Palladium fixing and low fresh oxygen storage capacity using tannic acid as a complexing and reducing agent
A method of manufacturing a catalyst article, the method comprising: providing a complex of a polyphenol and a PGM, the polyphenol comprising an ester functional group, the PGM comprising palladium; providing a support material; applying the complex to the support material to form a loaded support material; disposing the loaded support material on a substrate; and heating the loaded support material to form nanoparticles of the PGM on the support material.
1. A method of manufacturing a catalyst article, the method comprising:
providing a complex of a polyphenol and a PGM, the polyphenol comprising an ester functional group, the PGM comprising palladium;
providing a support material;
applying the complex to the support material to form a loaded support material;
disposing the loaded support material on a substrate; and
heating the loaded support material to form nanoparticles of the PGM on the support material.
2. The method of claim 1 , wherein the polyphenol comprises tannic acid.
3. The method of claim 1 , wherein the PGM consists of palladium.
4. The method of claim 1 , wherein the support material comprises an oxide selected from a group consisting of one or more of Al 2 O 3 , SiO 2 , TiO 2 , CeO 2 , ZrO 2 , CeO 2 —ZrO 2 , V 2 O 5 , La 2 O 3 and zeolites.
5. The method of claim 1 , wherein the support material comprises Al 2 O 3 and CeO 2 —ZrO 2 .
6. The method of claim 5 , wherein the Al 2 O 3 and/or CeO 2 —ZrO 2 is doped.
7. The method of claim 6 , wherein the Al 2 O 3 and/or CeO 2 —ZrO 2 is doped with an oxide of one or more of lanthanum, neodymium, yttrium, niobium, praseodymium, hafnium, molybdenum, titanium, vanadium, zinc, cadmium, manganese, iron, copper, calcium, barium, strontium, caesium, magnesium, potassium and sodium, preferably one or more of lanthanum, neodymium and yttrium.
8. The method of claim 1 , wherein the loaded support material is disposed on the substrate in the form of a slurry.
9. The method of claim 8 , wherein the slurry is prepared by a method comprising:
contacting a PGM salt and a polyphenol in water to form the complex of a polyphenol and a PGM in an aqueous solution, the PGM salt comprising palladium;
applying the complex to the support material to form a loaded support material by contacting the support material with the aqueous solution;
optionally, adding one or more of an oxygen storage material, preferably ceria-zirconia; a promoter salt; a binder; an acid or a base; a thickening agent; and a reducing agent to the aqueous solution.
10. The method of claim 8 , wherein the slurry is prepared by a method comprising:
contacting a support material and an aqueous solution of a PGM salt to form a slurry comprising a PGM-salt-loaded support material, the PGM salt comprising palladium;
applying the complex of a polyphenol and a PGM to the support material to form a loaded support material by contacting the slurry comprising the PGM-salt-loaded support material and a polyphenol in water;
optionally, adding one or more of an oxygen storage material, preferably ceria-zirconia; a promoter salt; a binder; an acid or a base; a thickening agent; and a reducing agent to the aqueous solution or the slurry comprising the PGM-salt-loaded support material.
11. The method of claim 8 , wherein the support material comprises alumina and ceria-zirconia.
12. The method of claim 8 , further comprising disposing a further slurry on the substrate, the further slurry comprising one or more of a further support material; an oxygen storage material; a promoter salt, preferably barium acetate, barium sulfate, barium citrate or a combination thereof; a binder; an acid or a base; a thickening agent; and a reducing agent, wherein disposing the further slurry on the substrate takes place before disposing the support material on the substrate and/or after heating the loaded support material to form nanoparticles of the PGM on the support material.
13. The method of claim 8 , wherein disposing the loaded support material on a substrate comprises contacting the slurry with the substrate and optionally:
applying a vacuum to the substrate, and/or
drying the slurry on the substrate.
14. The method of claim 1 , wherein the substrate is in the form of a honeycomb monolith, a wall-flow filter or a flow-through filter.
15. The method of claim 1 , wherein the heating is carried out:
at a temperature of from 400° C. to 700° C., preferably from 400° C. to 600° C., more preferably from 450° C. to 600° C.; and/or
for from 10 to 360 minutes, preferably from 35 to 120 minutes.