embossed surface structure.
11. The floor panel according to claim 1 , comprising a surface with different gloss levels comprising first zones with high gloss, second zones with silk gloss, and third zones with matt, or
wherein the surface has macro, micro, and nanoscale features.
12. The floor panel according to claim 11 , wherein the one or more zones of a surface of the panel which has/have a gloss value or macro, micro, and nanoscale features are aligned with one or more parts of the print pattern.
13. The floor panel according to claim 1 , wherein the resistance against separation of the substrate and the multi-layered top layer by peeling is at least 50 N/50 mm as determined by a peel test.
14. A method for producing a floor panel comprising the subsequent steps of:
S 1 : providing a substrate,
S 2 : applying a first coating comprising a PVC plastisol directly onto the substrate to obtain a decor layer,
S 3 : gelling the decor layer,
S 4 : applying a print pattern of single or stacked dots of printing material directly onto the gelled decor layer by means of digital printing,
S 5 : applying a second coating comprising a PVC plastisol onto the printed decor layer to obtain a wear-resistant layer, and
S 6 : gelling the wear-resistant layer and subsequently fusing the decor layer and wear-resistant layer, and further comprising the step of mechanically embossing the wear-resistant layer with an embossing mould during gelling, wherein the embossing mould is a release web, or wherein the embossing mould is a polymer coated paper.
15. The method according to claim 14 , further comprising a step of: S 7 : applying a lacquer layer directly on top of the fused wear-resistant layer.
16. The method according to claim 15 , wherein the lacquer layer is conformal with the wear-resistant layer, or
wherein the lacquer layer is a continuous or discontinuous, transparent layer that conforms to a mechanically and/or chemically embossed relief pattern.
17. The method for producing a floor panel according to claim 14 , wherein the floor panel is free of interlayer adhesive material.
18. The method for producing a floor panel according to claim 14 , wherein the substrate is a foamed substrate, or
wherein the substrate is a single layer substrate.
19. The method for producing a floor panel according to claim 14 , further comprising the steps of:
providing a blowing agent into the first coating to obtain a foamable decor layer in step S 2 ,
applying a pattern of single or stacked dots of printed material comprising foam inhibiting agent onto the gelled foamable decor layer by means of digital printing, and
foaming the foamable decor layer in step S 6 .
20. The method for producing a floor panel according to claim 14 , wherein the embossing mould is in contact with the wear-resistant layer during gelling without exerting additional pressure.
21. The method according to claim 14 , comprising generating multiple gloss levels in first zones with high gloss, second zones with silk gloss, and third zones which are matt on a surface of the floor panel, or
wherein the surface has macro, micro, and nanoscale features.
22. The method according to claim 21 , wherein one or more zones of a surface of the panel which has/have a gloss value or macro, micro, and nanoscale features are aligned with one or more parts of a print pattern.
23. A floor panel comprising:
a substrate;
a multi-layered top layer directly attached to the substrate, wherein the multi-layered top layer comprises:
a decor layer comprising a fused PVC plastisol,
a print pattern deposited as single or stacked dots of a digitally printed material on top of the decor layer,
a wear-resistant layer comprising a fused PVC plastisol provided above the print pattern, wherein the wear-resistant layer is obtained by gelling a PVC plastisol and by mechanically embossing the PVC plastisol during gelling and subsequently fusing the gelled PVC plastisol to obtain the fused wear-resistant layer, wherein resistance against separation of the substrate and the multi-layered top layer to peeling is at least 50 N/50 mm.