Granted Patent B2

US 12,686,970 · App. 17/782,062 · Granted Jul 21, 2026

Inventors: Jan-Olof Fechter (Alvesta, SE); Michael Germann (Laatzen, DE); Pontus Håkansson (Älmhult, SE); Martin Siewert (Rollshausen, DE)

Assignee: Inter IKEA Systems B.V.

D21B1/36B09B3/35B09B3/45C08J11/14C08L97/02D21B1/12B27N3/007B27N3/04C08J2397/02C08L2205/16Y02W30/78

Abstract

Claims (23)

1 . A process for recycling lignocellulosic fibers from a fiberboard comprising compressed lignocellulosic fibers bonded together by a binding agent, the process comprising the steps of:

disintegrating the fiberboard to provide fiberboard pieces;

steaming the fiberboard pieces in a steaming vessel by introducing steam into the steaming vessel to expose the fiberboard pieces to steam at a pressure of 1.1 to 10 bar absolute pressure and at a temperature of 103° C. to 180° C. to decompress and release the lignocellulosic fibers by hydrating them, as well as hydrolyzing the binding agent, wherein the moisture content of the fiberboard pieces to be steamed does not exceed 30% based on the dry weight of the fiberboard pieces;

releasing the overpressure;

removing excess water vapor to provide portions comprising released lignocellulosic fibers, wherein the moisture content in the portions comprising released lignocellulosic fibers is 15 to 30% based on the dry weight of the portions; and

separating the lignocellulosic fibers in the portions comprising released lignocellulosic fibers to provide recycled lignocellulosic fibers.

2 . The process according to claim 1 , wherein the fiberboard pieces are steamed at a pressure of 1.1 to 7 bar absolute pressure and at a temperature of 103° C. to 165° C.

3 . The process according to claim 2 , wherein the fiberboard pieces are steamed at a pressure of more than 1.1 bar to less than 2 bars and at a temperature of more than 103° C. to less than 120° C.

4 . The process according to claim 3 , wherein the fiberboard pieces are steamed at a pressure of 1.2 to 1.9 bar absolute pressure and at a temperature of 105° C. to 119° C.

5 . The process according to claim 4 , wherein the fiberboard pieces are steamed at a pressure of 1.2 to 1.7 bar absolute pressure and at a temperature of 105° C. to 115° C.

6 . The process according to claim 1 , wherein the residence time in the step of steaming the fiberboard pieces is 1 to 60 minutes.

7 . The process according to claim 6 , wherein the residence time in the step of steaming the fiberboard pieces is 5 to 20 minutes.

8 . The process according to claim 1 , wherein the fiberboard is disintegrated by crushing and/or shredding the fiberboard into fiberboard pieces.

9 . The process according to claim 1 , wherein the process further comprises a step of size-sorting the recycled lignocellulosic fibers to provide size fraction(s) of recycled lignocellulosic fibers.

10 . The process according to claim 1 , wherein said fiberboard is LDF (Low Density Fiberboard), MDF (Medium Density Fiberboard), or HDF (High Density Fiberboard).

11 . The process according to claim 10 , wherein said fiberboard is MDF (Medium Density Fiberboard) or HDF (High Density Fiberboard).

12 . The process according to claim 1 , wherein the steaming is performed in manner such that fiberboard pieces are separated from any condensed water.

13 . The process according to claim 1 , wherein the fiberboard pieces are present on a distance element for steaming them, whereby keeping the fiberboard pieces, as well as the resulting portions comprising released lignocellulosic fibers, separate from any condensed water.

14 . The process according to claim 1 , wherein the moisture content of the fiberboard pieces to be steamed does not exceed 25% based on the dry weight of the fiberboard pieces.

15 . The process according to claim 14 , wherein the moisture content of the fiberboard pieces to be steamed does not exceed 20% based on the dry weight of the fiberboard pieces.

16 . The process according to claim 15 , wherein the moisture content of the fiberboard pieces to be steamed does not exceed 15% based on the dry weight of the fiberboard pieces.

17 . The process according to claim 1 , wherein the process further comprises the step of mixing the recycled lignocellulosic fibers with a binding agent, and optionally virgin lignocellulosic fibers, to provide a mixture; arranging the resulting mixture into a layer; and compressing the layer into a fiberboard comprising recycled lignocellulosic fibers, wherein the layer optionally is heated in compressing it into a fiberboard.

18 . The process according to claim 1 , wherein the steaming of the fiberboard pieces comprises pressurizing the steaming vessel with the steam.