Co-extrusion SPC foam flooring and manufacturing method thereof

1. A co-extrusion foam flooring, comprising a stone-plastic base material structure,

wherein the stone-plastic base material structure sequentially comprises, from top to bottom, a first stable layer, a foaming layer and a second stable layer;

the first stable layer and the second stable layer are both sheets with a PVC resin and filler powder as main components;

wherein an amount of the PVC resin is 100 parts by weight and the amount of the filler powder is 200 to 300 parts by weight; and

wherein the foaming layer is a physical foaming layer comprising carbon dioxide as a physical foaming agent and the following components in parts by weight: 100 parts of polyvinyl chloride resin powder, 300 to 330 parts of calcium carbonate, 4 to 7 parts of a calcium zinc stabilizer, 1 to 1.5 parts of an internal lubricant, 1 to 1.5 parts of polyethylene wax, 4 to 8 parts of chlorinated polyethylene, 3 to 5 parts of acrylate, and 0.7 to 1.2 parts of a composite lubricant;

wherein a density of the foam flooring is in a range of 1.4 to 1.6 g/cm 3 ;

wherein the filler powder is calcium carbonate or comprises calcium carbonate as a main component and one material selected from the group consisting of calcium bicarbonate, glass fiber and carbon fiber or any mixture thereof.

2. The co-extrusion foam flooring of claim 1 , wherein a thickness of the first stable layer is in a range of 1 to 5 mm; a thickness of the foaming layer is in a range of 2 to 10 mm; and a thickness of the second stable layer is in a range of 1 to 5 mm.

3. The co-extrusion foam flooring of claim 1 , wherein the first stable layer and the second stable layer further comprise an additive, and the additive is one additive selected from the group consisting of a calcium zinc stabilizer, an internal lubricant, polyethylene wax, chlorinated polyethylene, acrylate, a composite lubricant, a colorant, and a combination thereof.

4. The co-extrusion foam flooring of claim 1 , wherein the foaming layer comprises 0.3 to 0.5 parts of a colorant.

5. The co-extrusion foam flooring of claim 1 , wherein the foaming layer comprises 0.4 to 0.6 parts of a colorant.

6. The co-extrusion foam flooring of claim 1 , wherein the foam flooring further comprises a decorative and protective structure sequentially comprising, from top to bottom, a UV coating, a wear-resistant layer and a decorative layer.

7. A method for preparing a co-extrusion foam flooring, wherein the co-extrusion foam flooring comprises a stone-plastic base material structure sequentially including, from top to bottom, a first stable layer, a foaming layer and a second stable layer;

the method comprising the following steps:

a. feeding raw materials for the first stable layer and the second stable layer into a high-speed mixer, mixing and heating the raw materials, cooling a mixture of the raw materials in the low-speed mixer, extruding the mixture from a first extruder;

b. feeding raw materials for the foaming layer into the high-speed mixer, mixing and heating the raw materials, cooling the raw materials in the low-speed mixer, introducing the raw materials into a second extruder; performing even melt plastification and extruding the raw materials from the second extruder; performing even melt plastification for the raw materials in the second extruder, injecting 4-10 wt % liquefied high-pressure carbon dioxide into the foaming agent injection device, maintaining a high pressure in a mold cavity to keep carbon dioxide in a liquid state so as to completely mix with the material, releasing the pressure during a course of extrusion;

c. allowing the extrudate of the first extruder to enter a mold flow channel distributor and converge with the extrudate of the second extruder at a die head, co-extruding the mixture through a die orifice of a die head to form the stone-plastic base material structure;

d. passing a plate released from the mold through an area between a background pattern roller and a first mirror finish roller to form a background pattern by compression, transferring the stone-plastic base material structure to an area between a second mirror finish roller and an embossing roller; allowing a servo feeding roller for the wear-resistant layer and the servo feeding roller for a decorative layer to transfer a wear-resistant layer and a decorative paper respectively to an area between the second mirror finish roller and an air release roller, performing pre-lamination; laminating the wear-resistant layer and the decorative paper on a base material layer through an action of the second mirror finish roller and the embossing roller to form the wear-resistant layer and the decorative layer having, as well as a surface pattern with concave and convex three-dimensional effect on a front face;

e. providing a UV coating on the wear-resistant layer;

wherein the foam flooring further comprises a decorative and protective structure sequentially comprising, from top to bottom, a UV coating, a wear-resistant layer and a decorative layer;

the first stable layer and the second stable layer are both sheets with a PVC resin and filler powder as main components;

wherein an amount of the PVC resin is 100 parts by weight and the amount of the filler powder is 200 to 300 parts by weight;

wherein the foaming layer is a physical foaming layer comprising carbon dioxide as a physical foaming agent and the following components in parts by weight: 100 parts of polyvinyl chloride resin powder, 300 to 330 parts of calcium carbonate, 4 to 7 parts of a calcium zinc stabilizer, 1 to 1.5 parts of an internal lubricant, 1 to 1.5 parts of polyethylene wax, 4 to 8 parts of chlorinated polyethylene, 3 to 5 parts of acrylate, and 0.7 to 1.2 parts of a composite lubricant;

wherein a density of the foam flooring is in a range of 1.4 to 1.6 g/cm 3 ; and

wherein the filler powder is calcium carbonate or comprises calcium carbonate as a main component and one material selected from the group consisting of calcium bicarbonate, glass fiber and carbon fiber or any mixture thereof.