Vehicle pane with reduced emissivity and light reflection
A vehicle pane with reduced emissivity and light reflection, includes a substrate having an exposed interior-side surface, an emissivity-reducing coating containing at least one layer based on a transparent conductive oxide (TCO) on the interior-side surface, and an anti-reflection coating based on nanoporous silicon oxide on the emissivity-reducing coating.
1 . A vehicle pane with reduced emissivity and light reflection, comprising:
a substrate having an exposed interior-side surface,
an emissivity-reducing coating containing at least one layer based on a transparent conductive oxide (TCO) on the interior-side surface and an upper anti-reflection layer with a refractive index of at most 1.8, and
an anti-reflection coating consisting of nanoporous silicon oxide or nanoporous silicon oxide doped with aluminium, zirconium, titanium, boron, tin, or zinc on the emissivity-reducing coating such that the upper anti-reflection layer with a refractive index of at most 1.8 of the emissivity-reducing coating is arranged between the transparent conductive oxide (TCO) and the anti-reflection coating, the anti-reflection coating being in direct contact with the upper anti-reflection layer,
wherein the anti-reflection coating has pores with a size from 1 nm to 500 nm,
wherein the anti-reflection coating has a refractive index from 1.2 to 1.4 and a thickness from 50 nm to 150 nm, and
wherein the upper anti-reflection layer comprises at least one of silicon oxide, doped silicon oxide, aluminum oxide, magnesium fluoride and calcium fluoride.
2 . The vehicle pane according to claim 1 , wherein the anti-reflection coating is a sol-gel coating, in which closed and/or open nanopores are formed.
3 . The vehicle pane according to claim 1 , wherein the layer based on a transparent conductive oxide (TCO) includes fluorine-doped tin oxide (FTO) or antimony-doped tin oxide (ATO) and has a thickness from 100 nm to 600 nm.
4 . The vehicle pane according to claim 1 , wherein the emissivity-reducing coating comprises the following layers, starting from the substrate:
a blocking layer against alkali diffusion with a refractive index of at least 1.9,
a lower anti-reflection layer with a refractive index of at most 1.8,
the layer based on a transparent conductive oxide, which is indium tin oxide,
a barrier layer to regulate oxygen diffusion with a refractive index of at least 1.9, and
said upper anti-reflection layer with a refractive index of at most 1.8.
5 . The vehicle pane according to claim 4 , wherein
the blocking layer contains a metal, a nitride, or a carbide,
the lower anti-reflection layer contains an oxide,
the barrier layer contains a metal, a nitride, or a carbide,
the upper anti-reflection layer contains at least one of silicon oxide, doped silicon oxide and aluminum oxide.
6 . The vehicle pane according to claim 5 , wherein
the blocking layer contains silicon nitride or silicon carbide,
the lower anti-reflection layer contains silicon oxide,
the barrier layer contains silicon nitride or silicon carbide, and
the upper anti-reflection layer contains silicon oxide.
7 . The vehicle pane according to claim 4 , wherein
the blocking layer has a thickness from 10 nm to 50 nm,
the lower anti-reflection layer has a thickness from 5 nm to 100 nm,
the layer based on a transparent conductive oxide has a thickness from 50 nm to 150 nm,
the barrier layer has a thickness from 5 nm to 20 nm,
the upper anti-reflection layer has a thickness from 10 nm to 100 nm.
8 . The vehicle pane according to claim 7 , wherein
the blocking layer has a thickness from 20 nm to 40 nm,
the lower anti-reflection layer has a thickness from 10 nm to 50 nm,
the layer based on a transparent conductive oxide has a thickness from 60 nm to 100 nm,
the barrier layer has a thickness from 7 nm to 12 nm, and
the upper anti-reflection layer has a thickness from 30 nm to 70 nm.
9 . The vehicle pane according to claim 1 , wherein the pores have a size from 20 nm to 80 nm.
10 . The vehicle pane according to claim 1 , wherein the anti-reflection coating has a refractive index from 1.25 to 1.35.
11 . A transportation vehicle for traffic on land, in the air, or on water, with a comprising the vehicle pane with reduced emissivity and light reflection according to claim 1 .
12 . A method for producing a vehicle pane with reduced emissivity and light reflection, comprising:
providing a substrate having an exposed interior-side surface;
applying an emissivity-reducing coating, which comprises at least one layer based on a transparent conductive oxide (TCO), and an upper anti-reflection layer with a refractive index of at most 1.8, to the exposed interior-side surface of the substrate; and
depositing an anti-reflection coating consisting of nanoporous silicon oxide or nanoporous silicon oxide doped with aluminium, zirconium, titanium, boron, tin, or zinc on the emissivity-reducing coating such that the upper anti-reflection layer with a refractive index of at most 1.8 of the emissivity-reducing coating is arranged between the transparent conductive oxide (TCO) and the anti-reflection coating, the anti-reflection coating being in direct contact with the upper anti-reflection layer,
wherein the anti-reflection coating has pores with a size from 1 nm to 500 nm,
wherein the anti-reflection coating has a refractive index from 1.2 to 1.4 and a thickness from 50 nm to 150 nm, and
wherein the upper anti-reflection layer comprises at least one of silicon oxide, doped silicon oxide, aluminum oxide, magnesium fluoride and calcium fluoride.
13 . The method according to claim 12 , wherein the anti-reflection coating is applied in in a sol-gel process, by
providing a precursor sol that contains silicon oxide precursors in a solvent,
mixing the precursor sol with a pore former,
applying the solution obtained to the interior-side surface of a substrate, and
condensing the precursor sol.
14 . The method according to claim 13 , wherein the pore former is removed after condensation of the precursor sol.
15 . The method according to claim 14 , wherein the pore former is implemented as polymeric nanoparticles, and wherein the removal of the pore former is achieved by a heat treatment at a temperature of at least 400° C.
16 . The method according to claim 14 , wherein the pore former is implemented as polymeric nanoparticles, and wherein the removal of the pore former is achieved by dissolving with a solvent.