POLYCARBONATE COMPOSITIONS CONTAINING FILLERS AND TRIACYLGLYCEROL CONTAINING EPOXY GROUPS
The invention relates to carbon fiber-containing polycarbonate compositions, the flowability of which is significantly improved by adding epoxidized triacylglycerols, for example as a constituent of epoxidized soy bean oil. In addition to the very high flowability, the compositions according to the invention have a high rigidity.
1 .- 15 . (canceled)
16 . A thermoplastic composition, containing
A) 50.0% by weight to 91.95% by weight of aromatic polycarbonate,
B) 8% to 49.95% by weight of carbon fibers,
C) 0.05% by weight to 10.0% by weight of epoxidized triacylglycerol.
17 . The thermoplastic composition as claimed in claim 16 , wherein the composition contains
A) 77.0% by weight to 91.5% by weight of aromatic polycarbonate,
B) 8% to 22% by weight of carbon fibers,
C) 0.2% to 1.0% by weight of epoxidized triacylglycerol,
D) 0.005% to 0.5% by weight of heat stabilizer and
E) 0.1% to 3% by weight of further additives.
18 . The thermoplastic composition as claimed in claim 17 , wherein the composition contains, as further additive, at least one alkali metal, alkaline earth metal and/or ammonium salt of an aliphatic or aromatic sulfonic acid, sulfonamide or sulfonimide derivative.
19 . The thermoplastic composition as claimed in claim 16 , wherein, as further additive, 0.1% to 0.5% by weight of potassium perfluoro-1-butanesulfonate is present.
20 . The thermoplastic composition as claimed in claim 16 , wherein the amount of epoxidized triacylglycerol in the composition is ≤0.8% by weight.
21 . The thermoplastic composition as claimed in claim 16 , wherein, as aromatic polycarbonate, bisphenol A-based polycarbonate is present.
22 . The thermoplastic composition as claimed in claim 16 , wherein the epoxidized triacylglycerol contains a mixture of triesters of glycerol with oleic acid, linoleic acid, linolenic acid, palmitic acid and/or stearic acid.
23 . The thermoplastic composition as claimed in claim 16 , wherein, as aromatic polycarbonate, exclusively aromatic homopolycarbonate is present.
24 . The thermoplastic composition as claimed in claim 16 , wherein at least 90% by weight of the C═C double bonds from the carboxylic acid moieties of the triacylglycerols have been completely epoxidized.
25 . The thermoplastic composition as claimed in claim 16 , wherein component C is introduced into the thermoplastic composition by admixing epoxidized soybean oil (CAS number 8013-07-8).
26 . The thermoplastic composition as claimed in claim 25 , wherein the acid number of the epoxidized soybean oil is ≤0.5 mg KOH/g, determined by DIN EN ISO 2114:2006-11.
27 . The thermoplastic composition as claimed in claim 17 , wherein the additives are selected from the group of the antioxidants, demolding agents, flame retardants, UV absorbers, IR absorbers, impact modifiers, antistats, optical brighteners, fillers other than component B, light-scattering agents, colorants such as organic pigments, inorganic pigments and/or additives for laser marking, and the composition does not contain any further components.
28 . The thermoplastic composition as claimed in claim 16 , wherein the composition consists of
A) 77.0% by weight to 91.5% by weight of aromatic polycarbonate,
B) 8% to 22% by weight of carbon fibers,
C) 0.2% to 1.0% by weight of epoxidized soybean oil, containing epoxidized triacylglycerols,
D) 0.005% to 0.5% by weight of heat stabilizer and
E) 0.1% to 3% by weight of further additives selected from the group consisting of antioxidants, demolding agents, flame retardants, UV absorbers, IR absorbers, impact modifiers, antistats, optical brighteners, light-scattering agents, colorants, including inorganic pigments, and/or additives for laser marking.
29 . A molding consisting of or comprising a thermoplastic composition as claimed in claim 16 .
30 . A method comprising providing an epoxidized triacylglycerol and improving the flowability of glass fiber- and/or carbon fiber-containing thermoplastic compositions based on aromatic polycarbonate.