TWC activity using rhodium/platinum and tannic acid as a complexing and reducing agent

1. A method of manufacturing a catalyst article, the method comprising:

providing a complex of a polyphenol and a PGM, the polyphenol comprising an ester functional group, the PGM comprising rhodium and/or platinum;

providing a support material;

applying the complex to the support material to form a loaded support material;

disposing the loaded support material on a substrate; and

heating the loaded support material to form nanoparticles of the PGM on the support material.

2. The method of claim 1 , wherein the polyphenol comprises tannic acid.

3. The method of claim 1 , wherein the PGM comprises rhodium.

4. The method of claim 1 , wherein the PGM comprises platinum.

5. The method of claim 1 , wherein the support material comprises an oxide selected from a group consisting of one or more of Al 2 O 3 , SiO 2 , TiO 2 , CeO 2 , ZrO 2 , CeO 2 —ZrO 2 , V 2 O 5 , La 2 O 3 and zeolites.

6. The method of claim 1 , wherein the support material comprises alumina and ceria-zirconia.

7. The method of claim 6 , wherein the alumina and/or ceria-zirconia is doped.

8. The method of claim 7 , wherein the alumina and/or ceria-zirconia is doped with an oxide of one or more of lanthanum, neodymium, yttrium, niobium, praseodymium, hafnium, molybdenum, titanium, vanadium, zinc, cadmium, manganese, iron, copper, calcium, barium, strontium, caesium, magnesium, potassium and sodium, preferably one or more of lanthanum, neodymium and yttrium.

9. The method of claim 1 , wherein the loaded support material is disposed on the substrate in the form of a slurry.

10. The method of claim 9 , wherein the slurry is prepared by a method comprising:

contacting a PGM salt and a polyphenol in water to form the complex of a polyphenol and a PGM in an aqueous solution, the PGM salt comprising rhodium and/or platinum;

applying the complex to the support material to form a loaded support material by contacting the support material with the aqueous solution;

optionally, adding one or more of an oxygen storage material, preferably ceria-zirconia; a promoter salt; a binder; an acid or a base; a thickening agent; and a reducing agent to the aqueous solution.

11. The method of claim 9 , wherein the PGM comprises rhodium and the support material comprises alumina and ceria-zirconia.

12. The method of claim 9 , further comprising disposing a further slurry on the substrate, the further slurry comprising one or more of a further support material; an oxygen storage material; a promoter salt; a binder; an acid or a base; a thickening agent; and a reducing agent, wherein disposing the further slurry on the substrate takes place before disposing the support material on the substrate and/or after heating the loaded support material to form nanoparticles of the PGM on the support material.

13. The method of claim 9 , wherein disposing the loaded support material on a substrate comprises contacting the slurry with the substrate and optionally:

applying a vacuum to the substrate, and/or

drying the slurry on the substrate.

14. The method of claim 13 , wherein the drying occurs:

at a temperature of from 60° C. to 200° C., preferably from 70° C. to 130° C.; and/or

for from 10 to 360 minutes, preferably from 15 to 60 minutes.

15. The method of claim 1 , wherein the substrate is in the form of a honeycomb monolith, a wall-flow filter, or a flow-through filter.

16. The method of claim 1 , wherein the heating is carried out:

at a temperature of from 400° C. to 700° C., preferably from 400° C. to 600° C., more preferably from 450° C. to 600° C.; and/or

for from 10 to 360 minutes, preferably from 35 to 120 minutes.